Development and Characterization of a Poly (Vinyl Alcohol)/Graphene Oxide Composite Hydrogel as An Artificial Cartilage Material

Sodium alginate/polyvinyl alcohol semi-interpenetrating hydrogels reinforced with PEG-grafted-graphene oxide

Semi-interpenetrating polymer network (SIPN) hydrogels composed of sodium alginate/poly (vinyl alcohol), reinforced by PEG-grafted-graphene oxide (GO-g-PEG) were prepared by ionic crosslinking of sodium alginate. The impact of grafted PEG molecular weight with two molecular weights, i.e. 400 and 2000 g/mol, and component composition were studied on the morphology, swelling behavior, mechanical and dynamic properties. SEM observation showed fine dispersion and distribution of GO-g-PEG throughout the hydrogel indicating a good interaction of particles with the components. Our results revealed that although incorporating GO-g-PEG increases the water content, it significantly enhances the mechanical properties, i.e. tensile modulus, elongation at break, and fracture toughness with a more pronounced impact at higher PEG molecular weight. As a result, the tensile modulus and the elongation at break increased by 270 % and 28 %, respectively. The SA/PVA SIPN hydrogels reinforced with the GO-g-PEG exhibit a non-linear elastic behavior with a toe at low strains. This behavior is attributed to the unique structural features of SIPN hydrogels and the orientation of GO-g-PEG particles with proper interaction with the components. The small amplitude oscillatory shear was also performed to further study the impact of SA, PVA, and GO-g-PEG compositions on the microstructure of hydrogels.

Enhancing the Mechanical Properties of Poly(vinyl alcohol) Fibers by Lithium Iodide Addition

The effect of lithium iodide (LiI) on the mechanical strength, properties, and molecular orientation of poly(vinyl alcohol) (PVA) fibers spun by wet spinning and then heat-stretched was studied. The stretchability of LiI-PVA fibers was improved, and the rupture during stretching was suppressed compared to PVA fibers. In addition, the tensile strength and elastic modulus of the thermally stretched fibers have been significantly improved. It was also found that the addition of LiI improves the molecular orientation of PVA. This was achieved because LiI reduced the hydrogen bonds between the molecular chains of PVA, resulting in reduced crystallinity. Most of the LiI in the fiber could be removed by a coagulation bath and washing during the spinning process. This means that LiI is eventually removed, and the heat-treatment strengthens the hydrogen bonds, resulting in excellent mechanical strength.

Adjusting Some Properties of Poly(methacrylic acid) (Nano)Composite Hydrogels by Means of Silicon-Containing Inorganic Fillers

The present work aims to show how the main properties of poly(methacrylic acid) (PMAA) hydrogels can be engineered by means of several silicon-based fillers (Laponite XLS/XLG, montmorillonite (Mt), pyrogenic silica (PS)) employed at 10 wt% concentration based on MAA. Various techniques (FT-IR, XRD, TGA, SEM, TEM, DLS, rheological measurements, UV-VIS) were used to comparatively study the effect of these fillers, in correlation with their characteristics, upon the structure and swelling, viscoelastic, and water decontamination properties of (nano)composite hydrogels. The experiments demonstrated that the nanocomposite hydrogel morphology was dictated by the way the filler particles dispersed in water. The equilibrium swelling degree (SDe) depended on both the pH of the environment and the filler nature. At pH 1.2, a slight crosslinking effect of the fillers was evidenced, increasing in the order Mt < Laponite < PS. At pH > pKaMAA (pH 5.4; 7.4; 9.5), the Laponite/Mt-containing hydrogels displayed a higher SDe as compared to the neat one, while at pH 7.4/9.5 the PS-filled hydrogels surprisingly displayed the highest SDe. Rheological measurements on as-prepared hydrogels showed that the filler addition improved the mechanical properties. After equilibrium swelling at pH 5.4, G’ and G” depended on the filler, the Laponite-reinforced hydrogels proving to be the strongest. The (nano)composite hydrogels synthesized displayed filler-dependent absorption properties of two cationic dyes used as model water pollutants, Laponite XLS-reinforced hydrogel demonstrating both the highest absorption rate and absorption capacity. Besides wastewater purification, the (nano)composite hydrogels described here may also find applications in the pharmaceutical field as devices for the controlled release of drugs.

Special Issue: Nanocomposite Hydrogels for Biomedical Applications

A hydrogel consists of a three-dimensional network of polymer chains, with water as a solvent in the system [...]

Polyvinyl alcohol modified polyvinylidene fluoride-graphene oxide scaffold promotes osteogenic differentiation potential of human induced pluripotent stem cells

Tissue engineering is fast becoming a key approach in bone medicine studies. Designing the ideally desirable combination of stem cells and scaffolds are at the hurt of efforts for producing implantable bone substitutes. Clinical application of stem cells could be associated with serious limitations, and engineering scaffolds that are able to imitate the important features of extracellular matrix is a major area of challenges within the field. In this study, electrospun scaffolds of polyvinylidene fluoride (PVDF), PVDF-graphene oxide (GO), PVDF-polyvinyl alcohol (PVA) and PVDF-PVA-GO were fabricated to study the osteogenic differentiation potential of human induced pluripotent stem cells (iPSCs) while cultured on fabricated scaffolds. Scanning electron microscopy study, viability assay, relative gene expression analysis, immunocytochemistry, alkaline phosphates activity, and calcium content assays confirmed that the osteogenesis rate of hiPSCs cultured on PVDF-PVA-Go is significantly higher than other scaffolds. Here, we showed that the biocompatible, nontoxic, flexible, piezoelectric, highly porous and interconnected three-dimensional structure of electrospun PVDF-PVA-Go scaffold in combination with hiPSCs (as the stem cells with significant advantageous in comparison to other types) makes them a highly promising scaffold-stem cell system for bone remodeling medicine. There was no evidence for the superiority of PVDF-GO or PVDF-PVA scaffold for osteogenesis, compared to each other; however both of them showed better potentials as to PVDF scaffold.