Retained Austenite Destabilization during Tempering of Low-Temperature Bainite

Kinetics of Martensite/Austenite Decomposition during Tempering of Ultrafine Nano-Bainitic Steels

In this study, the decomposition of a martensite/austenite (M/A) microconstituent in bainitic steels was analyzed using differential scanning calorimetry (DSC) data in conjunction with Kissinger's and Johnson-Mehl-Avrami-Kolmogorov (JMAK)'s formulas. In bainitic steel subjected to austempering heat treatment, the presence of an M/A microstructure adversely affects the mechanical properties. According to the kinetic equations derived, it is observed that after tempering the sample at 600 °C for 4000 s, the generation of each phase reaches its maximum. The SEM images taken before and after tempering reveal extensive decomposition of the M/A constituent in the microstructure. The proportion of the M/A microstructure decreased significantly from about 10% before tempering to less than 1% after. Additionally, the content of residual austenite also reduced nearly to zero. These observations are consistent with the predictions of the kinetic equations.

Strength-Toughness of a Low-Alloy 0.25C Steel Treated by Q&P Processing

Quenching and partitioning (Q&P) treatments were applied to 0.25C steel to produce the microstructures that exhibit an improved balance of mechanical properties. The simultaneous bainitic transformation and carbon enrichment of retained austenite (RA) during the partitioning stage at 350 °C result in the coexistence of RA islands with irregular shapes embedded in bainitic ferrite and film-like RA in the martensitic matrix. The decomposition of coarse RA islands and the tempering of primary martensite during partitioning is accompanied by a decrease in the dislocation density and the precipitation/growth of η-carbide in the lath interiors of primary martensite. The best combinations of a yield strength above 1200 MPa and an impact toughness of about 100 J were obtained in the steel samples quenched to 210-230 °C and subjected to partitioning at 350 °C for 100-600 s. A detailed analysis of the microstructures and the mechanical properties of the steel subjected to Q&P, water quenching, and isothermal treatment revealed that the ideal strength-toughness combinations could be attributed to the mixture of the tempered lath martensite with finely dispersed and stabilized RA and the particles of η-carbide located in the lath interiors.

Controlling the Thermal Stability of a Bainitic Structure by Alloy Design and Isothermal Heat Treatment

The aim of this work was to develop a novel bainitic steel that will be specifically dedicated to achieving a high degree of refinement (nano- or submicron scale) along with increased thermal stability of the structure at elevated temperatures. The material was characterized by improved in-use properties, expressed as the thermal stability of the structure, compared to nanocrystalline bainitic steels with a limited fraction of carbide precipitations. Assumed criteria for the expected low martensite start temperature, bainitic hardenability level, and thermal stability are specified. The steel design process and complete characteristics of the novel steel including continuous cooling transformation and time-temperature-transformation diagrams based on dilatometry are presented. Moreover, the influence of bainite transformation temperature on the degree of structure refinement and dimensions of austenite blocks was also determined. It was assessed whether, in medium-carbon steels, it is possible to achieve a nanoscale bainitic structure. Finally, the effectiveness of the applied strategy for enhancing thermal stability at elevated temperatures was analyzed.

Viewpoints on Technological Aspects of Advanced High-Strength Bainitic Steels

The development of advanced high-strength bainitic steels has been preceded and linked to different metallurgical advances, both in the field of fundamental materials science and in technological fields closer to the production and final application. The diversity and abundance of documents in literature has favored the co-existence of extensive terminology in the context of advanced high-strength steels and bainitic steels. In this work, the concept of advanced high-strength bainitic steels is briefly revisited from a wide perspective, with the aim of highlighting the main limitations and challenges for further development of these microstructures.