Fabrication of Cu1.5Mn1.5O4 Nanoparticles Using One Step Self-Assembling Route to Enhance Energy Consumption

Effects of Zinc Substitution on the Microstructural and Magnetic Characteristics of Cubic Symmetry Nickel Ferrite System

The preparation of ZnxNi1−xFe2O4 (x = 0 and 0.3) nanoparticles using glycine-mediated combustion route was successfully completed depending on the zwitterion and combustion characteristics of glycine. Using a variety of methods, including XRD, FTIR, SEM/EDX, and TEM, the investigated ferrites were characterized. XRD and FTIR analyses confirm that Zn0.3Ni0.7Fe2O4 and NiFe2O4 nanoparticles crystallize in the cubic symmetry in the space group Fd3m. An increase in the lattice parameters and a subsequent decrease in crystallite size were caused by the process of replacing Ni ions with Zn ions. In accordance with Waldron’s hypothesis, FTIR spectra demonstrate that the ferrites have a spinel-type structure as they are produced. The substitution process by Zn led to different changes in the half band widths with subsequent in splitting in the absorption band around 400 cm−1. The examined ferrites’ cation distribution showed that Zn2+ and Ni2+ ions favored the tetrahedral (A) and octahedral (B) sites, respectively, while Fe3+ ions occupied both A- and B-sites, providing mixed spinel ferrite. TEM analysis indicates the formation of spinel nanocrystalline particles with low agglomerations. The particle size of the as-synthesized ferrites did not exceed 16 nm. By applying the VSM approach at room temperature, the magnetic characteristics of the ferrites under investigation were established. The magnetization of Zn0.3Ni0.7Fe2O4 nanoparticles was found to be higher than that of NiFe2O4 nanoparticles according to the magnetic data. Increasing the magnetization and the experimental magnetic moment of Zn0.3Ni0.7Fe2O4 were accompanied by a decreasing of its coercivity. The net magnetization is oriented along different high symmetry directions. On the other hand, the anisotropy of the nickel ferrite increases by substituting Ni with a Zn ion.

Green Synthesis and Pinning Behavior of Fe-Doped CuO/Cu2O/Cu4O3 Nanocomposites

Egg white-induced auto combustion has been used to synthesize undoped and Fe-doped CuO/Cu2O/Cu4O3 nanocomposites in a soft, secure, and one-pot procedure. X-ray powder diffraction (XRD) and Fourier transform infrared (FTIR) investigations have been used to identify functional groups and the structural properties of crystalline phases present in the as-synthesized composites. Scanning Electron Microscopy/Energy Dispersive Spectrometry (SEM/EDS) elemental mapping analyses and Transmission Electron Microscopy (TEM) techniques were used to explore the morphological and compositional properties of these composites. N2- adsorption/desorption isotherm models have been used to examine the surface variables of the as-prepared systems. Based on the Vibrating Sample Magnetometer (VSM) technique, the magnetic properties of various copper-based nanocomposites were detected due to being Fe-doped. XRD results showed that the undoped system was composed of CuO as a major phase with Cu2O and Cu4O3 as second phases that gradually disappeared by increasing the dopant content. The crystalline phase’s crystallographic properties were determined. The average particle size was reduced when the synthesized systems were doped with Fe. The construction of porous and polycrystalline nanocomposites involving Cu, Fe, O, and C components was confirmed by SEM/EDS and TEM measurements. In terms of the increase in magnetization of the as-manufactured nanocomposites due to Fe-doping, oxygen vacancies at the surface/or interfacial of nanoparticles, while also domain wall pinning mechanisms, were investigated. Finally, employing the investigated production process, Fe doping of CuO/Cu2O/Cu4O3 nanocomposite resulted in the development of a single phase (CuO) exhibiting “pinned” type magnetization. This is the first publication to show that CuO/Cu2O/Cu4O3.