Porous Hexacyanometallate(III) Complexes as Catalysts in the Ring-Opening Copolymerization of CO2 and Propylene Oxide

Unraveling the role of internal-external metal substitution in Zn3[Co(CN6)]2 for the styrene oxide-CO2 cycloaddition reaction

We investigated the influence of the structural and textural properties along with the chemical environment of pure Zn3[Co(CN)6]2 in comparison with the modified phases on the catalytic performance in the cycloaddition reaction between styrene oxide and CO2. We relate these to the proposed reaction pathways and mechanisms. The natural cubic phase (ZnCoCn) was dehydrated to obtain the rhombohedral phase (ZnCoRn), while the stabilized cubic phase (ZnCoCs) was synthesized by substituting external zinc atoms with cadmium atoms. The rhombohedral stabilized phase (ZnCoRs) was achieved by the internal cobalt change with iron. All the materials were extensively characterized using X-ray diffraction (XRD), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), X-ray photoelectron spectroscopy (XPS), and N2 adsorption. The catalytic behavior of the four phases was tested. The crystalline structure of each phase was obtained, and by XPS, it was demonstrated that the chemical environments of all elements conforming to the rhombohedral stabilized phase are different from those of all other materials owing to the exchange of internal metals. The bulk textural properties were similar; only the ZnCoRs presented more micropore area but did not exceed the total surface area of the other materials. The product distribution and yield at reaction times of 2 h and 6 h were closer to those of the cubic phases. The natural rhombohedral phase exhibits the best performance. The tetrabutylammonium bromide (TBAB) and rhombohedral stabilized phase work together to yield a bigger copolymer quantity at the expense of the styrene carbonate (StCO3) production. From the proposed mechanism, the TBAB cation (TBA+) has a "protection" function that drives the closing of the StCO3 ring; however, the charge distribution anisotropy in the four nitrogen atoms generated by Co replacement in ZnCoRs could hold TBA+ as the reaction time progressed, causing an unavailability that triggered the copolymerization propagation step.

Transition Metal Hexacyanoferrate(II) Complexes as Catalysts in the Ring-Opening Copolymerization of CO2 and Propylene Oxide

The catalytic activity of four transition metal hexacyanoferrate(II) complexes (Ni2[Fe(CN)6], Co2[Fe(CN)6], KFe[Fe(CN)6] and Zn2[Fe(CN)6]) in the ring-opening copolymerization (ROCOP) of CO2 and propylene oxide (PO) is reported here for the first time and compared with that of other hexacyanometallate compounds. Complexes were prepared by coprecipitation employing tert-butanol as complexing agent. X-ray diffraction, Fourier-transform infrared spectroscopy, thermogravimetric analysis, elemental analysis, X-ray fluorescence, scanning electron microscopy, transmission electron microscopy and N2 physisorption were used to confirm the identity of the obtained materials. Except for Zn2[Fe(CN)6], which showed an amorphous nature, the complexes were constituted by aggregates of cubic nanocrystals with intra-crystalline micropores and inter-crystalline mesopores. Gas–solid phase titration with NH3 revealed the high potential of hexacyanoferrates as Lewis acid catalysts. In the case of Zn2[Fe(CN)6], the lack of structural organization led to an extremely high density of acid sites (43 μmol m−2). The resulting copolymers were analyzed via nuclear magnetic resonance spectroscopy and gel permeation chromatography. The studied transition metal hexacyanoferrate(II) catalysts showed mild activity in the target reaction, giving rise to polyethercarbonates with moderate CO2 content (9.3–18.1 wt%), random configuration (67.0–92.4% of polyethercarbonate linkages), modest molecular weights (MW, g mol−1 = 3400–20,200) and high dispersity (ĐM = 4.0–5.4). Cyclic propylene carbonate (PC) was also produced (1.4–19.8 wt%). Among all, the Co2[Fe(CN)6] complex stands as a potential catalyst for CO2/PO ROCOP due to its high CO2 uptake, selectivity and molecular weight of the obtained copolymer.