Preparation and Characterization of Cu-Mn-Ce@γ-Al2O3 to Catalyze Ozonation in Coal Chemical Wastewater-Biotreated Effluent

An ozone catalytic oxidation system for the degradation of organic compounds in secondary wastewater from refining and chemical processes

To overcome the low catalytic efficiency, insufficient catalyst strength, and poor ozone circulation in the advanced treatment of secondary wastewater, a hollow cylindrical Fe-Cu-Ce-Mn/Al2O3 catalyst was prepared by the step impregnation method. Compared with the common impregnation method, the step impregnation method produced a more uniform and compact distribution of each metal element, which was more conducive to generating the synergistic effect of various metals; thus, increasing the mineralization rate of organic matter. The hollow cylindrical design ensured the strength of the catalyst and the circulation of ozone. The reduction of the chemical oxygen demand (COD) was compared under different experimental conditions, with the optimal conditions found to be an ozone contact time of 40 min and ozone dosage of 40 mg/L. The average COD, ammonia nitrogen, and ultraviolet absorbance at 254 nm (UV254) removal rates were 36%, 19%, and 20%, respectively. After 3 weeks of continuous experiment, the removal rate was still high. Following analysis by three dimensional fluorescence, GC-MS, and the molecular weight detection of water samples before and after treatment, it was found that the catalyst enhanced the effect of ozone on wastewater treatment, with a significant removal of tryptophan-like aromatic proteins and soluble microbial metabolites, and the removal of most of the small molecular organic matter. In addition, part of the refractory organic matter could be converted into easily degradable organic matter, which greatly improved the biodegradability and mineralization rate of wastewater, and provided good conditions for subsequent treatment.

The Effect of Magnetic Composites (γ-Al2O3/TiO2/γ-Fe2O3) as Ozone Catalysts in Wastewater Treatment

Using municipal sewage as a source of reclaimed water is an important way to alleviate the shortage of water resources. At present, advanced oxidation technology (AOPs), represented by ozone oxidation, is widely used in wastewater treatment. In this study, γ-Al₂O₃, a low-cost traditional ozone catalyst, was selected as the matrix. By modifying magnetic γ-Fe₂O₃ with a titanate coupling agent, in situ deposition, and calcination, the final formation of a γ-Al₂O₃/TiO₂/γ-Fe₂O₃ micrometer ozone catalyst was achieved. A variety of material characterization methods were used to demonstrate that the required material was successfully prepared. The catalyst powder particles have strong magnetic properties, form aggregates easily, and have good precipitation and separation properties. Subsequently, ibuprofen was used as the degradation substrate to investigate the ozone catalytic performance of the prepared catalyst, and this proved that it had good ozone catalytic activity. The degradation process was also analyzed. The results showed that in the ozone system, some of the ibuprofen molecules will be oxidized to form 1,4-propanal phenylacetic acid, which is then further oxidized to form 1,4-acetaldehyde benzoic acid and p-phenylacetaldehyde. Finally, the prepared catalyst was applied to the actual wastewater treatment process, and it also had good catalytic performance in this context. GC-MS detection of the water samples after treatment showed that the types of organic matter in the water were significantly reduced, among which nine pollutants with high content, such as bisphenol A and sulfamethoxazole, were not detected after treatment.

Recent Developments in Activated Carbon Catalysts Based on Pore Size Regulation in the Application of Catalytic Ozonation

Due to its highly developed pore structure and large specific surface area, activated carbon is often used as a catalyst or catalyst carrier in catalytic ozonation. Although the pore structure of activated carbon plays a significant role in the treatment of wastewater and the mass transfer of ozone molecules, the effect is complicated and unclear. Because different application scenarios require catalysts with different pore structures, catalysts with appropriate pore structure characteristics should be developed. In this review, we systematically summarized the current adjustment methods for the pore structure of activated carbon, including raw material, carbonization, activation, modification, and loading. Then, based on the brief introduction of the application of activated carbon in catalytic ozonation, the effects of pore structure on catalytic ozonation and mass transfer are reviewed. Furthermore, we proposed that the effect of pore structure is mainly to provide catalytic active sites, promote free radical generation, and reduce mass transfer resistance. Therefore, large external surface area and reasonable pore size distribution are conducive to catalytic ozonation and mass transfer.