Microstructure and Corrosion Behavior of Laser Cladding FeCoNiCrBSi Based High-Entropy Alloy Coatings

Multifunctional amorphous FeCoNiTixSi high-entropy alloys with excellent electromagnetic-wave absorption performances

Amorphous high-entropy alloys (HEAs) as electromagnetic-wave absorbing materials have been rarely reported. In this work, amorphous FeCoNiTixSi HEAs were synthesized by introducing a high content of large-atom Ti using the high-energy ball-milling technique. This amorphous structure could improve the saturated magnetization and coercivity of HEAs, but slightly degraded the mechanical and oxidation resistance properties. In terms of electromagnetic properties, FeCoNiTi0.01Si and FeCoNiTiSi exhibit excellent electromagnetic-wave absorption performances, with significant absorptions of -68.4 dB at 6.14 GHz and -63.4 dB at 9.12 GHz, corresponding to bandwidths of 5.15 GHz (1.69 mm) and 3.64 GHz (1.43 mm), respectively. Overall, the prepared FeCoNiTixSi HEAs exhibited superior comprehensive performances compared to other HEA absorption materials. This work provided a novel strategy for the development of new electromagnetic-wave absorption materials with low weight, high absorption efficiency, and resistance to harsh environments.

Effect of Si and B on the Electrochemical Behavior of FeCoNiCr-Based High-Entropy Amorphous Alloys

The ability to produce high-entropy alloys with an amorphous structure, so-called high-entropy metallic glasses (HEMGs), offers the possibility to produce new compositions with good mechanical properties and resistance to corrosion. In this study, corrosion behavior was studied in two HEMGs, FeCoNiCrB and FeCoNiCr(BSi). In both cases, the total amount of metalloid atoms was kept constant at 20 at.%. The electrochemical behavior of these alloys was studied by means of linear polarization resistance (LPR) measurements and electrochemical impedance spectroscopy in a 3 wt.% NaCl solution. The effect of corrosion was characterized by using X-ray photoelectron spectroscopy (XPS) and the surface morphology was checked using a scanning electron microscope (SEM). The results show that samples with B but without Si exhibit better corrosion resistance due to its chemical homogeneity and lack of structural heterogeneity.