Bio-Corrosion Behavior of Ceramic Coatings Containing Hydroxyapatite on Mg-Zn-Ca Magnesium Alloy

Review of the Effect of Surface Coating Modification on Magnesium Alloy Biocompatibility

Magnesium alloy, as an absorbable and implantable biomaterial, has been greatly developed in the application field of biomaterials in recent years due to its excellent biocompatibility and biomechanics. However, due to the poor corrosion resistance of magnesium alloy in the physiological environment, the degradation rate will be unbalanced, which seriously affects the clinical use. There are two main ways to improve the corrosion resistance of magnesium alloy: one is by adding alloying elements, the other is by surface modification technology. Compared with adding alloy elements, the surface coating modification has the following advantages: (1) The surface coating modification is carried out without changing the matrix elements of magnesium alloy, avoiding the introduction of other elements; (2) The corrosion resistance of magnesium alloy can be improved by relatively simple physical, chemical, or electrochemical improvement. From the perspective of corrosion resistance and biocompatibility of biomedical magnesium alloy materials, this paper summarizes the application and characteristics of six different surface coating modifications in the biomedical magnesium alloy field, including chemical conversion method, micro-arc oxidation method, sol-gel method, electrophoretic deposition, hydrothermal method, and thermal spraying method. In the last section, it looks forward to the development prospect of surface coating modification and points out that preparing modified coatings on the implant surface combined with various modification post-treatment technologies is the main direction to improve biocompatibility and realize clinical functionalization.

Synergistic effect of deep ball burnishing and HA coating on surface integrity, corrosion and immune response of biodegradable AZ31B Mg alloys

The fast degradation and consequent loss of mechanical integrity is a major problem of biodegradable Mg alloy, which limits its clinical viability. This paper presents the influence of a synergistic approach combining deep ball burnishing and hydroxyapatite (HA) coating on biomechanical integrity, degradation and immune response of Mg alloy (AZ31B). The burnishing resulted in smooth surface topography, increased hardness from 0.87 to 1.45 GPa and induced microstructural disturbances with deformation twins/twin bands, which enabled formation of a dense and compact platelet-like crystals HA coating of 110 μm thickness. Compared to the untreated and burnished specimens, the burnished + HA coated surface provided remarkably higher corrosion resistance as indicated by lower corrosion current density and smaller mass loss. HA coating and surface integrity enhancement by burnishing were predominantly responsible for improved corrosion resistance. HA coating on the burnished surface exhibited hydrophilic properties and adequate bonding strength. While the modified surfaces promoted cell growth, the burnished + HA surface outperformed in exhibiting less pro-inflammatory and high anti-inflammatory cytokines, demonstrating that the treated surfaces were not posing any threat to immune cells. The findings indicate that the synergistic surface treatment can be a viable means to enhance corrosion resistance and immune response of Mg alloys implants.