Adhesion-Induced Demolding Forces of Hard Coated Microstructures Measured with a Novel Injection Molding Tool

The demolding of plastic parts remains a challenging aspect of injection molding. Despite various experimental studies and known solutions to reduce demolding forces, there is still not a complete understanding of the effects that occur. For this reason, laboratory devices and in-process measurement injection molding tools have been developed to measure demolding forces. However, these tools are mostly used to measure either frictional forces or demolding forces for a specific part geometry. Tools that can be used to measure the adhesion components are still the exception. In this study, a novel injection molding tool based on the principle of measuring adhesion-induced tensile forces is presented. With this tool, the measurement of the demolding force is separated from the actual ejection step of the molded part. The functionality of the tool was verified by molding PET specimens at different mold temperatures, mold insert conditions and geometries. It was demonstrated that once a stable thermal state of the molding tool was achieved, the demolding force could be accurately measured with a comparatively low force variance. A built-in camera was found to be an efficient tool for monitoring the contact surface between the specimen and the mold insert. By comparing the adhesion forces of PET molded on polished uncoated, diamond-like carbon and chromium nitride (CrN) coated mold inserts, it was found that a CrN coating reduced the demolding force by 98.5% and could therefore be an efficient solution to significantly improve demolding by reducing adhesive bond strength under tensile loading.

Direct Processing of PVD Hard Coatings via Focused Ion Beam Milling for Microinjection Molding

Hard coatings can be applied onto microstructured molds to influence wear, form filling and demolding behaviors in microinjection molding. As an alternative to this conventional manufacturing procedure, "direct processing" of physical-vapor-deposited (PVD) hard coatings was investigated in this study, by fabricating submicron features directly into the coatings for a subsequent replication via molding. Different diamondlike carbon (DLC) and chromium nitride (CrN) PVD coatings were investigated regarding their suitability for focused ion beam (FIB) milling and microinjection molding using microscope imaging and areal roughness measurements. Each coating type was deposited onto high-gloss polished mold inserts. A specific test pattern containing different submicron features was then FIB-milled into the coatings using varied FIB parameters. The milling results were found to be influenced by the coating morphology and grain microstructure. Using injection-compression molding, the submicron structures were molded onto polycarbonate (PC) and cyclic olefin polymer (COP). The molding results revealed contrasting molding performances for the studied coatings and polymers. For CrN and PC, a sufficient replication fidelity based on AFM measurements was achieved. In contrast, only an insufficient molding result could be obtained for the DLC. No abrasive wear or coating delamination could be found after molding.

Texturing Technologies for Plastics Injection Molding: A Review

Texturing is an engineering technology that can be used to enable surface functionalization in the plastics injection molding industry. A texture is defined as the geometrical modification of the topography by addition of surface features that are characterized by a smaller scale than the overall surface dimensions. Texturing is added to products to create novel functionalities of plastic products and tools, which can be exploited to modify interactions with other materials in contact with the surface. The geometry, dimensions, and positioning on the surface define the function of a texture and its properties. This work reviews and discuss the wide range of texturing technologies available in the industry. The advantages and limitations of each technology are presented to support the development of new surface engineering applications in the plastics manufacturing industry.