Porous Silicon-Based Catalysts for the Dehydration of Glycerol to High Value-Added Products

Structural and optical properties of alginate-based antibacterial dressing with calcium phosphate and zinc oxide for biodegradable wound painting applications

The skin is the outermost part of the body. Although susceptible to damage, the skin is in direct contact with the external environment. Wound dressing is a clinical method that plays a vital role in wound healing. Herein, we developed an antibacterial wound dressing using alginate as the basic material. The dressing was prepared using the solvent casting method, which was used to analyze the effects of adding CaP and ZnO on its structural, optical, and antibacterial properties. Adding CaP exhibited strong but stiff mechanical properties, unlike the CaP/ZnO, which possessed high strength and elasticity. The optical properties of sample S2 did not have a considerable impact. By contrast, the addition of ZnO to sample S3 notably increases the wavelength and absorption value. The diameter of the inhibition zone for S. aureus bacteria exhibited a successive increase in its antibacterial properties, and sample S3 exhibited the highest value. Thus, sample S3 is the most promising wound dressing concerning speeding up the wound healing process because it possesses the most optimal mechanical, optical, and antibacterial properties. The main limitation to be addressed is that sample S3 cannot be easily digested in the environment.

Recent Advances in Carbon-Silica Composites: Preparation, Properties, and Applications

The thermal catalytic conversion of biomass is currently a prevalent method for producing activated carbon with superb textural properties and excellent adsorption performance. However, activated carbon suffers severely from its poor thermal stability, which can easily result in spontaneous burning. In contrast, silica material is famed for its easy accessibility, high specific surface area, and remarkable thermal stability; however, its broader applications are restricted by its strong hydrophilicity. Based on this, the present review summarizes the recent progress made in carbon-silica composite materials, including the various preparation methods using diverse carbon (including biomass resources) and silica precursors, their corresponding structure–function relationship, and their applications in adsorption, insulation, batteries, and sensors. Through their combination, the drawbacks of the individual materials are circumvented while their original advantages are maintained. Finally, several bottlenecks existing in the field of carbon-silica composites, from synthesis to applications, are discussed in this paper, and possible solutions are given accordingly.

Insight into Active Centers and Anti-Coke Behavior of Niobium-Containing SBA-15 for Glycerol Dehydration

Niobium containing SBA-15 was prepared by two methods: impregnation with different amounts of ammonium niobate(V) oxalate (Nb-15/SBA-15 and Nb-25/SBA-15 containing 15 wt.% and 25 wt.% of Nb, respectively) and mixing of mesoporous silica with Nb2O5 followed by heating at 500 °C (Nb2O5/SBA-15). The use of these two procedures allowed obtaining materials with different textural/surface properties determined by N2 adsorption/desorption isotherms, XRD, UV-Vis, pyridine, and NO adsorption combined with FTIR spectroscopy. Nb2O5/SBA-15 contained exclusively crystalline Nb2O5 on the SBA-15 surface, whereas the materials prepared by impregnation had both metal oxide and niobium incorporated into the silica matrix. The niobium species localized in silica framework generated Brønsted (BAS) and Lewis (LAS) acid sites. The inclusion of niobium into SBA-15 skeleton was crucial for the achievement of high catalytic performance. The strongest BAS were on Nb-25/SBA-15, whereas the highest concentration of BAS and LAS was on Nb-15/SBA-15 surface. Nb2O5/SBA-15 material possessed only weak LAS and BAS. The presence of the strongest BAS (Nb-25/SBA-15) resulted in the highest dehydration activity, whereas a high concentration of BAS was unfavorable. Silylation of niobium catalysts prepared by impregnation reduced the number of acidic sites and significantly increased acrolein yield and selectivity (from ca. 43% selectivity for Nb-25/SBA-15 to ca. 61% for silylated sample). This was accompanied by a considerable decrease in coke formation (from 47% selectivity for Nb-25/SBA-15 to 27% for silylated material).

Catalytic Deactivation of HY Zeolites in the Dehydration of Glycerol to Acrolein

The study of the deactivation of HY zeolites in the dehydration reaction of glycerol to acrolein has represented a challenge for the design of new catalysts. HY zeolites with SiO2/Al2O3 molar ratios between 3.5 and 80 were studied. The solids were characterized by XRD, N2 physisorption, SEM-EDXS, Raman and UV-vis spectroscopies, infrared spectroscopy of pyridine (FTIR-Py) and catalytic activity tests from 250 °C to 325 °C. It was found that the total amount of acid sites per unit area of catalyst decreased as the SiO2/Al2O3 molar ratio increased from 3.5 to 80, resulting in the decrease in the initial glycerol conversion. The initial acrolein selectivity was promoted with the increase of the Brønsted/Lewis acid sites ratio at any reaction temperature. The deactivation tests showed that the catalyst lifetime depended on the pore structure, improving with the presence of large surface areas as evidenced by the deactivation rate constants. The characterization of the deactivated catalysts by XRD, N2 physisorption and thermogravimetric analysis indicated that the deposition of coke resulted in the total obstruction of micropores and the partial blockage of mesopores. Moreover, the presence of large mesopores and surface areas allowed the amount of coke deposited at the catalyst surface to be reduced.

A Brief Overview of Recent Progress in Porous Silica as Catalyst Supports

Porous silica particles have shown applications in various technological fields including their use as catalyst supports in heterogeneous catalysis. The mesoporous silica particles have ordered porosity, high surface area, and good chemical stability. These interesting structural or textural properties make porous silica an attractive material for use as catalyst supports in various heterogeneous catalysis reactions. The colloidal nature of the porous silica particles is highly useful in catalytic applications as it guarantees better mass transfer properties and uniform distribution of the various metal or metal oxide nanocatalysts in solution. The catalysts show high activity, low degree of metal leaching, and ease in recycling when supported or immobilized on porous silica-based materials. In this overview, we have pointed out the importance of porous silica as catalyst supports. A variety of chemical reactions catalyzed by different catalysts loaded or embedded in porous silica supports are studied. The latest reports from the literature about the use of porous silica-based materials as catalyst supports are listed and analyzed. The new and continued trends are discussed with examples.