Mimicking Natural Microenvironments: Design of 3D-Aligned Hybrid Scaffold for Dentin Regeneration

Biomineralization: A new tool for developing eco-sustainable Ti-doped hydroxyapatite-based hybrid UV filters

It is well known that the prolonged exposure to UV radiation from sunlight can compromise human health and is particularly damaging to the skin, leading to sunburn, photo-aging and skin cancer. Sunscreen formulations containing UV-filters present a barrier against solar UV and help to mitigate the harmful effects however, concern about their safety for both human and environmental health is still a much-debated topic. EC regulations classify UV-filters depending on their chemical nature, particle size, and mechanism of action. Furthermore, it regulates their use in cosmetic products with specific limitations in terms of concentration (organic UV filters) and particle size and surface modification to reduce their photo-activity (mineral UV filters). The regulations have prompted researchers to identify new materials that show promise for use in sunscreens. In this work, biomimetic hybrid materials composed of titanium-doped hydroxyapatite (TiHA) grown on two different organic templates, derived from animal (gelatin - from pig skin) and vegetable (alginate - from algae) sources. These novel materials were developed and characterized to obtain sustainable UV-filters as a safer alternative for both human and ecosystem health. This 'biomineralization' process yielded TiHA nanoparticles that demonstrated high UV reflectance, low photoactivity, good biocompatibility and an aggregate morphology which prevents dermal penetration. The materials are safe for topical application and for the marine environment; moreover, they can protect organic sunscreen components from photodegradation and yield long-lasting protection.

Applications of Hydrogels in Drug Delivery for Oral and Maxillofacial Diseases

Oral and maxillofacial diseases have an important impact on local function, facial appearance, and general health. As a multifunctional platform, hydrogels are widely used in the biomedical field due to their excellent physicochemical properties. In recent years, a large number of studies have been conducted to adapt hydrogels to the complex oral and maxillofacial environment by modulating their pore size, swelling, degradability, stimulus-response properties, etc. Meanwhile, many studies have attempted to use hydrogels as drug delivery carriers to load drugs, cytokines, and stem cells for antibacterial, anticancer, and tissue regeneration applications in oral and maxillofacial regions. This paper reviews the application and research progress of hydrogel-based drug delivery systems in the treatment of oral and maxillofacial diseases such as caries, endodontic diseases, periodontal diseases, maxillofacial bone diseases, mucosal diseases, oral cancer, etc. The characteristics and applications of hydrogels and drug-delivery systems employed for the treatment of different diseases are discussed in order to provide a reference for further research on hydrogel drug-delivery systems in the future.

Functional role of inorganic trace elements in dentin apatite tissue-Part 1: Mg, Sr, Zn, and Fe

Many essential elements exist in nature with significant influence on dentin and bone apatite tissue. Hydroxyapatite (HAp) is the major inorganic crystalline structure of dentin that provides a site for various physiological functions such as surface layer ion exchange. Decades of apatite research have shown that enamel is a high-substituted crystalline apatite, but recent findings suggest that dentin apatite may play a more important role in regulating ion exchange as well as mineral crystallinity. This article is the first part of a review series on the functional role of inorganic trace elements including magnesium, strontium, zinc, and iron in dentin hydroxyapatite. The morphology, physiology, crystallinity, and solubility of these elements as they get substituted into the HAp lattice are extensively discussed. An electronic search was performed on the role of these elements in dentin apatite from January 2007 to September 2021. The relationship between different elements and their role in the mineral upkeep of dentin apatite was evaluated. Several studies recognized the role of these elements in dentinal apatite composition and its subsequent effects on morphology, crystallinity, and solubility. These elements are of great importance in physiological processes and an essential part of living organisms. Magnesium and strontium stimulate osteoblast activity, while zinc can improve overall bone quality with its antibacterial properties. Iron nanoparticles are also vital in promoting bone tissue growth as they donate or accept electrons in redox reactions. Thus, understanding how these elements impact dentin apatite structure is of great clinical significance.

Additive-Free Gelatine-Based Devices for Chondral Tissue Regeneration: Shaping Process Comparison among Mould Casting and Three-Dimensional Printing

Gelatine is a well-known and extensively studied biopolymer, widely used in recent decades to create biomaterials in many different ways, exploiting its molecular resemblance with collagen, the main constituent of the extra-cellular matrix, from which it is derived. Many have employed this biopolymer in tissue engineering and chemically modified (e.g., gelatin methacryloyl) or blended it with other polymers (e.g., alginate) to modulate or increase its performances and printability. Nevertheless, little is reported about its use as a stand-alone material. Moreover, despite the fact that multiple works have been reported on the realization of mould-casted and three-dimensional printed scaffolds in tissue engineering, a clear comparison among these two shaping processes, towards a comparable workflow starting from the same material, has never been published. Herein, we report the use of gelatine as stand-alone material, not modified, blended, or admixed to be processed or crosslinked, for the realization of suitable scaffolds for tissue engineering, towards the two previously mentioned shaping processes. To make the comparison reliable, the same pre-process (e.g., the gelatin solution preparation) and post-process (e.g., freeze-drying and crosslinking) steps were applied. In this study, gelatine solution was firstly rheologically characterized to find a formulation suitable for being processed with both the shaping processes selected. The realized scaffolds were then morphologically, phisico-chemically, mechanically, and biologically characterized to determine and compare their performances. Despite the fact that the same starting material was employed, as well as the same pre- and post-process steps, the two groups resulted, for most aspects, in diametrically opposed characteristics. The mould-casted scaffolds that resulted were characterized by small, little-interconnected, and random porosity, high resistance to compression and slow cell colonization, while the three-dimensional printed scaffolds displayed big, well-interconnected, and geometrically defined porosity, high elasticity and recover ability after compression, as well as fast and deep cell colonization.

Mineralizing Gelatin Microparticles as Cell Carrier and Drug Delivery System for siRNA for Bone Tissue Engineering

The local release of complexed siRNA from biomaterials opens precisely targeted therapeutic options. In this study, complexed siRNA was loaded to gelatin microparticles cross-linked (cGM) with an anhydride-containing oligomer (oPNMA). We aggregated these siRNA-loaded cGM with human mesenchymal stem cells (hMSC) to microtissues and stimulated them with osteogenic supplements. An efficient knockdown of chordin, a BMP-2 antagonist, caused a remarkably increased alkaline phosphatase (ALP) activity in the microtissues. cGM, as a component of microtissues, mineralized in a differentiation medium within 8–9 days, both in the presence and in the absence of cells. In order to investigate the effects of our pre-differentiated and chordin-silenced microtissues on bone homeostasis, we simulated in vivo conditions in an unstimulated co-culture system of hMSC and human peripheral blood mononuclear cells (hPBMC). We found enhanced ALP activity and osteoprotegerin (OPG) secretion in the model system compared to control microtissues. Our results suggest osteoanabolic effects of pre-differentiated and chordin-silenced microtissues.

3D Printed In Vitro Dentin Model to Investigate Occlusive Agents against Tooth Sensitivity

Tooth sensitivity is a painful and very common problem. Often stimulated by consuming hot, cold, sweet, or acidic foods, it is associated with exposed dentin microtubules that are open to dental pulp. One common treatment for tooth hypersensitivity is the application of occlusive particles to block dentin microtubules. The primary methodology currently used to test the penetration and occlusion of particles into dentin pores relies upon dentin discs cut from extracted bovine/human teeth. However, this method is limited due to low accessibility to the raw material. Thus, there is a need for an in vitro dentin model to characterize the effectiveness of occlusive agents. Three-dimensional printing technologies have emerged that make the printing of dentin-like structures possible. This study sought to develop and print a biomaterial ink that mimicked the natural composition and structure of dentin tubules. A formulation of type I collagen (Col), nanocrystalline hydroxyapatite (HAp), and alginate (Alg) was found to be suitable for the 3D printing of scaffolds. The performance of the 3D printed dentin model was compared to the natural dentin disk by image analysis via scanning electron microscopy (SEM), both pre- and post-treatment with occlusive microparticles, to evaluate the degree of dentinal tubule occlusion. The cytocompatibility of printed scaffolds was also confirmed in vitro. This is a promising biomaterial system for the 3D printing of dentin mimics.

Calcium-Based Biomineralization: A Smart Approach for the Design of Novel Multifunctional Hybrid Materials

Biomineralization consists of a complex cascade of phenomena generating hybrid nano-structured materials based on organic (e.g., polymer) and inorganic (e.g., hydroxyapatite) components. Biomineralization is a biomimetic process useful to produce highly biomimetic and biocompatible materials resembling natural hard tissues such as bones and teeth. In detail, biomimetic materials, composed of hydroxyapatite nanoparticles (HA) nucleated on an organic matrix, show extremely versatile chemical compositions and physical properties, which can be controlled to address specific challenges. Indeed, different parameters, including (i) the partial substitution of mimetic doping ions within the HA lattice, (ii) the use of different organic matrices, and (iii) the choice of cross-linking processes, can be finely tuned. In the present review, we mainly focused on calcium biomineralization. Besides regenerative medicine, these multifunctional materials have been largely exploited for other applications including 3D printable materials and in vitro three-dimensional (3D) models for cancer studies and for drug testing. Additionally, biomineralized multifunctional nano-particles can be involved in applications ranging from nanomedicine as fully bioresorbable drug delivery systems to the development of innovative and eco-sustainable UV physical filters for skin protection from solar radiations.