Optical Investigation of Eu3+ Doped Bi12GeO20 (BGO) Crystals

A Comparative Study of Eu3+-Doped Sillenites: Bi12SiO20 (BSO) and Bi12GeO20 (BGO)

The spectroscopic properties of Eu³⁺-doped Bi₁₂SiO₂₀ (BSO) were investigated and compared with that of Eu³⁺-doped Bi₁₂GeO₂₀ (BGO). The emission properties and the absorption spectra have been measured at 10 K as well as at 300 K (room temperature). Luminescence was detected due to the direct excitation of the ⁵D₀ level of Eu³⁺, as well as through the excitation of the ⁵D₁ level. The Judd-Ofelt theoretical framework was used to compute the radiative lifetimes (τ) and the omega parameters (Ω_λ). The electric dipole transition probabilities, asymmetry ratios (R), along with the branching ratios (β) were also determined based on the obtained experimental data. The strongest detected luminescence belongs to the ⁵D₀ → ⁷F₀ transition observed at 578 nm, similar to the BGO sillenite. Reasons for the major presence of the ⁵D₀ → ⁷F₀ emission, theoretically forbidden by the Judd-Ofelt Theory, were investigated and compared with that of the BGO sillenite. Obtained results showed that the strong ⁵D₀ → ⁷F₀ line is also present in Eu:BSO, indicating that this is a feature of the entire sillenite family and not just Eu:BGO.

A Review on X-ray Excited Emission Decay Dynamics in Inorganic Scintillator Materials

Scintillator materials convert high-energy radiation into photons in the ultraviolet to visible light region for radiation detection. In this review, advances in X-ray emission dynamics of inorganic scintillators are presented, including inorganic halides (alkali-metal halides, alkaline-earth halides, rare-earth halides, oxy-halides, rare-earth oxyorthosilicates, halide perovskites), oxides (binary oxides, complex oxides, post-transition metal oxides), sulfides, rare-earth doped scintillators, and organic-inorganic hybrid scintillators. The origin of scintillation is strongly correlated to the host material and dopants. Current models are presented describing the scintillation decay lifetime of inorganic materials, with the emphasis on the short-lived scintillation decay component. The whole charge generation and the de-excitation process are analyzed in general, and an essential role of the decay kinetics is the de-excitation process. We highlighted three decay mechanisms in cross luminescence emission, exitonic emission, and dopant-activated emission, respectively. Factors regulating the origin of different luminescence centers controlling the decay process are discussed.