Biodegradable Mg/HA/TiO2 Nanocomposites Coated with MgO and Si/MgO for Orthopedic Applications: A Study on the Corrosion, Surface Characterization, and Biocompatability

Based on the synergistic effect of Mg2+ and antibacterial peptides to improve the corrosion resistance, antibacterial ability and osteogenic activity of magnesium-based degradable metals

To overcome the restricted degradation, poor antiacterial and osteoindctive problems of magnesium and its alloys, this study presented the spinning coating of an antimicrobial peptide (AP)-loaded silk fibroin (SF) composite onto a corrosion-resistant MgO-coated AZ31 Mg alloy via anodization (aMgO) and electrodeposition (eMgO) methods. The composite coatings not only created a smooth and hydrophilic surface, but also obviously improved the corrosion resistance according to the test of corrosion potential and current density. The colonization of E. coli on MgO-AP composite coatings was significantly reduced as compared to the MgO layers, due to the potential synergetic effects of APs and Mg2+. Compared with the bare AZ31, the composite coating inhibited the corrosion of the substrate and the release of Mg2+, supported the adhesion, spreading and proliferation of osteoblasts, and presented a significantly improved osteogenic differentiation trend. Therefore, the MgO-AP composite coating, which had both antibacterial and bone-promoting abilities, was expected to be applied for surface modification of magnesium alloy implants to solve the clinical problems of bacterial infection and poor osseointegration.

Ultrasound-assisted synthesis of mixed calcium magnesium oxide (CaMgO2) nanoflakes for photocatalytic degradation of methylene blue

In the present study, mixed calcium magnesium oxide (CaMgO₂) nanoflakes were synthesized using an ultrasound-assisted co-precipitation method. The physicochemical, structural and functional properties and elemental composition of the nanoflakes had been characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), High-resolution transmission electron microscopy (HR-TEM), Fourier Transform Infrared spectroscopy (FTIR), UV-VIS spectroscopy, X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. Moreover, the photocatalytic actions of the nanoflakes were evaluated by the removal rates of methylene blue (MB) and p-nitrophenol (4-NP) under UV irradiation at room temperature. SEM-EDS studies revealed that the nanoflakes consisted of mixed oxide such as magnesium oxide (MgO) and calcium oxide (CaO) particles. The size of the nanoflakes was found to be in the range of 10-30 nm and the average size was 25 nm as confirmed by HR-TEM analysis. XRD revealed that the standard crystal size was calculated to be 25 nm. The synthesized nanoflakes had a strong photocatalytic activity for methylene blue (MB) and p-nitrophenol (4-NP) degradation in the presence of H₂O₂ under UV light irradiation within 60 min and 30 min, respectively. Hence, the present study proposes that the CaMgO₂ nanoflakes can be employed for the removal of dyes from wastewater.

Low-Cost Deposition of Antibacterial Ion-Substituted Hydroxyapatite Coatings onto 316L Stainless Steel for Biomedical and Dental Applications

Substitutions of ions into an apatitic lattice may result in antibacterial properties. In this study, magnesium (Mg)-, zinc (Zn)-, and silicon (Si)-substituted hydroxyapatite (HA) were synthesized using a microwave irradiation technique. Polyvinyl alcohol (PVA) was added during the synthesis of the substituted HA as a binding agent. The synthesized Mg-, Zn-, and Si-substituted HAs were then coated onto a 316L-grade stainless-steel substrate using low-cost electrophoretic deposition (EPD), thereby avoiding exposure to high temperatures. The deposited layer thickness was measured and the structural, phase and morphological analysis were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The bacterial adhesion of Staphylococcus aureus was characterized at 30 min, 2 h and 6 h. The results showed homogeneous, uniform thickness (50–70 µm) of the substrate. FTIR and XRD showed the characteristic spectral peaks of HA, where the presence of Mg, Zn and Si changed the spectral peak intensities. The Mg–HA coating showed the least bacterial adhesion at 30 min and 2 h. In contrast, the Si–HA coating showed the least adhesion at 6 h. EPD showed an effective way to get a uniform coating on bio-grade metal implants, where ionic-substituted HA appeared as alternative coating material compared to conventional HA and showed the least bacterial adhesion.

The Potential of Magnesium Based Materials in Mandibular Reconstruction

The future of biomaterial design will rely on development of bioresorbable implant materials that completely and safely degrade in vivo after the tissues grow, without generating harmful degradation products at the targeted anatomic site. Permanent biomaterials such as Ti6Al4V alloy, 316L stainless steel, and Co-based alloys currently used in mandibular reconstruction often result in stress shielding effects due to mismatch in the Young’s modulus values between the bone and the implant, resulting in implant loosening. Also, allergic responses due to metal ion releases necessitates revision surgery to prevent long term exposure of the body to toxic implant contents. Bioresorbable metals are perceived as revolutionary biomaterials that have transformed the nature of metallic biomaterials from bioinert to bioactive and multi-bio functional (anti-bacterial, anti-proliferation, and anti-cancer). In this aspect, magnesium (Mg)-based materials have recently been explored by the biomedical community as potential materials for mandibular reconstruction, as they exhibit favorable mechanical properties, adequate biocompatibility, and degradability. This article reviews the recent progress that has led to advances in developing Mg-based materials for mandibular reconstruction; correlating with the biomechanics of mandible and types of mandibular defects. Mg-based materials are discussed regarding their mechanical properties, corrosion characteristics, and in vivo performance. Finally, the paper summarizes findings from this review, together with a proposed scope for advancing the knowledge in Mg-based materials for mandibular reconstruction.