In situ Decolorization Monitoring of Textile Dyes for an Optimized UV-LED/TiO2 Reactor

Effect of TiO2/Fe2O3 nanopowder synthesis method on visible light photocatalytic degradation of reactive blue dye

Water pollution and scarcity of clean water are major issues of concern globally. In this study, titanium dioxide (TiO2) photocatalyst doped with ferric oxide (Fe2O3) was used to degrade reactive blue dye (171) using sunlight irradiation. Two approaches were employed to synthesize the photocatalyst: synthesis of ferric oxide and titanium precursor through ultrasonic-assisted sol-gel method and using iron (III) nitrate nonahydrate with commercial titanium dioxide. The photocatalysts were characterized using FTIR Spectroscopy, SEM, XRD analyses, and UVDRS to determine their chemical composition, morphology, crystallinity, and light absorption, respectively. The effect of contaminant concentration (1-3 ppm), solution pH and photocatalyst type on the degradation efficiency was studied. Doping enabled visible light absorption as confirmed by the UVDRS analysis. Solar photocatalytic degradation resulted in complete (100 % removal) of the dye within 2 h under solar irradiation for all concentrations of the dye studied. Furthermore, the photocatalysts exhibited superior performance in both neutral and acidic solutions compared to basic ones. After four cycles, the dye removal efficiency has decreased by less than 15 % for all the photocatalysts confirming the significant activity and high stability of the nanocomposite. The increased dye photodegradation efficacy of Fe2O3 doped TiO2 under sunlight irradiation is attributed to the narrowing of the photocatalyst's bandgap from 3.76 eV (in pure TiO2) to 2.83 eV. This narrowing of the bandgap enhances the absorption of visible light from sunlight, thus making this photocatalyst effective under sunlight and eliminating the use of electricity which is a requirement for ultraviolet photocatalysis.

Synthesis and characterization of Fe3O4@SiO2 -supported metal-organic framework PAEDTC@MIL-101 (Fe) for degradation of chlorpyrifos and diazinon pesticides

In this study, a new core-shell Fe3O4@SiO2/PAEDTC@MIL-101 (Fe) photocatalyst was prepared by sol-gel method and used to degrade diazinon (DZN) and chlorpyrifos (CPS) from aqueous solutions. The characteristics analyzed by various techniques indicate that the core-shell photocatalyst with a specific surface area of 992 m2/g, pore size of 1.35 nm and saturation magnetization of nanocomposite was 12 emu/g has been successfully synthesized and can be separated from the reaction solution by a magnetic field. The maximum efficiencies of DZN (98.8%) and CPS (99.9%) were provided at pH of 5, photocatalyst dosage of 0.6 g/L, pollutant concentration of 25 mg/L, radiation intensity of 15 W, and time of 60 min. The presence of anions such as sulfate, nitrate, bicarbonate, phosphate, and chloride had a negative effect on the performance of the photocatalysis system. Compared to the adsorption and photolysis systems alone, the photocatalytic process based on Fe3O4@SiO2/PAEDTC@MIL-101 (Fe) under two UV and visible light sources showed a high efficiency of 90% in the reaction time of 60 min. The BOD5/COD ratio improved after 50 min to above 0.4 with TOC and COD removal rates >80%. Scavenging tests showed that •OH radical, hole (h+), electron (e-), and O2•- anion were produced in the reaction reactor, and the •OH radical was the dominant species in the degradation of DZN and CPS. The stability tests confirmed the recyclability of the photocatalyst in 360 min of reactions, with a minimum reduction of 7%. Energy consumption for the present system during different reactions was between 15.61 and 25.06 kWh/m3 for DZN degradation and 10-22.87 kWh/m3 for CPS degradation.

UV-Based Advanced Oxidation Processes of Remazol Brilliant Blue R Dye Catalyzed by Carbon Dots

UV-based advanced oxidation processes (AOPs) (UV/H₂O₂ and UV/S₂O₈^2-) with a titanium(IV)-doped carbon dot, TiP-CD, as a catalyst were developed for the decomposition of Remazol Brilliant Blue R (Reactive Blue 19), an anthraquinone textile dye (at T = 25 °C and pH = 7). The Ti-CD, with marked catalytic UV properties, was successfully synthesized by the one-pot hydrothermal procedure, using L-cysteine as carbon precursor, ethylenediamine as nitrogen source, PEG (polyethylene glycol) as a capping agent, and titanium(IV) isopropoxide (precursor of TiO₂ doping). Contrary to azo dyes (methyl orange, orange II sodium salt, and reactive black 5), which achieved complete degradation in a time interval less than 30 min in the developed AOP systems (UV/H₂O₂, UV/S₂O₈^2-, and UV/TiO₂), the RBB-R showed relatively low degradation rates and low discoloration rate constants. In the presence of the catalyzer, the reaction rate significantly increased, and the pseudo-first-order rate constants for the RBB-R discoloration were UV/3.0 mM H₂O₂/TIP-CD-0.0330 min^-1 and UV/1.02 mM S₂O₈^2-/TIP-CD-0.0345 min^-1.

State-of-the-art and current challenges for TiO2/UV-LED photocatalytic degradation of emerging organic micropollutants

The development of ultraviolet light-emitting diodes (UV-LED) opens new possibilities for water treatment and photoreactor design. TiO₂ photocatalysis, a technology that has been continuously drawing attention, can potentially benefit from LEDs to become a sustainable alternative for the abatement of organic micropollutants (OMPs). Recently reported data on photocatalytic degradation of OMPs and their parameters of influence are here critically evaluated. The literature on OMP degradation in real water matrices, and at environmentally relevant concentrations, is largely missing, as well as the investigations of the impact of photoreactor design in pollutant degradation kinetics. The key factors for reducing UV-LED treatment technology costs are pointed out, like the increase in external quantum and wall-plug efficiencies of UV-LEDs compared to other technologies, as well as the need for an appropriate design optimizing light homogeneity in the reactor. Controlled periodic illumination, wavelength coupling and H₂O₂ addition are presented as efficiency enhancement options. Although electrical energy per order (E_EO) values for UV-LED photocatalysis have decreased to the range of traditional mercury lamps, values are still not low enough for practical employment. Moreover, due to the adoption of high initial OMP concentration in most experiments, it is likely that most literature E_EO values are overestimated. Given the process characteristics, which are favoured by translucent matrices and small diameters for more homogenous light distribution and better transportation of radicals, innovative reactor designs should explore the potential of point-of-use applications to increase photocatalysis applicability at large scale.

Environmental Applications of Photocatalytic Processes

Photocatalytic processes have been investigated in different environmental fields, but their applications at full scale are still scarce [...]