Development of an Interaction Assay between Single-Stranded Nucleic Acids Trapped with Silica Particles and Fluorescent Compounds

Induction of antigen-specific immunity by mesoporous silica nanoparticles incorporating antigen peptides

Mesoporous silica nanoparticles (MSNs) are physically and chemically stable inorganic nanomaterials that have been attracting much attention as carriers for drug delivery systems in the field of nanomedicine. In the present study, we investigated the potential of MSN vaccines that incorporate antigen peptides for use in cancer immunotherapy. In vitro experiments demonstrated that fluorescently labeled MSNs accumulated in a line of mouse dendritic cells (DC2.4 cells), where the particles localized to the cytosol. These observations could suggest that MSNs have potential for use in delivering the loaded molecules into antigen-presenting cells, thereby stimulating the host acquired immune system. In vivo experiments demonstrated prolonged survival in mice implanted with ovalbumin (OVA)-expressing lymphoma cells (E.G7-OVA cells) following subcutaneous inoculation with MSNs incorporating OVA antigen peptides. Furthermore, OVA-specific immunoglobulin G antibodies and cytotoxic T lymphocytes were detected in the serum and the spleen cells, respectively, of mice inoculated with an MSN-OVA vaccine, indicating the induction of antigen-specific responses in both the humoral and cellular immune systems. These results suggested that the MSN therapies incorporating antigen peptides may serve as novel vaccines for cancer immunotherapy.

A Quantitative Approach to Characterize the Surface Modification on Nanoparticles Based on Localized Dielectric Environments

Nanoparticles (NPs) are utilized for the functionalization of composite materials and nanofluids. Although oxide NPs (e.g., silica (SiO2)) exhibit less dispersibility in organic solvents or polymers due to their hydrophilic surface, the surface modification using silane coupling agents can improve their dispersibility in media with low dielectric constants. Herein, SiO2 NPs were functionalized using octyltriethoxysilane (OTES, C8) and dodecyltriethoxysilane (DTES, C12), wherein the degrees of surface modification of SiO2@C8 and SiO2@C12 were quantitatively evaluated based on the ratio of modifier to surface silanol group (θ) and the volume fraction of organic modifier to total particle volume (ϕR). The variations of surface properties were revealed by analyzing the Hansen solubility parameters (HSP). Particularly, the surface modification using OTES or DTES significantly affected the polarity (δP) of NPs. The local dielectric environments of surface-modified SiO2 NPs were characterized using a solvatochromic dye, Laurdan. By analyzing the peak position of the steady-state emission spectrum of Laurdan in a NP suspension, the apparent dielectric environments surrounding NPs (εapp) were obtained. A good correlation between ϕR and εapp was observed, indicating that ϕR is a reliable quantity for understanding the properties of surface-modified NPs. Furthermore, the generalized polarization (GP) of NPs was investigated. The surface-modified SiO2 NPs with higher ϕR (≥0.15) exhibited GP > 0, suggesting that the modifiers are well-organized on the surface of NPs. The localized dielectric environment surrounding NPs could be predicted by analyzing the volume fraction of nonpolar moieties derived from modifiers. Alternatively, εapp and GP can be utilized for understanding the properties of inorganic-organic hybrid NPs.

Fabrication of TiO2 ̶ KH550 ̶ PEG Super-Hydrophilic Coating on Glass Surface without UV/Plasma Treatment for Self-Cleaning and Anti-Fogging Applications

In this study, we have developed a self-cleaning transparent coating on a glass substrate by dip coating a TiO₂ – KH550 – PEG mixed solution with super-hydrophilicity and good antifogging properties. The fabrication of the thin-film-coated glass is a one-step solution blending method that is performed by depositing only one layer of modified TiO₂ nanoparticles at room temperature. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to determine the structure and morphology of the nanoparticles and the thin-film-coated glass. The surface functional groups were investigated using Fourier-transform infrared spectroscopy (FT-IR), and the optical properties of the glass coating were measured using a UV/Vis spectrometer. The results revealed that the KH-500-modified TiO₂ film coating was in an anatase crystalline form. The hydrophilicity of the coated and uncoated glass substrates was observed by measuring their water contact angle (WCA) using a contact angle instrument. The maximum transparency of the coated glass measured in the visible region (380–780 nm) was approximately 70%, and it possessed excellent super-hydrophilic properties (WCA ~0°) at an annealing temperature of 350 °C without further need of UV or plasma treatment. These results demonstrate the super-hydrophilic coated glass surface has potential for use in self-cleaning and anti-fogging applications.