Microstructure Characterization and Battery Performance Comparison of MOF-235 and TiO2-P25 Materials

Photocatalytic Performance of Sol-Gel Prepared TiO2 Thin Films Annealed at Various Temperatures

Titanium dioxide (TiO2) in the form of thin films has attracted enormous attention for photocatalysis. It combines the fundamental properties of TiO2 as a large bandgap semiconductor with the advantage of thin films, making it competitive with TiO2 powders for recycling and maintenance in photocatalytic applications. There are many aspects affecting the photocatalytic performance of thin film structures, such as the nanocrystalline size, surface morphology, and phase composition. However, the quantification of each influencing aspect needs to be better studied and correlated. Here, we prepared a series of TiO2 thin films using a sol-gel process and spin-coated on p-type, (100)-oriented silicon substrates with a native oxide layer. The as-deposited TiO2 thin films were then annealed at different temperatures from 400 °C to 800 °C for 3 h in an ambient atmosphere. This sample synthesis provided systemic parameter variation regarding the aspects mentioned above. To characterize thin films, several techniques were used. Spectroscopic ellipsometry (SE) was employed for the investigation of the film thickness and the optical properties. The results revealed that an increasing annealing temperature reduced the film thickness with an increase in the refractive index. Atomic force microscopy (AFM) was utilized to examine the surface morphology, revealing an increased surface roughness and grain sizes. X-ray diffractometry (XRD) and UV-Raman spectroscopy were used to study the phase composition and crystallite size. The annealing process initially led to the formation of pure anatase, followed by a transformation from anatase to rutile as the annealing temperature increased. An overall enhancement in crystallinity was also observed. The photocatalytic properties of the thin films were tested using the photocatalytic decomposition of acetone gas in a home-built solid (photocatalyst)-gas (reactant) reactor. The composition of the gas mixture in the reaction chamber was monitored using in situ Fourier transform infrared spectroscopy. Finally, all of the structural and spectroscopic characteristics of the TiO2 thin films were quantified and correlated with their photocatalytic properties using a correlation matrix. This provided a good overview of which film properties affect the photocatalytic efficiency the most.

Physicochemical and Antibacterial Evaluation of TiO2/CNT Mesoporous Nanomaterials Prepared by High-Pressure Hydrothermal Sol-Gel Method under an Ultrasonic Composite Environment

TiO₂ has attracted significant research interest, principally due to its nontoxicity, high stability, and abundance. Carbon-doped TiO₂ can improve light absorption efficiency. In order to prepare high-efficiency photocatalysts, carbon-doped composites were prepared by hydrothermal reaction in a high-pressure reactor, and then TiO₂/CNT mesoporous composites were prepared by the sol-gel method in an ultrasonic environment. Characterized by SEM and TEM, the composite materials contained TiO₂ nanoparticles as well as CNT. After phase analysis, it was the anatase-doped phase. The following infrared light absorption performance and Escherichia coli bactericidal performance tests showed that it had better infrared and visible light absorption performance than pure TiO₂. The TiO₂/CNT mesoporous nanomaterials synthesized in this work are possible for clean industrial productions.