Ag-Doped TiO2 Composite Films Prepared Using Aerosol-Assisted, Plasma-Enhanced Chemical Vapor Deposition

Efficient Solar Light Photocatalyst Made of Ag3PO4 Coated TiO2-SiO2 Microspheres

Solar light active photocatalyst was prepared as silver phosphate (Ag₃PO₄) coating on titania-silica (TiO₂-SiO₂) microspheres. Titania-silica microsphere was obtained by spray drying TiO₂-SiO₂ colloidal solutions, whereas Ag₃PO₄ was applied by wet impregnation. XRD on the granules and SEM analysis show that the silver phosphate particles cover the surface of the titania-silica microspheres, and UV-visible diffuse reflectance analysis highlights that Ag₃PO₄/TiO₂-SiO₂ composites can absorb the entire visible light spectrum. BET measurements show higher specific surface area of the composite samples compared to bare Ag₃PO₄. Photocatalytic activity was evaluated by dye degradation tests under solar light irradiation. The prepared catalysts follow a pseudo-first-order rate law for dye degradation tests under solar light irradiation. The composite catalysts with an Ag₃PO₄/TiO₂-SiO₂ ratio of 1:1.6 wt% show better catalytic activity towards both rhodamine B and methylene blue degradation and compared with the results with uncoated TiO₂-SiO₂ microspheres and the benchmark commercial TiO₂ (Evonik-P25) as a reference. The composite photocatalyst showed exceptional efficiency compared to its pristine counterparts and reference material. This is explained as having a higher surface area with optimum light absorption capacity.

Preparation of TiO2-CNT-Ag Ternary Composite Film with Enhanced Photocatalytic Activity via Plasma-Enhanced Chemical Vapor Deposition

In this study, a TiO2-CNT-Ag ternary composite film was successfully synthesized using the plasma-enhanced chemical vapor deposition method by simultaneously feeding a carbon nanotube (CNT)/Ag suspension and titanium tetraisopropoxide gas. The prepared TiO2-CNT-Ag film was characterized by scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and ultraviolet-visible spectroscopy. Moreover, the Ag/Ti ratio of the film was confirmed using an inductivity-coupled plasma optical emission spectrometer. The performance of the TiO2-composite film for the degradation of rhodamine 6G under simulated solar light irradiation was evaluated. The rate constant of the prepared TiO2-CNT-Ag for rhodamine 6G degradation was approximately 1.8 times greater than that of prepared TiO2. This result indicates that the addition of CNT and Ag significantly improved the photocatalytic activity of the prepared films.