Wierzbicka E, Vaghefinazari B, Mohedano M, Visser P, Posner R, Blawert C, Zheludkevich M, Lamaka S, Matykina E, Arrabal R. Chromate-Free Corrosion Protection Strategies for Magnesium Alloys-A Review: Part II-PEO and Anodizing. MATERIALS (BASEL, SWITZERLAND) 2022; 15:ma15238515. [PMID: 36500010 PMCID: PMC9737229 DOI: 10.3390/ma15238515] [Citation(s) in RCA: 4] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 09/09/2022] [Revised: 11/10/2022] [Accepted: 11/23/2022] [Indexed: 05/18/2023]
Abstract
Although hexavalent chromium-based protection systems are effective and their long-term performance is well understood, they can no longer be used due to their proven Cr(VI) toxicity and carcinogenic effect. The search for alternative protection technologies for Mg alloys has been going on for at least a couple of decades. However, surface treatment systems with equivalent efficacies to that of Cr(VI)-based ones have only begun to emerge much more recently. It is still proving challenging to find sufficiently protective replacements for Cr(VI) that do not give rise to safety concerns related to corrosion, especially in terms of fulfilling the requirements of the transportation industry. Additionally, in overcoming these obstacles, the advantages of newly introduced technologies have to include not only health safety but also need to be balanced against their added cost, as well as being environmentally friendly and simple to implement and maintain. Anodizing, especially when carried out above the breakdown potential (technology known as Plasma Electrolytic Oxidation (PEO)) is an electrochemical oxidation process which has been recognized as one of the most effective methods to significantly improve the corrosion resistance of Mg and its alloys by forming a protective ceramic-like layer on their surface that isolates the base material from aggressive environmental agents. Part II of this review summarizes developments in and future outlooks for Mg anodizing, including traditional chromium-based processes and newly developed chromium-free alternatives, such as PEO technology and the use of organic electrolytes. This work provides an overview of processing parameters such as electrolyte composition and additives, voltage/current regimes, and post-treatment sealing strategies that influence the corrosion performance of the coatings. This large variability of the fabrication conditions makes it possible to obtain Cr-free products that meet the industrial requirements for performance, as expected from traditional Cr-based technologies.
Collapse
Affiliation(s)
- Ewa Wierzbicka
- Departamento de Ingeniería Química y de Materiales, Facultad de Ciencias Químicas, Universidad Complutense de Madrid, 28040 Madrid, Spain
- Department of Functional Materials and Hydrogen Technology, Faculty of Advanced Technologies and Chemistry, Military University of Technology, Kaliskiego Street 2, 00-908 Warsaw, Poland
| | - Bahram Vaghefinazari
- Institute of Surface Science, Helmholtz-Zentrum Hereon, 21502 Geesthacht, Germany
| | - Marta Mohedano
- Departamento de Ingeniería Química y de Materiales, Facultad de Ciencias Químicas, Universidad Complutense de Madrid, 28040 Madrid, Spain
| | | | - Ralf Posner
- Henkel AG & Co. KGaA, 40191 Düsseldorf, Germany
| | - Carsten Blawert
- Institute of Surface Science, Helmholtz-Zentrum Hereon, 21502 Geesthacht, Germany
| | - Mikhail Zheludkevich
- Institute of Surface Science, Helmholtz-Zentrum Hereon, 21502 Geesthacht, Germany
| | - Sviatlana Lamaka
- Institute of Surface Science, Helmholtz-Zentrum Hereon, 21502 Geesthacht, Germany
| | - Endzhe Matykina
- Departamento de Ingeniería Química y de Materiales, Facultad de Ciencias Químicas, Universidad Complutense de Madrid, 28040 Madrid, Spain
| | - Raúl Arrabal
- Departamento de Ingeniería Química y de Materiales, Facultad de Ciencias Químicas, Universidad Complutense de Madrid, 28040 Madrid, Spain
| |
Collapse
|
2
|
Effect of Graphite Content on the Conductivity, Wear Behavior, and Corrosion Resistance of the Organic Layer on Magnesium Alloy MAO Coatings. COATINGS 2022. [DOI: 10.3390/coatings12040434] [Citation(s) in RCA: 2] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 01/07/2023]
Abstract
To impart electrical conductivity on magnesium alloy micro-arc oxidation coatings, a graphite/epoxy conductive layer was prepared on the surface of a ceramic layer in this work, focusing on wear behavior and corrosion resistance of the coating. At a graphite weight of 80 wt%, the square resistance of the coating decreased to 217.6 kΩ/□, and it exhibited good resistance. Combined with the distribution of graphite particles in the coating and the change in surface resistance, we determined that the conductive mechanism of the coating occurred through quantum tunneling when the graphite content was 60 wt%. When the graphite content increased from 60 to 80 and 100 wt%, the formation of conductive paths on the surface of the coating further improved the conductivity. The hardness of the organic coatings was positively related to the graphite content. Analysis of the wear scars and wear debris after dry friction and wear testing showed that the wear forms of the coating consisted of abrasive wear when the graphite content was in the range of 20–40 wt%. When the graphite content was in the range of 60–100 wt%, the wear forms of the coating consisted of abrasive wear and peeling wear.
Collapse
|
3
|
Degradation Resistance and In Vitro Cytocompatibility of Iron-Containing Coatings Developed on WE43 Magnesium Alloy by Micro-Arc Oxidation. COATINGS 2020. [DOI: 10.3390/coatings10111138] [Citation(s) in RCA: 5] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 12/13/2022]
Abstract
Iron (Fe) is an important trace element for life and plays vital functions in maintaining human health. In order to simultaneously endow magnesium alloy with good degradation resistance, improved cytocompatibility, and the proper Fe amount for the body accompanied with degradation of Mg alloy, Fe-containing ceramic coatings were fabricated on WE43 Mg alloy by micro-arc oxidation (MAO) in a nearly neutral pH solution with added 0, 6, 12, and 18 g/L ferric sodium ethylenediaminetetraacetate (NaFeY). The results show that compared with the bare Mg alloy, the MAO samples with developed Fe-containing ceramic coatings significantly improve the degradation resistance and in vitro cytocompatibility. Fe in anodic coatings is mainly present as Fe2O3. The increased NaFeY concentration favorably contributes to the enhancement of Fe content but is harmful to the degradation resistance of MAO coatings. Our study reveals that the developed Fe-containing MAO coating on Mg alloy exhibits potential in clinical applications.
Collapse
|
4
|
The Role of Ammonium Chloride in the Powder Thermal Diffusion Alloying Process on a Magnesium Alloy. COATINGS 2019. [DOI: 10.3390/coatings9040252] [Citation(s) in RCA: 3] [Impact Index Per Article: 0.6] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 11/16/2022]
Abstract
The powder thermal diffusion alloying method could be utilized to fabricate Al-rich intermetallic coatings on magnesium alloys in the air. While the role of ammonium chloride powder in the diffusion alloying source is still to be investigated. This research took the AZ91D magnesium alloy as the substrate. Diffusion sources with various powders were utilized as the diffusion source. Microstructure observation and phase identification were enrolled to investigate the role of the ammonium chloride powder in the diffusion alloying process. Results indicate that HCl gas could turn some solid Al powder into gaseous AlCl3 to enhance the transport of active Al atoms, moreover, it reacts with the dense MgO film and converts it to a loose one, which enables the AlCl3 gas to penetrate MgO and arrive the matrix to form a protective coating. Furthermore, the ammonium chloride content should be confined to 10 wt. % of the diffusion alloying source. Too much ammonium chloride powder would result in a worse intermetallic coating.
Collapse
|