Impediment of Iron Corrosion by N,N′-Bis[2-hydroxynaphthylidene]amino]oxamide in 3.5% NaCl Solution

Influence of Tantalum Addition on the Corrosion Passivation of Titanium-Zirconium Alloy in Simulated Body Fluid

Ti-15%Zr alloy and Ti-15%Zr-2%Ta alloy were fabricated to be used in biomedical applications. The corrosion of these two alloys after being immersed in simulated body fluid for 1 h and 72 h was investigated. Different electrochemical methods, including polarization, impedance, and chronoamperometric current with time at 400 mV were employed. Also, the surface morphology and the compositions of its formed film were reported by the use of scanning electron microscope and energy dispersive X-ray. Based on the collected results, the presence of 2%Ta in the Ti-Zr alloy passivated its corrosion by minimizing its corrosion rate. The polarization curves revealed that adding Ta within the alloy increases the corrosion resistance as was confirmed by the impedance spectroscopy and current time data. The change of current versus time proved that the addition of Ta reduces the absolute current even at high anodic potential, 400 mV. The results of both electrochemical and spectroscopic methods indicated that pitting corrosion does not occur for both Ti-Zr and Ti-Zr-Ta alloys, even after their immersion in SBF solutions for 72 h.

Methylenedisalicylic Acid as a Biocorrosion Inhibitor for Aluminum in Concentrated Sodium Chloride Solutions

3,3'-Methylenedisalicylic acid (MDS) was synthesized and ascertained on the basis of elemental analyses (C, H) and spectral measurements (IR, mass, ¹H NMR, and UV-vis). Moreover, the prepared MDS compound has been assayed for its antimicrobial action against the growth of fungi as well as Gram-positive and Gram-negative bacteria. The results demonstrated the possibility of its usefulness to restrain the growth of both fungi and bacteria, whereas MDS showed its best impact against Candida albicans. The inhibitive impact of MDS on the corrosion of aluminum (Al) in concentrated sodium chloride solution (3.5 wt % NaCl) has been investigated. The corrosion work was done by potentiodynamic cyclic polarization, electrochemical impedance spectroscopy, and chronoamperometric current-time measurements and complemented by scanning electron microscopy and energy-dispersive X-ray investigations. It was found that MDS molecules protect the aluminum against corrosion, and its ability increases with the increase of concentration from 5 × 10^-5 to 1 × 10^-4 M and further to 5 × 10^-4 M. The electrochemical results were supported by the morphological analysis and proved that the presence of MDS inhibits the uniform and pitting corrosion of Al in the chloride solutions.

Enhancement of Surface and Interface Properties of Low Carbon Steel by Hybrid ZnO and NiO Nanoparticles Reinforced Tin Coating

Tin matrix nanocomposite coatings containing ZnO and NiO nanoparticles, both individually and combined, were deposited on low carbon steel substrates. The aim was to investigate the effect of reinforcement of nanoparticles on microstructural morphology and thickness of tin coatings, modification in the interfacial layer between coating and substrate, and the corrosion resistance of low carbon steel substrate. Optical and scanning electron microscopy were employed for microstructural observation, while potentiostat-galvanostat was utilized for electrochemical investigation. It was found that the tin nanocomposite coatings with nanoparticles significantly modified the coating thickness, intermetallic layer thickness, and surface corrosion resistance. Coatings through the direct tinning process are considered to be a simple and low-cost route for protecting metallic materials from corrosion, and the presence of ZnO and NiO nanoparticles in tin coatings further increases the corrosion resistance of low carbon steels.

Alleviation of Iron Corrosion in Chloride Solution by N,N′-bis[2-Methoxynaphthylidene]amino]oxamide as a Corrosion Inhibitor

The alleviation of iron corrosion in 3.5% NaCl sodium chloride solution using N,N′-bis[2-methoxynaphthylidene]amino]oxamide (MAO) as a corrosion inhibitor has been reported. The work was achieved using various investigation techniques. Potentiodynamic cyclic polarization (PCP) displayed a powerful inhibition for the corrosion via reducing the iron’s cathodic and anodic reactions. This was reflected in reduced corrosion currents and increased polarization resistances in the presence and upon the increase of MAO concentration. The electrochemical impedance spectroscopy results indicated that MAO molecules provoke the corrosion resistance via increasing polarization resistance. The power of MAO on decreasing pitting attack was also investigated through measuring the change of current with time at −0.475 V(Ag/AgCl). Scanning electron microscopy images were taken of the surface after the current–time measurements were performed in the absence and presence of MAO. The current-time experiments indicated that MAO highly mitigates the corrosion of iron. The energy dispersive X-ray analyzer reported the products found on the tested surfaces. The effect of extending the exposure time from 1 h to 48 h was also tested and was found to alleviate the corrosion of iron, whether MAO molecules are absent or present.

Influence of Zirconium on the Corrosion Passivation of Titanium in Simulated Body Fluid

Pure Ti and 85%Ti-15%Zr alloy were sintered in a heat induction high frequency furnace. The corrosion behaviour of Ti and 85%Ti-15%Zr in simulated body fluid (SBF) was studied. The work was achieved using different techniques as the cyclic polarization (PCP), the impedance spectroscopy (EIS), and the change of the potentiostatic current with time (PCT) experiments. The morphology of the surfaces of Ti and Ti-Zr after being corroded in SBF for 72 were investigated by a scanning electron microscope (SEM) and the analysis for the layer formed on that surface was collected via energy dispersive X-ray (EDX). Results depicted that the 15% Zr present within Ti decreases the corrosion via increasing Ti corrosion resistance and minimizing its measured corrosion rate. PCP data proved that the addition of Zr reduced all anodic, cathodic and corrosion currents. EIS results confirmed that Zr has a positive impact on the reduction of corrosion resistance. PCT, SEM, and EDX examinations displayed that both Ti and Ti-Zr alloy don’t show pitting corrosion even after 72 h exposure to SBF.