Carbon Nanodots as a Potential Transport Layer for Boosting Performance of All-Inorganic Perovskite Nanocrystals-Based Photodetector

Development of a Highly Efficient Optoelectronic Device Based on CuFeO2/CuO/Cu Composite Nanomaterials

Herein, an optoelectronic device synthesized from a CuFeO₂/CuO/Cu nanocomposite was obtained through the direct combustion of Cu foil coated with Fe₂O₃ nanomaterials. The chemical, morphological, and optical properties of the nanocomposite were examined via different techniques, such as XRD, XPS, TEM, SEM, and UV/Vis spectrophotometer. The optical reflectance demonstrated a great enhancement in the CuFeO₂ optical properties compared to CuO nanomaterials. Such enhancements were clearly distinguished through the bandgap values, which varied between 1.35 and 1.38 eV, respectively. The XRD and XPS analyses confirmed the chemical structure of the prepared materials. The produced current density (J_ph) was studied in dark and light conditions, thereby confirming the obtained optoelectronic properties. The J_ph dependency to monochromatic wavelength was also investigated. The J_ph value was equal to 0.033 mA·cm^-2 at 390 nm, which decreased to 0.031 mA·cm^-2 at 508 nm, and then increased to 0.0315 mA·cm^-2 at 636 nm. The light intensity effects were similarly inspected. The J_ph values rose when the light intensities were augmented from 25 to 100 mW·cm^-2 to reach 0.031 and 0.05 mA·cm^-2, respectively. The photoresponsivity (R) and detectivity (D) values were found at 0.33 mA·W^-1 and 7.36 × 10¹⁰ Jones at 390 nm. The produced values confirm the high light sensitivity of the prepared optoelectronic device in a broad optical region covering UV, Vis, and near IR, with high efficiency. Further works are currently being designed to develop a prototype of such an optoelectronic device so that it can be applied in industry.

Investigation of highly luminescent inorganic perovskite nanocrystals synthesized using optimized ultrasonication method

All-inorganic halide perovskite nanocrystals are next-generation materials with excellent optical and semiconductor properties suitable for display applications. In this study, we introduce an optimized ultrasonication method for the high-capacity synthesis of highly luminescent inorganic perovskite nanocrystals. After the synthesis of CsPbBr₃ with superior optical performance by ultrasonication method, halide anion exchange was performed to tune the stable emission wavelength over the entire visible range. In particular, the maximum photoluminescence wavelengths of the red and green perovskite nanocrystals were appropriate for light-emitting diode applications, and their full-width-at-half-maximum were very narrow, showing outstanding color purity. The materials also had excellent thermal and photo-stability, which is a necessary requirement for perovskite nanocrystal/organic light-emitting diode hybrid device applications. We formulated uniformly stable perovskite nanocrystal inks and optimized their physical and rheological properties for successful inkjet-printing. Finally, we fabricated a hybrid device with a color conversion layer based on the red and green perovskite nanocrystals synthesized using the optimized ultrasonication and halide-ion-exchange methods. The color reproduction range of the fabricated devices was 27.3 % wider than that of the National Television System Committee values, indicating very vivid colors.