Tribological Investigation of Layered Zirconium Phosphate in Anhydrous Calcium Grease

Preparation of Zirconium Hydrogen Phosphate Coatings on Sandblasted/Acid-Etched Titanium for Enhancing Its Osteoinductivity and Friction/Corrosion Resistance

Background

Sandblasted/acid-etched titanium (SLA-Ti) implants are widely used for dental implant restoration in edentulous patients. However, the poor osteoinductivity and the large amount of Ti particles/ions released due to friction or corrosion will affect its long-term success rate.

Purpose

Various zirconium hydrogen phosphate (ZrP) coatings were prepared on SLA-Ti surface to enhance its friction/corrosion resistance and osteoinduction.

Methods

The mixture of ZrCl₄ and H₃PO₄ was first coated on SLA-Ti and then calcined at 450°C for 5 min to form ZrP coatings. In addition to a series of physiochemical characterization such as morphology, roughness, wettability, and chemical composition, their capability of anti-friction and anti-corrosion were further evaluated by friction-wear test and by potential scanning. The viability and osteogenic differentiation of MC3T3-E1 cells on different substrates were investigated via MTT, mineralization and PCR assays.

Results

The characterization results showed that there were no significant changes in the morphology, roughness and wettability of ZrP-modified samples (SLA-ZrP0.5 and SLA-ZrP0.7) compared with SLA group. The results of electrochemical corrosion displayed that both SLA-ZrP0.5 and SLA-ZrP0.7 (especially the latter) had better corrosion resistance than SLA in normal saline and serum-containing medium. SLA-ZrP0.7 also exhibited the best friction resistance and great potential to enhance the spreading, proliferation and osteogenic differentiation of MC3T3-E1 cells.

Conclusion

We determined that SLA-ZrP0.7 had excellent comprehensive properties including anti-corrosion, anti-friction and osteoinduction, which made it have a promising clinical application in dental implant restoration.

Lubrication Performance of α-Zirconium Phosphates as an Anti-Wear Additive in Vegetable Oil-Based Anhydrous Calcium Grease

Vegetable oil has significant potential as a base oil, and substitute for mineral oil in grease formulation due to its biodegradability, low toxicity and excellent lubrication. This paper studied the development of vegetable oil-based greases with α-Zr(HPO4)2·H2O (α-ZrP) as an additive, exploring base oil influence in tribological behavior. The results demonstrated that the addition of α-ZrP in vegetable-based greases is beneficial to anti-wear property. α-ZrP particles exhibit good performance in anti-wear, friction-reduction and load-carrying capacity, and its tribological performances are better than the normally used molybdenum disulfide and graphite additives. Owing to its superior tribological properties as a vegetable oil-based grease additive, α-ZrP holds great potential for use in environmentally friendly applications in the future.