Numerical and Experimental Studies on the Improvement of Gas Chamber Structure during Gas-Assisted Extrusion

In the gas-assisted extrusion process, the melt inside the die is in a low-viscosity molten state, so the flow field of the gas cushion layer has a great effect on the cross-sectional shape of the micro-tube. Therefore, this study establishes the gas distribution chamber model of the gas-assisted die. Ansys Fluent software was used to simulate the gas flow field of the gas distribution chamber. The effect of the gas chamber structure on the size of the micro-tube was analyzed by the extrusion experiment. The research shows that the velocity unevenness coefficient of the gas outlet of the single gas chamber die is 11.8%, which is higher than that of the double gas chamber die. The use of a double gas chamber die can improve the stability of the gas cushion layer and the wall thickness non-uniformity of the micro-tube, which verifies the simulation results.

Effect of Pressure Difference between Inner and Outer Gas Layer on Micro-Tube Deformation during Gas-Assisted Extrusion

In the process of double-layer gas-assiste extrusion of a plastic micro-tube, the tugging effect caused by the pressure difference of the gas cushion layer inside the die has a great influence on the external dimensions of the micro-tube. Therefore, this study establishes a two-phase extrusion model based on compressible gas and incompressible melt. Ansys Polyflow finite element software was used to numerically simulate the extrusion process of the melt to analyze the effect of the gas cushion layer pressure difference on the micro-tube deformation. The research shows that the shrinkage rate of the micro-tube increases with increasing pressure of the outer cushion layer, and the degree of tube wall migration increases, too. In the process of extrusion, the first normal stress difference at the entrance of the gas cushion layer shows a significant effect on the melt velocity field distribution and the extruded micro-tube cross-sectional deformation.