Green and Efficient Processing of Wood with Supercritical CO2: A Review

Effect of NaOH Pretreatment on Permeability and Surface Properties of Three Wood Species

To improve the permeability of wood, three chemical reagents were used to pretreat Chinese fir, white oak, and poplar. Through a factorial experiment with the mass change rate of the wood as the indicator, NaOH was preliminarily selected as the pretreatment agent. Further orthogonal experiments were conducted to explore the effects of NaOH concentration, temperature, and treatment time on the mass change rate, dye uptake rate, transverse dye penetration rate, and color difference of the wood. A fuzzy, comprehensive analysis was used to optimize the pretreatment process. The results showed that after NaOH pretreatment, the highest mass change rates of Chinese fir, white oak, and poplar were 11.30, 10.66, and 8.53%, respectively. Compared with untreated wood, the dye uptake rate of three wood species increased by 1.05, 1.43, and 1.13 times, respectively; the radial dye penetration rate increased by 5.05, 4.14, and 3.38 times, respectively; and the tangential dye penetration rate increased by 3.91, 3.45, and 3.84 times, respectively. These findings indicate an enhancement in permeability for all three wood species following NaOH pretreatment. The brightness of the three wood species decreased after NaOH pretreatment, while the yellow and red colors increased in Chinese fir and poplar and decreased in white oak. Scanning electron microscopy showed that pits in the wood opened after pretreatment, while extractives decreased. Infrared spectroscopy analysis indicated varying degrees of extraction effects from NaOH pretreatment across the three wood species, along with increased active hydroxyl groups within the wood structure. X-ray diffraction analysis revealed that NaOH dissolved noncrystalline substances in wood, leading to improved crystallinity. These experimental findings provide essential data for future endeavors in wood pretreatment and subsequent staining processes.

Effect of Temperature and Pressure of Supercritical CO2 on Dewatering, Shrinkage and Stresses of Eucalyptus Wood

Supercritical CO2 (SuCO2) dewatering can mitigate capillary tension and reduce wood collapse. In this study, Eucalyptus urophylla × E. grandis specimens were dewatered by SuCO2 at temperatures of 35, 40 and 55 °C, in pressures of 10 and 30 MPa, respectively, for 1h. Effects of temperature and pressure on dewatering rate, moisture content (MC) distribution and gradient, shrinkage and residual stress of wood after dewatering were investigated. The results indicate that the SuCO2 dewatering rate is much faster than that of conventional kiln drying (CKD). The dewatering rate increases with increasing of temperature and pressure; however, pressure has a significant influence, especially for the high-temperature dewatering process; the MC distribution after 1h dewatering is uneven and MC gradients decrease with reducing of mean final MC of wood. MC gradients along radial direction are much smaller than that in tangential direction; collapse of wood significantly reduces after dewatering due to SuCO2 decreasing the capillary tension, and residual stress of wood during dewatering is mainly caused by pressure of SuCO2, which decreases with increasing temperature. SuCO2 dewatering has great potential advantages in water-removal of wood prone to collapse or deformation.