Bonding Efficacy and Fracture Pattern of Adhesives Submitted to Mechanical Aging with the Rub&Roll Device

Bond Strength to Microtraction and Nanofiltration Using Ethanol Wet Bonding Technique in Fresh Extracted Teeth: An Ex Vivo Study

Objective

The objective of this study was to evaluate the bond strength to microtraction and nanofiltration using ethanol wet bonding technique in fresh extracted teeth.

Materials and Methods

This quasi-experimental ex vivo study evaluated 48 teeth that had an indication of premolar extraction due to orthodontic reasons. The protocol of dental preparation and restorative procedure was carried out to evaluate the adhesion resistance by means of the universal testing machine at a loading speed of 0.5 mm/min and 500MPa. To evaluate the nanofiltration, matches were made that were immersed in ammoniac silver nitrate for 24h, and then the specimens impregnated with silver were washed thoroughly in distilled water and placed in a photo-developer solution for 8h under a fluorescent light. All statistical analyses were statistically evaluated with a level of significance P < 0.05.

Results

The ethanol technique without premature failure (PF) group had an average of 31.26 ± 10.26MPa, whereas the lowest value was found in the water technique group with PF, which had 22.59 ± 12.27MPa. When performing inferential statistics, it was evidenced that there were statistically significant differences between both techniques with a value of P < 0.05.

Conclusion

According to the results in both cases, the adhesive strength showed superiority in the ethanol wash group. It determines that this technique presents greater tolerance to the residual presence of water. Finally, in relation to nanofiltration we found that there were no significant differences between the groups evaluated.

Mimicking and Measuring Occlusal Erosive Tooth Wear with the "Rub&Roll" and Non-contact Profilometry

Chewing, drinking, and occasional tooth grinding will result in physiological tooth wear during a lifetime. Extreme challenges, such as bruxism or habitual chewing on foreign objects, may lead to excessive wear. Recently, the role of erosion in accelerating mechanical tooth wear has been recognized, but the interplay between chemical and mechanical wear processes has not been extensively studied. Our laboratory recently introduced a novel oral wear simulation device, the Rub&Roll, that enables the user to perform wear and loading studies separately or simultaneously in an erosive and/or abrasive environment. This manuscript describes an application of the device: the combined mechanical and erosive loading of extracted human (pre)molars in a simulated chewing movement, with a controlled application of force, velocity, fluid, and time, and the application of non-contact profilometry in visualizing and measuring the resulting wear pattern. The occlusal morphology that was created in the experiment with the highest loading level is very similar to the clinical presentation of erosive wear.