Picosecond Pulsed Laser Deposition of Metals and Metal Oxides

In this work, we present the fabrication of thin films/nanostructures of metals and metal oxides using picosecond laser ablation. Two sets of experiments were performed: the depositions were carried out in vacuum and in air at atmospheric pressure. The subjects of investigation were the noble metals Au and Pt and the metal oxides ZnO and TiO2. We studied and compared the phase composition, microstructure, morphology, and physicochemical state of the as-deposited samples' surfaces in vacuum and in air. It was found that picosecond laser ablation performed in vacuum led to the fabrication of thin films with embedded and differently sized nanoparticles. The implementation of the same process in air at atmospheric pressure resulted in the fabrication of porous nanostructures composed of nanoparticles. The ablation of pure Pt metal in air led to the production of nanoparticles with an oxide shell. In addition, more defects were formed on the metal oxide surface when the samples were deposited in vacuum. Furthermore, the laser ablation process of pure Au metal in a picosecond regime in vacuum and in air was theoretically investigated using molecular dynamics simulation.

Property-governed performance of platinum-modified titania photocatalysts

Titania is probably the most widely investigated semiconductor photocatalyst because of various advantages, such as high activity, thermal and chemical stability, low price, abundance, and negligible toxicity. However, pristine titania is also characterized by charge carriers’ recombination, and thus lower quantum yields of photocatalytic reactions than theoretical 100%. Moreover, its wide bandgap, despite being recommended for excellent redox properties, means also inactivity under visible part of solar radiation. Accordingly, titania has been surface modified, doped and coupled with various elements/compounds. For example, platinum deposited on the surface of titania has shown to improve both UV activity and the performance under vis. Although the studies on titania modification with platinum started almost half a century ago, and huge number of papers have been published up to now, it is unclear which properties are the most crucial and recommended to obtain highly efficient photocatalyst. In the literature, the opposite findings could be found on the property-governed activities that could result from huge differences in the reaction systems, and also examined photocatalysts. Considering the platinum properties, its content, the size of nanoparticles and the oxidation state, must be examined. Obviously, the characteristics of titania also influence the resultant properties of deposited platinum, and thus the overall photocatalytic performance. Although so many reports on Pt/TiO₂ have been published, it is hardly possible to give indispensable advice on the recommended properties. However, it might be concluded that usually fine platinum NPs uniformly deposited on the titania surface result in high photocatalytic activity, and thus in the low optimal content of necessary platinum. Moreover, the aggregation of titania particles might also help in the lowering the necessary platinum amount (even to 0.2 wt%) due to the interparticle electron transfer mechanism between titania particles in one aggregate. In respect of platinum state, it is thought that it is highly substrate-specific case, and thus either positively charged or zero valent platinum is the most recommended. It might be concluded that despite huge number of papers published on platinum-modified titania, there is still a lack of comprehensive study showing the direct correlation between only one property and the resultant photocatalytic activity.

Highly Photoactive Titanium Dioxide Supported Platinum Catalyst: Synthesis Using Cleaner Ultrasound Approach

Catalysts increase reaction rates; however, the surface area to volume ratio of catalysts has a vital role in catalytic activity. The noble metals such as platinum (Pt) and gold (Au) are expensive; despite this, they have proven their existence in catalysis, motivating the synthesis of supported metal catalysts. Metal catalysts need to be highly dispersed onto the support. In this investigation, an ultrasound approach has been attempted to synthesise highly photoactive titanium dioxide (TiO2) nanoparticles by the hydrolysis of titanium tetraisopropoxide in an acetone/methanol mixture. To enhance its photocatalytic activity, TiO2 was doped with Pt. The synthesised photocatalyst was characterised by techniques such as particle size analysis (PSA), XRD, FE-SEM, TEM, and EDX. The enhancement in the surface characteristics of Pt-doped TiO2 compared with bare TiO2 support was confirmed with Brunauer–Emmett–Teller (BET) analysis. The enhanced surface area and uniformity in particle size distribution at the nanoscale level were due to the effects of ultrasonic irradiation. The obtained results corroborated the size and composition of the synthesised catalysts. The size of the catalysts is in the nanometre range, and good dispersion of Pt catalysts over the TiO2 support was observed. The UV-Visible spectroscopy analysis was performed to study the optical properties of the synthesised TiO2 and Pt/TiO2 photocatalysts. An increase in the absorbance was noted when Pt was added to TiO2, which is due to the decrease in the band gap energy.