Comparative Physicochemical and Electrochemical Characterization of the Structure and Composition of Thin Pd Binary and Ternary Codeposits with Pt, Ru, and Rh

Effect of the Alloying Metal on the Corrosion Resistance of Pd-Rich Binary Alloys with Pt, Rh, and Ru in Sulfuric Acid

The paper presents the study of the corrosion resistance of electrodeposited Pd and its binary alloys with Pt, Rh, and Ru on a polycrystalline Au substrate. The corrosion resistance was tested in 0.5 M sulfuric acid at room temperature using potentiodynamic polarization and electrochemical impedance spectroscopy techniques. The morphology/composition and work function values were determined by scanning electron microscopy/energy-dispersive X-ray spectroscopy and scanning Kelvin probe, respectively. The obtained results revealed that the Pd electrode is the most resistant to corrosion, whereas the Pd-Ru electrode is the most susceptible to dissolution. It was found that the corrosion resistance of Pd-binary alloys decrease in the following order: Pd > Pd-Pt > Pd-Rh > Pd-Ru. This effect was assigned mainly to the difference in surface roughness factor of tested electrodes.

Tuning hydrogen sorption properties of Pd by its alloying with Ru, Rh, and Pt: the study of binary alloys in concentrated alkaline media

The hydrogen electrosorption process was examined in 6 M KOH on Pd binary alloys, containing Rh, Ru, and Pt. Pd-alloys were electrochemically deposited on Au substrate. The electrodes were subjected to activation procedure—hydrogen pretreatment procedure (HPP) at first in 0.5 M H2SO4 and then in 6 M KOH. It was noticed that it was possible to achieve comparable reversibility of hydrogen electrosorption process in acid and in concentrated base. The obtained values of the α→β phase transition potential, hysteresis extent, and maximum hydrogen absorption capacity show good agreement with the data from acidic medium. The observed kinetics of hydrogen electrosorption were strongly hindered in concentrated alkaline media, whereas the influence of the electrolyte on the thermodynamic functions of hydrogen absorption is less pronounced.