Thermal Behavior of a Light Timber-Frame Wall vs. a Theoretical Simulation with Various Insulation Materials

Experimental Assessment of Hemp Shiv and Green Adhesives to Produce a Biocomposite Material

This study investigated the utilization of innovative green composites made from hemp shiv, a waste by-product of hemp cultivation, with the aim of promoting sustainability within the construction industry. The manufacturing method involved the application of pressure in a mold to create the samples. These materials were produced using an environmentally friendly binder consisting of colophony, arabic gum, and corn starch. Moreover, white glue and bioepoxy were also used to compare with the green resins. Three different binder compositions were used for the specimens. The samples underwent mechanical testing through tensile and bending assessments, and their performance was compared to that of non-green binders to validate the effectiveness of the manufacturing processes. The study revealed that decreasing the moisture content during the curing process was crucial for improving the mechanical properties. The best results were achieved when using arabic gum as a binder, yielding a tensile strength of 2.16 MPa and a bending strength of 5.25 MPa, with a composition of 62.5% hemp shiv and a manufacturing process involving a pressure of 5 MPa.

Environmental and Energy-Efficiency Considerations for Selecting Building Envelopes

Life cycle assessments in the construction industry reveal that 70–80% of all CO2 emissions occur precisely at the stage of material production (stages A1–A3 of the life cycle). Therefore, not only does the strength and thermal properties of the material selected for construction have major importance, but also the environmental impact of the material and the amount of energy spent to extract, manufacture and transport the materials. The paper presents the thermal calculations for envelope structures, assessing their environmental impact with respect to three parameters: carbon dioxide emissions, total energy consumption and amount of waste generated during material production. The research method used was an analysis of documents from real manufacturers and calculations of the main environmental parameters. Our investigation has led us to conclude that the largest amount of carbon dioxide emissions is produced by structures containing reinforced concrete, since the weight fraction of concrete is significantly greater than that of all other compared materials. The largest amount of non-renewable energy is consumed by structures containing clay bricks and reinforced concrete, since they consist of natural sources. The largest amount of waste is generated by structures containing expanded polystyrene and reinforced concrete consisting of cement, whose production in turn generates a large amount of waste.

A Sustainable Approach to Build Insulated External Timber Frame Walls for Passive Houses Using Natural and Waste Materials

This paper presents structures of timber-framed walls designed for passive houses, using natural and waste resources as insulation materials, such as wool, wood fibers, ground paper, reeds (Phragmites communis), and Acrylonitrile Butadiene Styrene (ABS) wastes. The insulation systems of stud walls composed of wool–ABS composite boards and five types of fillers (wool, ABS, wood fibers, ground paper, and reeds) were investigated to reach U-value requirements for passive houses. The wall structures were designed at a thickness of 175 mm, including gypsum board for internal wall lining and oriented strand board (OSB) for the exterior one. The testing protocol of thermal insulation properties of wall structures simulated conditions for indoor and outdoor temperatures during the winter and summer seasons using HFM-Lambda laboratory equipment. In situ measurements of U-values were determined for the experimental wall structures during winter time, when the temperature differences between outside and inside exceeded 10 °C. The results recorded for the U-values between 0.20 W/m2K and 0.35 W/m2K indicate that the proposed structures are energy-efficient walls for passive houses placed in the temperate-continental areas. The vapour flow rate calculation does not indicate the presence of condensation in the 175 mm thick wall structures, which proves that the selected thermal insulation materials are not prone to degradation due to condensation. The research is aligned to the international trend in civil engineering, oriented to the design and construction of low-energy buildings on the one hand and the use of environmentally friendly or recycled materials on the other.