Study of How Photoelectrodes Modified by TiO2/Ag Nanofibers in Various Structures Enhance the Efficiency of Dye-Sensitized Solar Cells under Low Illumination

Towards Integration of Two-Dimensional Hexagonal Boron Nitride (2D h-BN) in Energy Conversion and Storage Devices

The prominence of two-dimensional hexagonal boron nitride (2D h-BN) nanomaterials in the energy industry has recently grown rapidly due to their broad applications in newly developed energy systems. This was necessitated as a response to the demand for mechanically and chemically stable platforms with superior thermal conductivity for incorporation in next-generation energy devices. Conventionally, the electrical insulation and surface inertness of 2D h-BN limited their large integration in the energy industry. However, progress on surface modification, doping, tailoring the edge chemistry, and hybridization with other nanomaterials paved the way to go beyond those conventional characteristics. The current application range, from various energy conversion methods (e.g., thermoelectrics) to energy storage (e.g., batteries), demonstrates the versatility of 2D h-BN nanomaterials for the future energy industry. In this review, the most recent research breakthroughs on 2D h-BN nanomaterials used in energy-based applications are discussed, and future opportunities and challenges are assessed.

AgNWs@TiO2 and AgNPs@TiO2 Double-Layer Photoanode Film Improving Light Capture and Application under Low Illumination

In this article, silver nanowires (AgNWs) were prepared and introduced into the double-layer photoanode of dye-sensitized solar cells (DSSCs). Silver nanowires with a diameter of about 50–60 nm and a length of 1–2 mm were prepared by the polyol method. The power conversion efficiency of the double-layer photoanode DSSC made of AgNWs@TiO2 and AgNPs@TiO2 composite materials is 6.38%. Compared with the unmodified DSSC, the composite double-layer photoanode combined with AgNWs and AgNPs increased the efficiency of DSSC by 58.7%. This increased efficiency was mainly due to the localized surface plasmon resonance effect caused by AgNPs and AgNWs. The increased light collection was caused by the plasma effect of AgNPs, and it increased the short-circuit photocurrent density (JSC). The conductive properties of AgNWs improved interface charge transfer and delay charge recombination. The effect of a low light environment on DSSC efficiency was also investigated, and the best photovoltaic conversion efficiency under an irradiance of 10 mW/cm2 was found to be 8.78%.