Formation and Optimization of Electrical Discharge Coatings Using Conventional Electrodes

A comparative characterization analysis of electrode materials for optimal deposition on copper by advancing electrical discharge coating

This research explores the efficiency of Electrical Discharge Coating (EDC) as an advanced surface modification technique using powder suspension, conventional electrodes, and 3D printed electrodes (3DPE), focusing on Ti6Al4V alloys. Conventional Ti electrodes resulted in 100% titanium content with a thickness of 110 µm, while the powder suspension coating was inadequate. The use of 3D printed electrodes showed promising results, with uniform deposition of 61.20 µm thickness and enhanced surface properties under 10 A current. Further analysis of 3D printed Ti6Al4V EDC revealed a higher Ti percentage of 44.20%, TiC formation of 84.17%, and enhanced microhardness with lower surface roughness. Thorough optimization of 3D printed electrode EDC has been undertaken. The study suggests the potential replacement of traditional electrodes such as powder metallurgy with 3D printed counterparts, advancing surface modification techniques and opening new avenues for materials engineering and manufacturing processes.

Improving Micro-EDM Machining Efficiency for Titanium Alloy Fabrication with Advanced Coated Electrodes

Enhancing the operational efficacy of electrical discharge machining (EDM) is crucial for achieving optimal results in various engineering materials. This study introduces an innovative solution-the use of coated electrodes-representing a significant advancement over current limitations. The choice of coating material is critical for micro-EDM performance, necessitating a thorough investigation of its impact. This research explores the application of different coating materials (AlCrN, TiN, and Carbon) on WC electrodes in micro-EDM processes specifically designed for Ti-6Al-4V. A comprehensive assessment was conducted, focusing on key quality indicators such as depth of cut (Z), tool wear rate (TWR), overcut (OVC), and post-machining surface quality. Through rigorous experimental methods, the study demonstrates substantial improvements in these quality parameters with coated electrodes. The results show significant enhancements, including increased Z, reduced TWR and OVC, and improved surface quality. This evidence underscores the effectiveness of coated electrodes in enhancing micro-EDM performance, marking a notable advancement in the precision and quality of Ti-6Al-4V machining processes. Among the evaluated coatings, AlCrN-coated electrodes exhibited the greatest increase in Z, the most significant reduction in TWR, and the best OVC performance compared to other coatings and the uncoated counterpart.

Evaluation of Bronze Electrode in Electrical Discharge Coating Process for Copper Coating

One of the widely used non-traditional machines for machining of hard materials into complex shapes and different sizes is the electrical discharge machine (EDM). Recently, the EDM has been used for deposition by controlling the input parameters (current and duty cycle). This work was carried out to evaluate the readily available bronze (88% Cu + 12% Sn) electrode for deposition of copper material on titanium alloy. Experiments were conducted according to Taguchi experimental design considering the input parameters of current, Ton, Toff and preheating temperature of substrates. Titanium alloy was further hardened by preheating at temperatures of 100 °C, 300 °C and 500 °C and quenching in brine, castor oil and vegetable oil in order to avoid workpiece erosion. After this treatment, hardness, grain area, grain diameter and number of grains were characterized to compare with pretreated substrates. Then, the treated substrates were taken for copper deposition with the EDM. Output parameters such as material deposition rate (MDR), electrode wear rate (EWR), coating thickness (CT), elemental composition and surface crack density (SCD) were found. Material characterization was carried out using a scanning electron microscope (SEM) with energy dispersive X-ray spectroscopy (EDX) and optical microscopy. Output parameters were optimized with technique for order of preference by similarity to ideal solution (TOPSIS) to find optimum parameters. A sixth experiment with parameter values of Ton of 440 µs, Toff of 200 µs, preheating temperature of 300 °C and quenching medium of castor oil was optimum with MDR of 0.00506 g/m, EWR of 0.00462 g/m, CT of 40.2 µm and SCD 19.4 × 10⁷ µm².

SWOT Analysis of Electrical Discharge Coatings: A Case Study of Copper Coating on Titanium Alloy

The electrical discharge machine (EDM) has been one of the most widely used non-traditional machines in recent decades, primarily used for machining hard materials into various complex shapes and different sizes and, nowadays, used for surface modifications/hard coatings. In this study, the SWOT (strengths, weaknesses, opportunities and threats) of electrical discharge coating was analyzed by conducting a case study. For the purpose of the case study, copper was deposited on the titanium alloy surface (Ti6Al4V). Three electrodes of different copper alloy materials, viz., brass, bronze and copper, were selected for coating the Ti6Al4V surface. Input parameters such as current, pulse-on, pulse-off, flushing pressure and the electrode material were optimized to develop a uniform coating. Experiments were designed according to the L18 orthogonal array, and among them, the samples that showed proper coating, as seen with the naked eye, were selected for morphological and elemental analyses by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX. Further, the output responses, viz., the material deposition rate (MDR), electrode wear rate (EWR), surface roughness (SR), elemental data (copper (Cu) and zinc (Zn)) and coating thickness (CT), were considered for the optimization of coatings. Implementing the Technique for Order Performance by Similarity to Ideal Solution, copper coating with a thickness of 20.43 µm, developed with an MDR with input parameters of 20 A current, 600 µs pulse-on, 120 µs pulse-off, 0.5 bar flushing pressure and the brass electrode, was selected as the optimum coating. The most influential parameters in this coating process were the current and pulse-on time. In this study, a SWOT table was developed to depict the strengths, weaknesses, opportunities and threats of electrical discharge coating.