Extracting Turnover Frequencies of Electron Transfer in Heterogeneous Catalysis: A Study of IrO2-TiO2 Anatase for Water Oxidation Using Ce4+ Cations

Study of rutile TiO2(110) single crystal by transient absorption spectroscopy in the presence of Ce4+cations in aqueous environment. Implication on water splitting

Ce4+cations are commonly used as electron acceptors during the water oxidation to O2reaction over Ir- and Ru-based catalysts. They can also be reduced to Ce3+cations by excited electrons from the conduction band of an oxide semiconductor with a suitable energy level. In this work, we have studied their interaction with a rutile TiO2(110) single crystal upon band gap excitation by femtosecond transient absorption spectroscopy (TAS) in solution in the 350-900 nm range and up to 3.5 ns. Unlike excitation in the presence of water alone the addition of Ce4+resulted in a clear ground-state bleaching (GSB) signal at the band gap energy of TiO2(ca. 400 nm) with a time constantt= 4-5 ps. This indicated that the Ce4+cations presence has quenched the e-h recombination rate when compared to water alone. In addition to GSB, two positive signals are observed and are attributed to trapped holes (in the visible region, 450-550 nm) and trapped electrons in the IR region (>700 nm). Contrary to expectation, the lifetime of the positive signal between 450 and 550 nm decreased with increasing concentrations of Ce4+. We attribute the decrease in the lifetime of this signal to electrostatic repulsion between Ce4+at the surface of TiO2(110) and positively charged trapped holes. It was also found that at the very short time scale (<2-3 ps) the fast decaying TAS signal of excited electrons in the conduction band is suppressed because of the presence of Ce4+cations. Results point out that the presence of Ce4+cations increases the residence time (mobility) of excited electrons and holes at the conduction band and valence band energy levels (instead of being trapped). This might provide further explanations for the enhanced reaction rate of water oxidation to O2in the presence of Ce4+cations.

Study of the Kinetics of Reduction of IrO2 on TiO2 (Anatase) by Temperature-Programmed Reduction

The interaction between IrO2 and TiO2 (anatase) in non-isothermal reduction conditions has been studied by the temperature programmed reduction technique. IrO2 clusters are of sizes between 0.5 and 0.9 nm as determined from High Resolution Transmission Electron Microscopy (HRTEM). Largely, two main regions for reduction were found and modeled at ca. 100 and 230 °C. The first region is attributed to the partial reduction of IrO2 clusters, while the second one is due to reduction of the formed crystalline (rutile IrO2), during TPR, to Ir metal. Two methods for calculating kinetic parameters were tested. First, by applying different ramping rates on a 3.5 wt.% IrO2/TiO2 using Kissinger’s method. The apparent activation energy values for the first and second reduction regions were found to be ca. 35 and 100 kJ/mol, respectively. The second method was based on fitting different kinetic models for the experimental results in order to extract qualitative information on the nature of interaction during the reduction process. It was found that the first reduction is largely due to the amount of IrO2 (reactant concentration) while the second one involved phase boundary effect as well as nucleation.

Commemorative Issue in Honor of Professor Gerhard Ertl on the Occasion of His 85th Birthday

This Special Issue (SI) is dedicated to Professor Gerhard Ertl on his eighty-fifth birthday [...]