Influence of K2NbF7 Catalyst on the Desorption Behavior of LiAlH4

Improved dehydrogenation performance of LiAlH4 doped with BaMnO3

Due to its high gravimetric capacity of hydrogen (10.5 wt%), LiAlH4 has been regarded as a promising material for solid-state hydrogen storage material for onboard usage. However, high decomposition temperature, poor kinetics and irreversibility retard its application. To counter this problem, various weight percentages of BaMnO3 are introduced into the LiAlH4 system as an additive in this work. As a result, the starting hydrogen release of LiAlH4 was reduced to 109-115 °C and the second desorption temperature occurred at around 134-158 °C, much lower than pure LiAlH4. The isothermal desorption kinetics also proved that faster desorption kinetics can be observed at 90 °C for 80 min. About 2.00-2.60 wt% of H2 could be desorbed by the composite, whereas only <1.00 wt% of H2 was desorbed by undoped LiAlH4. Additionally, adding BaMnO3 reduced the activation energies by 30 kJ/mol for the first stages and 34 kJ/mol for the second stages. Based on the X-ray diffraction result, the active species formed of MnO2 and Ba or Ba-containing materials are believed to be responsible for the noticeable enhancement in the desorption properties of LiAlH4.

Paving the Way to the Fuel of the Future-Nanostructured Complex Hydrides

Hydrides have emerged as strong candidates for energy storage applications and their study has attracted wide interest in both the academic and industry sectors. With clear advantages due to the solid-state storage of hydrogen, hydrides and in particular complex hydrides have the ability to tackle environmental pollution by offering the alternative of a clean energy source: hydrogen. However, several drawbacks have detracted this material from going mainstream, and some of these shortcomings have been addressed by nanostructuring/nanoconfinement strategies. With the enhancement of thermodynamic and/or kinetic behavior, nanosized complex hydrides (borohydrides and alanates) have recently conquered new estate in the hydrogen storage field. The current review aims to present the most recent results, many of which illustrate the feasibility of using complex hydrides for the generation of molecular hydrogen in conditions suitable for vehicular and stationary applications. Nanostructuring strategies, either in the pristine or nanoconfined state, coupled with a proper catalyst and the choice of host material can potentially yield a robust nanocomposite to reliably produce H2 in a reversible manner. The key element to tackle for current and future research efforts remains the reproducible means to store H2, which will build up towards a viable hydrogen economy goal. The most recent trends and future prospects will be presented herein.

Improved Dehydrogenation Properties of LiAlH4 by Addition of Nanosized CoTiO3

Despite the application of lithium aluminium hydride (LiAlH4) being hindered by its sluggish desorption kinetics and unfavourable reversibility, LiAlH4 has received special attention as a promising solid-state hydrogen storage material due to its hydrogen storage capacity (10.5 wt.%). In this work, investigated for the first time was the effect of the nanosized cobalt titanate (CoTiO3) which was synthesised via a solid-state method on the desorption behaviour of LiAlH4. Superior desorption behaviour of LiAlH4 was attained with the presence of a CoTiO3 additive. By means of the addition of 5, 10, 15 and 20 wt.% of CoTiO3, the initial desorption temperature of LiAlH4 for the first stage was reduced to around 115−120 °C and the second desorption stage was reduced to around 144−150 °C, much lower than for undoped LiAlH4. The LiAlH4-CoTiO3 sample also presents outstanding desorption kinetics behaviour, desorbing hydrogen 30−35 times faster than undoped LiAlH4. The LiAlH4-CoTiO3 sample could desorb 3.0−3.5 wt.% H2 in 30 min, while the commercial and milled LiAlH4 desorbs <0.1 wt.% H2. The apparent activation energy of the LiAlH4-CoTiO3 sample based on the Kissinger analysis was decreased to 75.2 and 91.8 kJ/mol for the first and second desorption stage, respectively, lower by 28.0 and 24.9 kJ/mol than undoped LiAlH4. The LiAlH4-CoTiO3 sample presents uniform and smaller particle size distribution compared to undoped LiAlH4, which is irregular in shape with some agglomerations. The experimental results suggest that the CoTiO3 additive promoted notable advancements in the desorption performance of LiAlH4 through the in situ-formed AlTi and amorphous Co or Co-containing active species that were generated during the desorption process.