Separation of BTX Fraction from Reservoir Brines by Sorption onto Hydrophobized Biomass in a Fixed-Bed-Column System

Enhanced oil-water emulsion separation through coalescence filtration utilizing milkweed fiber: a sustainable paradigm

Over the past few years, the environment and public safety have suffered due to the detrimental effects of oily industrial effluents. Natural fibers have gained popularity for their affordability, reusability, and effectiveness in separating oil from oily wastewater. Milkweed fibers were characterized using FTIR (Fourier transform infrared spectroscopy), SEM (scanning electron microscopy), and contact angle techniques. With four porosities (0.90, 0.92, 0.95, and 0.98), deep bed coalescence filters were built at three different filter bed heights (10 mm, 20 mm, and 30 mm). Using milkweed coalescence filtering technology, a novel oil separation method is described along with a method to calculate oil film thickness following emulsified oily water saturation. By combining a bed height of 30 mm and a porosity of 0.98, a maximum oil separation of 99.73% and an optimized D50 droplet ratio were achieved. Throughout a prolonged operational period lasting 250 min, the filter bed, possessing a depth of 30 mm and a porosity of 98%, exhibited no discernible fouling indications. Following five cycles, the milkweed filter bed measuring 30 mm in depth and featuring a porosity of 98% displayed an impressive oil separation efficiency of 91.5%. This study found that using a milkweed deep bed filter, coalescence filtering effectively removes oil from oily effluent. Furthermore, milkweed is a natural and biodegradable fiber that is easy to dispose of after use and does not harm the environment.

Oil separation from oil in water emulsion by coalescence filtration using kapok fibre

In this study, the stable emulsion of engine oil in water of concentration 10% was prepared using a non-ionic surfactant. Kapok fibres were used as filter beds to separate oil from the oil-water emulsion. The surface morphology of fibres was investigated using Scanning Electron Microscope (SEM) analysis and chemical bond analysis of fibres done using Fourier transform infrared (FTIR). Kapok filter beds were prepared with three different bed heights 10, 20 and 30 mm each with four different porosities 0.90, 0.92, 0.95 and 0.98 for preparing the coalescence filter. The oil-water emulsion (influent) was pumped into the filtration column and the coalesced oil droplets, water, as well as un-coalesced oil droplets, especially the finer oil droplets, were collected as effluent. Oil separation efficiency was evaluated in terms of change in droplet size (D50) and oil concentration from influent to effluent. With increasing porosity and bed height, apart from porosity of 0.92, the separation efficiency increases. Increasing the bed heights at lower porosities does not improve the efficiency of the process. A combination of 0.98 porosity and a bed height of 30 mm provided the highest filtration performance in terms of oil separation efficiency and D50 droplet ratio. At 0.98 porosity, increasing the bed height from 10 mm to 30 mm resulted in a D50 droplet ratio of 0.25-0.14, representing a significant decrease in droplet size in the effluent and therefore an increase in oil separation efficiency from 91.3% to 99.63%.