Application of the Intraoral Scanner in the Diagnosis of Dental Wear: An In Vivo Study of Tooth Wear Analysis

A two-year clinical trial of enamel wear opposing 5Y-TZP and lithium disilicate crowns

STATEMENT OF PROBLEM

Clinical information on enamel wear opposing 5 mol% yttria-stabilized tetragonal zirconia polycrystal (5Y-TZP) or lithium disilicate crowns is lacking. Moreover, the effect of surface roughness on the wear of enamel antagonists remains unclear.

PURPOSE

The purpose of this clinical study was to quantify the vertical wear and total volume of wear while also measuring the surface roughness of antagonists at 6-month intervals over 2 years.

MATERIAL AND METHODS

A tooth-supported first molar 5Y-TZP Lava Esthetic Fluorescent Zirconia crown or an IPS e.max CAD lithium disilicate crown was randomly provided for 24 participants (n=12). The contralateral first molar and opposite teeth were the natural enamel controls. The crowns were fabricated using computer-aided design and computer-aided manufacturing (CAD-CAM) technology and then polished. The data were gathered every 6 months at recall appointments with an intraoral scanner and a polyvinyl siloxane impression. A 3-dimensional (3D) comparative software program was used to measure the maximum vertical and volume loss on opposing enamel, as well as on the enamel control on the opposite side of the mouth. The surface of epoxy resin replicas was analyzed using a scanning electron microscope. The surface roughness of the cusp replica was measured with a 3D laser microscope. The crown's antagonist enamel and natural enamel wear were compared using a 2-way repeated measure ANOVA (α=.05).

RESULTS

No significant difference was found in the average volume loss between the crown's antagonist enamel (ZTE 0.042 ±0.005 mm3, LTE 0.048 ±0.006 mm3) and the enamel control (ZCE 0.046 ±0.004 mm3, LCE 0.050 ±0.005 mm3) (P>.05). No significant difference was found in surface roughness between the crown's antagonist enamel (antagonist enamel of zirconia group [ZTE] 0.7 ±0.3 µm, antagonist enamel of lithium disilicate group [LTE] 0.6 ±0.3 µm) and the enamel control (enamel control of zirconia group [ZCE] 0.7 ±0.3 µm, enamel control of lithium disilicate group [LCE] 0.5 ±0.2 µm) in both zirconia and lithium disilicate groups (P>.05). Also, no correlation was found between the amount of wear and the roughness of the surface. The wear patterns observed on the opposing enamel surfaces of the monolithic zirconia and lithium disilicate materials were found to be similar to those seen on natural enamel.

CONCLUSIONS

A 2-year clinical investigation found that polished lithium disilicate and 5Y-TZP crowns did not affect enamel wear more than enamel against enamel, contrary to laboratory studies. Another finding revealed that surface roughness did not significantly affect wear.

Assessing tooth wear progression in non-human primates: a longitudinal study using intraoral scanning technology

Intraoral scanners are widely used in a clinical setting for orthodontic treatments and tooth restorations, and are also useful for assessing dental wear and pathology progression. In this study, we assess the utility of using an intraoral scanner and associated software for quantifying dental tissue loss in non-human primates. An upper and lower second molar for 31 captive hamadryas baboons (Papio hamadryas) were assessed for dental tissue loss progression, giving a total sample of 62 teeth. The animals are part of the Southwest National Primate Research Center and were all fed the same monkey-chow diet over their lifetimes. Two molds of each dentition were taken at either two- or three-year intervals, and the associated casts scanned using an intraoral scanner (Medit i700). Tissue loss was calculated in WearCompare by superimposition of the two scans followed by subtraction analysis. Four individuals had dental caries, and were assessed separately. The results demonstrate the reliability of these techniques in capturing tissue loss data, evidenced by the alignment consistency between scans, lack of erroneous tissue gain between scans, and uniformity of tissue loss patterns among individuals (e.g., functional cusps showing the highest degree of wear). The average loss per mm2 per year for all samples combined was 0.05 mm3 (0.04 mm3 for females and 0.08 mm3 for males). There was no significant difference in wear progression between upper and lower molars. Substantial variation in the amount of tissue loss among individuals was found, despite their uniform diet. These findings foster multiple avenues for future research, including the exploration of wear progression across dental crowns and arcades, correlation between different types of tissue loss (e.g., attrition, erosion, fractures, caries), interplay between tissue loss and microwear/topographic analysis, and the genetic underpinnings of tissue loss variation.

Intraoral Scanning for Monitoring Dental Wear and Its Risk Factors: A Prospective Study

Dental wear arises from mechanical (attrition or abrasion) and chemical (erosion) factors. Despite its prevalence and clinical significance, accurately measuring and understanding its causes remain challenging in everyday practice. This one-year study with 39 participants involved comprehensive examinations and full-arch intraoral scans at the start and after 12 months. Volume loss exceeding 100 µ on each tooth's surfaces (buccal, lingual/palatine and incisal/occlusal) was measured by comparing three-dimensional scans from both time points. This study also assessed factors such as abrasion and erosion through clinical exams and questionnaires. There were no significant differences in dental wear in participants with sleep bruxism. However, noticeable wear occurred in the front teeth of those with waking bruxism and joint-related symptoms. Increased wear was associated with frequent consumption of acidic drinks, regular swimming, dry mouth, nocturnal drooling and heartburn, while no significant wear was found in patients with reflux. The used methodology proved effective in accurately assessing the progression of dental wear, which is important as many patients may initially be asymptomatic. The variability observed in dental wear patterns underscores the need to develop specific software applications that allow immediate and efficient comparison of wear areas based on extensive analysis of patient databases.

Tooth Wear Evaluation System 2.0-Evaluation of diagnostic reliability in the assessment of signs and symptoms for tooth wear by non-experts

BACKGROUND

Tooth wear is a multifactorial condition that manifests through various signs and symptoms. These individual signs and symptoms were described in multiple studies, leading to the inclusion in TWES 2.0 (Tooth Wear Evaluation System 2.0) and the forthcoming DC-TW (Diagnostic Criteria for Tooth Wear). However, a study evaluating their reliability has yet to be conducted.

OBJECTIVE

The aim of the study was to examine the reliability in the assessment of 6 signs of pathological tooth wear and 18 clinical signs and symptoms determining aetiology, all of which are included in the TWES 2.0/DC-TW.

METHODS

48 dental students (operators) evaluated patient cases from a patient pool of 14 patients on dental casts and high-resolution intraoral photographs. The agreement between all operators for each sign and symptom was calculated based on ICC (Intraclass Correlation Coefficients). Additionally, the agreement of each operator's evaluation with a predefined sample solution was calculated based on Cohen's kappa.

RESULTS

Inter-user agreement ranged from near perfect (0.91) to poor (0.02) for the various pathology signs or aetiology symptoms of tooth wear (mean 0.32). The agreements of the operator's ratings compared to the sample solution resulted in Cohen's kappa from 0.18 to 1 (mean 0.59) for the pathology signs and ranged from 0.02 to 0.51 for the aetiology signs (mean 0.38).

CONCLUSIONS

The reliability of the signs and symptoms examined and the ability of individual investigators to correctly identify and assign signs and symptoms varied widely. The current assessment tools for the qualification of tooth wear need further refinement, and examiners need intensive training in tooth wear assessment.

Performance of self-cured versus light-cured universal adhesive in patients with non-carious cervical lesions: 18-month randomized clinical trial

OBJECTIVE

To evaluate the clinical performance of self versus light-cured universal adhesive in non-carious cervical lesions (NCCLs) after 18 months.

MATERIALS AND METHODS

Sixty-eight NCCLs in 28 patients were divided into two equal groups; G1: self-cured universal adhesive (Palfique,Tokuyama,Japan) and G2: light-cured universal adhesive (Single Bond Universal,3 M ESPE,USA). Nanohybrid resin composite (Z350XT, 3 M ESPE, USA) was used as a final restoration. Evaluation for fracture, loss of retention, marginal adaptation and discoloration were done after 1 week, 6,12, and 18 months using FDI criteria. Postoperative sensitivity was assessed after 1 week. Chi-Square and Mann-Whitney tests with statistical significance at (P ≤ 0.05) were used for intergroup comparison,while the intragroup one was performed using the Cochran's Q and Friedman's tests. Survival rate was analyzed using Kaplan-meier and Log-rank test.

RESULTS

Both groups exhibited fracture and retention loss, however, there was statistically significant difference favoring the control group at 6 months (p = 0.0114,0.0016). For secondary outcomes, marginal adaptation and discoloration revealed no significant differences. For postoperative sensitivity, there was a significant difference favoring the control group (p = 0.0007, 0.0011). Palfique had 1.5 Relative-Risk (RR) after 6 months (95% CI 0.5659-4.2617; P = 0.3928) and 20% less risk of failure after 18 months (RR 0.8) (95% CI 0.4618-1.3858; P = 0.4260). Tested adhesives showed equal survival rate (P = 0.5685).

CONCLUSIONS

Both adhesives revealed similar clinical performance in restoring the NCCLs after 18 m, however, the early failure was more frequent in the self-cured universal adhesive.

3D quantitative analysis and SEM qualitative analysis of natural antagonist enamel opposing CAD-CAM monolithic zirconia or lithium disilicate tooth-supported crowns versus enamel opposing natural enamel

PURPOSE

This study aimed to evaluate the maximum vertical wear, volume wear, and surface characteristic of antagonist enamel, opposing monolithic zirconia or lithium disilicate crowns.

MATERIALS AND METHODS

The study comprised 24 participants (n = 12), who were randomly allocated to receive either a 5 mol% Y-TZP or a lithium disilicate crown in positions which would oppose the natural first molar tooth. The contralateral first molar along with its antagonist was considered as the enamel opposing natural enamel control. Data collection was performed using an intraoral scanner and polyvinylsiloxane impression. The means of the maximum vertical loss and the volume loss at the occlusal contact areas of the crowns and the various natural antagonists were measured by 3D comparison software. A scanning electron microscope was subsequently used to assess the wear characteristics.

Results

The one-year results from 22 participants (n = 11) indicated no significant differences when comparing the zirconia crown's antagonist enamel (40.28 ± 9.11 µm, 0.04 ± 0.02 mm3) and the natural enamel wear (38.91 ± 7.09 µm, 0.04 ± 0.02 mm3) (P > .05). Also, there is no significant differences between lithium disilicate crown's antagonist enamel (47.81 ± 9.41 µm, 0.04 ± 0.02 mm3) and the natural enamel wear (39.11 ± 7.90 µm, 0.04 ± 0.02 mm3) (P > .05).

Conclusion

While some studies suggested that monolithic zirconia caused less wear on opposing enamel than lithium disilicate, this study found similar wear levels to enamel for both materials compared to natural teeth.

Comparison between intraoral scanning and direct visual analysis for the assessment of developmental defects of enamel

OBJECTIVE

To compare direct visual analysis (DVA) and intraoral scanning (IOS) for the assessment of developmental defects of the enamel (DDE).

METHODS

Thirty-nine extracted permanent human teeth with DDE were selected by an experienced examiner and digitised using IOS. The scanning was recorded using the OBS Studio software parallel to the IOS software to obtain a coloured high-definition MP4 file of the process. Two other experienced, blinded, and calibrated examiners randomly analysed the same teeth through DVA and IOS. A third examiner resolved any disagreements between the two examiners. Descriptive statistics were used to analyse the frequencies of the scores. Cohen's kappa test was used to determine whether the DVA scores were different from those assigned using IOS. Spearman's test was used to verify non-random examiner errors. The Chi-square test was used to compare score frequencies. Statistical significance was set at p <0.05.

RESULTS

Scores indicating more severe and extended DDE (p <0.05) were more frequently assigned with IOS than with DVA (IOS: 25.64%, 25.64%, 38.46%, and 35.90% between one-third to two-third of the lingual, occlusal, mesial, and distal surfaces, respectively; vs. DVA: 10.26%, 7.69%, 15.38%, and 10.26% for the respective aforementioned tooth surfaces). Contrarily, 'no visible enamel defect' was significantly less assigned for IOS than for DVA (IOS: 15.38%, 43.59%, 35.90%, 15.38%, and 17.95% for buccal, lingual, occlusal, mesial, and distal surfaces, respectively; vs. DVA: 38.46%, 66.67%, 56.41%, 51.28%, and 43.59% for the respective aforementioned tooth surfaces). Kappa agreement ranged from fair to moderate when comparing DVA and IOS; the correlation between both methods was positive, indicating that the examiners assigned the scores properly and the differences arose from employing different methods.

CONCLUSION

The assessment of DDE differed depending on the method used. IOS scores indicated more severe and extended DDE than DVA scores. Clinical investigation is the next step in validating the use of IOS for DDE diagnosis.

CLINICAL SIGNIFICANCE

This study showed that DDE can be assessed differently using IOS. It is clinically relevant as it directly affects the determination of the severity of the defect and dental treatment planning.

Diagnostic Applications of Intraoral Scanners: A Systematic Review

In addition to their recognized value for obtaining 3D digital dental models, intraoral scanners (IOSs) have recently been proven to be promising tools for oral health diagnostics. In this work, the most recent literature on IOSs was reviewed with a focus on their applications as detection systems of oral cavity pathologies. Those applications of IOSs falling in the general area of detection systems for oral health diagnostics (e.g., caries, dental wear, periodontal diseases, oral cancer) were included, while excluding those works mainly focused on 3D dental model reconstruction for implantology, orthodontics, or prosthodontics. Three major scientific databases, namely Scopus, PubMed, and Web of Science, were searched and explored by three independent reviewers. The synthesis and analysis of the studies was carried out by considering the type and technical features of the IOS, the study objectives, and the specific diagnostic applications. From the synthesis of the twenty-five included studies, the main diagnostic fields where IOS technology applies were highlighted, ranging from the detection of tooth wear and caries to the diagnosis of plaques, periodontal defects, and other complications. This shows how additional diagnostic information can be obtained by combining the IOS technology with other radiographic techniques. Despite some promising results, the clinical evidence regarding the use of IOSs as oral health probes is still limited, and further efforts are needed to validate the diagnostic potential of IOSs over conventional tools.

Intraoral scanner-based monitoring of tooth wear in young adults: 24-month results

OBJECTIVES

Tooth wear causes irreversible cumulated surface loss and already occurs at a young age. Therefore, the objective of this clinical prospective observational study was to monitor the occlusal surface of a mandibular first molar in young adults for a period of 24 months. Furthermore, potential aetiological factors obtained by a questionnaire were considered.

MATERIALS AND METHODS

The study teeth (FDI #36 or #46) of 81 participants (mean age 22.8 ± 2.2 years) were scanned with the intraoral scanner (IOS, Trios 3, 3Shape) at the second follow-up (T2) after an observation period of 24 months. Standard-tessellation-language datasets were superimposed with baseline (T0) and T2 scans in 3D analysis software (GOM Inspect). The maximum vertical substance loss was measured between T0 and T2 at 6/7 areas (4/5 cusps and 2 ridges) of each study tooth and data compared to the already published data of the first follow-up (T1) after 12-month observation period. The morphology of tooth wear was classified into three groups: cupping (C), facet (F) and combined cupping-facet (CF). The analysis of aetiological factors, such as acid impacts, was based on a questionnaire filled out by participants at time points T0, T1 and T2. Non-parametric tests were used for statistical analysis (p < 0.05).

RESULTS

The buccal load-bearing cusps (mesiobuccal: median 15 μm, 95%CI 11/18 μm; mesiolingual 8 μm, 0/11 μm) were most affected by tooth wear. Loss values increased significantly at T2 compared to T1 for all areas, although significantly less than in the first 12 months (T0-T1). Areas that already exhibited F at T0 mostly displayed them also at T2 and only rarely developed further into C or CF. The only association between aetiological factors and loss values could be detected for sex as males had significantly higher loss values than females.

CONCLUSIONS

Progression of tooth wear could be clearly shown with high interindividual variations in loss values among participants. This indicates the need for individual monitoring with IOS.

CLINICAL RELEVANCE

IOSs show the potential for patient-specific monitoring to detect the progression of tooth wear. Thus, data of 24 months fills the gap of tooth wear data for young adults in literature. Further studies over a longer observation period are highly recommended to gain more information about the dynamic of tooth wear and aetiological factors.

Effect of defect size and tooth anatomy in the measurements of a 3D patient monitoring tool

Purpose

To assess the influence of defect size and tooth anatomy on the measurements performed by a 3D patient monitoring tool.

Methods

A fully dentate model was scanned to obtain a master digital file. Virtual duplicates received defects created in molars (16, 18, 28) and incisors (11, 12, 22), according to different depths (60, 80, 120 microns) and sizes (small, medium, large) totaling 180 conditions. The surface changes measured by the 3D Patient Monitoring Tool (3Shape TRIOS Patient Monitoring [TPM]) were compared with the reference by 2 calibrated operators. False Positives (FP), and False Negatives (FN) defect were registered. Pearson chi-square test, Multivariate binary logistic regression and Spearman rank correlation were used to evaluate the data (α = 0.05).

Results

A significant association was found between the area and the presence of FP and FN (P < .01). Larger defects had higher chances to present FP or an FN respectively. There was a significant association between the tooth and the presence of a FP value (FP, P = .02; FN, P = .005) specially in molars. No significant association was found between the defect depth and the presence of a FP value. Spearman rank correlation showed a strong association between the presence of an FP and an FN (r = 0.858, P < .01).

Conclusions

The defect size and tooth anatomy significantly affected the virtual follow-up, whereas defect depth did not. Small defects were correctly detected in all cases. An incorrect measurement on one side of the tooth simultaneously resulted in incorrect measurement on the opposite side.

Clinical relevance

The clinician should be aware that different factors related to the characteristics of the defects could affect the quality of the full-arch digital follow-up. Therefore, caution is needed when interpreting the models comparison in cases that a larger area of a tooth has been modified.

Enamel Wear of Antagonist Tooth Caused by Dental Ceramics: Systematic Review and Meta-Analysis

BACKGROUND

This systematic review and meta-analysis aimed to evaluate the wear of the antagonist tooth in ceramic restorations.

MATERIAL AND METHODS

This study was carried out based on Preferred Reporting Items for Systematic Review and Meta-analysis (PRISMA) recommendations; it was also registered in PROSPERO (register number: CRD42022316252). Three databases were consulted in the literature search, Embase, Scopus, and Web of Science. The citation searching was conducted by two researchers independently. The clinical studies that evaluated wear in antagonist teeth concerning ceramic restoration were included. Twelve articles were selected after eliminating duplicates ones and applying the inclusion criteria, and two were chosen through citation. Fourteen articles were considered for the qualitative and quantitative analysis (meta-regression and meta-analysis).

RESULTS

The mean linear wear of the antagonist tooth in relation to feldspathic was 8.914 μm, for lithium disilicate it was 0.018 μm, and for zirconia it was 0.257 μm. The mean volumetric wear of the antagonist tooth in relation to feldspathic was 0.273 mm3, for hybrid ceramic it was 0.030 mm3, for lithium disilicate it was 0.018 mm3, and for zirconia it was 0.014 mm3. The mean natural tooth wear was 0.7974 μm per month. Tooth wear caused by zirconia at six months was 31.755 μm, at 12 months it was 24.648 μm, and at 24 months it was 20.662 μm.

CONCLUSIONS

Feldspathic produces greater wear of the antagonist tooth from ceramic restorations linearly and volumetrically. In addition, zirconia generates the least wear that will decrease over time, and it will be equal to or less than the natural wear in the tooth.