Layered Double Hydroxide Sorbents for Removal of Selenium from Power Plant Wastewaters

Insight into the synthesis of LDH using the urea method: morphology and intercalated anion control

Layered double hydroxides (LDHs) are a class of layered solids applied in many application fields. The study of synthetic methods able to control the interlayer composition and morphology of LDH is an open issue. The urea method, which exploits the thermal decomposition of urea, is known for yielding highly crystalline LDH in the carbonate form. This form is highly stable and, to replace carbonate ions with more easily exchangeable anions, a second step is required. In this work, we modified the urea method to obtain MgAl and ZnAl LDH in the chloride or nitrate form through a one-step synthesis. The effects of the urea/(Al + M(II)) molar ratio (R), reaction time and metal salt concentrations were deeply investigated. We found that LDH in chloride and nitrate forms can be prepared from solutions of metal salts not exceeding 1 M by adjusting R and maintaining the reaction time at 48 hours. The morphology of these products was found to depend on the R value and on the metal salts used in the synthesis. A high R value and nitrate salts favoured the formation of sand-rose crystals, while chloride salts induced the formation of plate-like crystals. The crystal growth mechanism and the parameters influencing the morphology are discussed with reference to ZnAl LDH by monitoring the synthesis over time.

LDH-TiO2 Composite for Selenocyanate (SeCN-) Photocatalytic Degradation: Characterization, Treatment Efficiency, Reaction Intermediates and Modeling

Selenium as a nutrient has a narrow margin between safe and toxic limits. Hence, wastewater discharges from selenium-containing sources require appropriate treatment that considers health concerns and stringent selenium-related water treatment standards. This work examined the use of a photocatalysis-cum-adsorption system based on a layered double hydroxide coupled with TiO2 (LDH-TiO2) to remove aqueous phase selenocyanate (SeCN−), which is difficult to treat and requires specific treatment procedures. The synthesized LDH and LDH-TiO2 composite samples were characterized using the X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and thermogravimetry analysis (TGA) methods. The XRD results for the uncalcined LDH indicated a hydrotalcite mass with a rhombohedral structure, whereas increasing the calcination temperature indicated transition to an amorphous state. FESEM results for the LDH-TiO2 matrix indicated round titanium dioxide particles and LDH hexagonal layers. The TGA findings for uncalcined LDH showed a gradual decrease in weight up to 250 °C, followed by a short plateau and then a sharp decrease in LDH weight from 320 °C, with a net weight loss around 47%. Based on the characterization and initial selenocyanate adsorption results, the 250 °C calcined LDH-TiO2 matrix was used for the selenocyanate photocatalysis. A ~100% selenium removal was observed using LDH:TiO2 at a 1.5:1 w/w ratio with a 2 g/L dose, whereas up to 80% selenium removal was noted for LDH:TiO2 at a 0.5:1 w/w ratio. The respective difference in the efficiency of selenium treatment was attributed to enhanced LDH-based adsorption sites in the enhanced LDH:TiO2 w/w ratio. Furthermore, the selenite and selenate that occurred during SeCN− photocatalytic degradation (PCD) were also nearly completely removed via adsorption. An optimization exercise using response surface methodology (RSM) for total selenium removal showed R2 values of more than 0.95, with a prediction accuracy of more than 90%. In summary, the present findings show that the use of a photocatalysis-cum-adsorption system based on LDH-TiO2 is a promising technique to treat industrial wastewater discharges for selenocyanate and also remove the resulting intermediates.