1
|
Karaman GE, Bulut M, Yazan Sukur E. Comparative analysis of shear bond strength of MTA and Theracal PT with different restorative materials. BMC Oral Health 2024; 24:974. [PMID: 39174990 PMCID: PMC11340176 DOI: 10.1186/s12903-024-04763-z] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/03/2024] [Accepted: 08/16/2024] [Indexed: 08/24/2024] Open
Abstract
BACKGROUND This study aimed to compare the in vitro shear bond strength (SBS) of mineral trioxide aggregate (MTA) and dual-cured, resin-modified calcium silicate material (Theracal PT) to composite resin, compomer, and bulk-fill composite, and to evaluate the bond failure mode under a stereomicroscope. METHODS Ninety acrylic specimens, each with a 4 mm diameter and 2 mm height central hole, were prepared. These specimens were randomly divided into two groups based on the capping materials: MTA and Theracal PT. Each group was further subdivided into three subgroups (n = 15) according to the restorative materials: composite resin, compomer, and bulk-fill composite. The specimens were then subjected to shear testing using a universal testing machine at a crosshead speed of 1 mm/min. Post-test, the fracture locations were examined using a stereomicroscope. Data were analyzed using a two-way analysis of variance (ANOVA) and the Tukey test. RESULTS The SBS values for the Theracal PT group were significantly higher than those for the MTA group (p < 0.001). Within the MTA groups, no significant differences were observed in SBS values across the different restorative materials. However, a significant difference was found between the mean SBS values of the Theracal PT + composite resin group and the Theracal PT + compomer group (p < 0.001). CONCLUSIONS Theracal PT shows promise in dentistry due to its superior bond strength. Given its bond values, Theracal PT appears capable of forming durable and long-lasting restorations by establishing reliable bonds with various restorative materials commonly used in dentistry.
Collapse
Affiliation(s)
- Gözde Ece Karaman
- Department of Pediatric Dentistry, Faculty of Dentistry, Istanbul Okan University, Istanbul, Turkey.
| | - Müge Bulut
- Department of Pediatric Dentistry, Faculty of Dentistry, Istanbul Okan University, Istanbul, Turkey
| | - Elif Yazan Sukur
- Department of Pediatric Dentistry, Faculty of Dentistry, Istanbul Okan University, Istanbul, Turkey
| |
Collapse
|
2
|
Bektas I, Hazar Yoruc AB, Cinel L, Ekinci M, Horoz SE, Turet DM, Mentes A. Histological evaluation of different concentrations of hyaluronic-acid-added zinc oxide eugenol on rat molar pulp. Odontology 2024:10.1007/s10266-024-00973-7. [PMID: 38958828 DOI: 10.1007/s10266-024-00973-7] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/28/2024] [Accepted: 06/20/2024] [Indexed: 07/04/2024]
Abstract
Hyaluronic acid (HA), known for diverse properties, was investigated for its potential in dental pulp therapy. This study investigated the potential of HA in dental pulp therapy by examining the physical properties and effects of zinc oxide eugenol (ZOE) pulpotomy materials containing varying HA concentrations on rat molar teeth. In vitro tests assessed compressive strength and hardness of ZOE materials blended with HA (0.5%, 1%, 3%) and HA gels (0.54%, 0.8%). 120 samples, encompassing the control group, underwent compressive strength testing, while 60 samples were designated for hardness assessment. In vivo experiments on rat molars studied histological effects of HA-containing ZOE on dental pulp over 1 week and 1 month. Gels with HA concentrations of 0.5%, 1%, and 0.54% were used in pulpotomy on 22 rats. Each rat underwent the procedure on four teeth, with one tooth serving as a control, totaling 88 teeth subjected to the intervention. In the analyses, SPSS 22.0 was used and the significance level was set at P = 0.05. Findings showed that HA at 0.5% maintained compressive strength, but higher concentrations decreased mechanical properties significantly (P = 0.001). Histological assessments indicated better outcomes with lower HA concentrations in terms of odontoblast layer continuity (P = 0.005 at 1 month) and pulp vitality (P = 0.001 at 1 week and P = 0.018 at 1 month). The study suggests HA holds promise for pulpotomy and regenerative endodontic treatments, but further research is needed to understand long-term clinical implications.
Collapse
Affiliation(s)
- Irmak Bektas
- Department of Pediatric Dentistry, Institute of Health Sciences, Marmara University, Basibuyuk, Saglik Yerleskesi 9/3 Maltepe, 34854, Istanbul, Turkey.
| | - Afife Binnaz Hazar Yoruc
- Department of Metallurgical and Materials Engineering, Yildiz Technical University, Davutpasa Cad. No.127 Esenler,, 34210, Istanbul, Turkey
| | - Leyla Cinel
- Department of Pathology, School of Medicine, Marmara University, Pendik Egitim Arastirma Hastanesi, Ust Kaynarca, Pendik, Istanbul, Turkey
| | - Meltem Ekinci
- Department of Pediatric Dentistry, Institute of Health Sciences, Marmara University, Basibuyuk, Saglik Yerleskesi 9/3 Maltepe, 34854, Istanbul, Turkey
| | - Seher Eda Horoz
- Department of Pathology, School of Medicine, Marmara University, Pendik Egitim Arastirma Hastanesi, Ust Kaynarca, Pendik, Istanbul, Turkey
| | - Deniz Mukaddes Turet
- Experimental Animal Implementation and Research Center, Medical School, Marmara University, Basibuyuk, Maltepe, 34854, Istanbul, Turkey
| | - Ali Mentes
- Department of Pediatric Dentistry, Institute of Health Sciences, Marmara University, Basibuyuk, Saglik Yerleskesi 9/3 Maltepe, 34854, Istanbul, Turkey
- Department of Pediatric Dentistry, School of Dentistry, Marmara University, Basibuyuk, Saglik Yerleskesi 9/3 Maltepe, 34854, Istanbul, Turkey
| |
Collapse
|
3
|
Ergül R, Aksu S, Çalışkan S, Tüloğlu N. Shear bond strength of calcium silicate-based cements to glass ionomers. BMC Oral Health 2024; 24:140. [PMID: 38281948 PMCID: PMC10822172 DOI: 10.1186/s12903-024-03890-x] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/12/2023] [Accepted: 01/12/2024] [Indexed: 01/30/2024] Open
Abstract
BACKGROUND A shear bond strength between the biomaterial and restorative material is crucial for minimizing bacterial microleakage and ensuring a favorable long-term prognosis for vital pulp therapy. This study aimed to conduct a comparative evaluation of the shear bond strength between calcium silicate-based biomaterials utilized in vital pulp treatment and various glass ionomer cement materials, both with and without the application of adhesive agents. METHODS A total of 270 acrylic blocks, each featuring cavities measuring 4 mm in diameter and 2 mm in depth, were prepared. Calcium silicate-containing biomaterials (ProRoot MTA, Medcem Pure Portland Cement, and Medcem MTA), following manufacturers' instructions, were placed within the voids in the acrylic blocks and allowed to set for the recommended durations. The biomaterial samples were randomly categorized into three groups based on the restorative material to be applied: conventional glass ionomer cement, resin-modified glass ionomer cement, and bioactive restorative material. Using cylindrical molds with a diameter of 3.2 mm and a height of 3 mm, restorative materials were applied to the biomaterials in two different methods, contingent on whether adhesive was administered. After all samples were incubated in an oven at 37 °C for 24 h, shear bond strength values were measured utilizing a universal testing device. The obtained data were statistically evaluated using ANOVA and post-hoc Tukey tests. RESULTS The highest shear bond strength value was noted in the Medcem MTA + ACTIVA bioactive restorative material group with adhesive application, while the lowest shear bond strength value was observed in the ProRoot MTA White + Equia Forte HT Fil group without adhesive application (P < 0.05). CONCLUSION Activa Bioactive Restorative may be considered a suitable restorative material in combination with calcium silicate-based biomaterials for vital pulp treatment. The application of adhesives to calcium silicate-based biomaterials can effectively address the technical limitations.
Collapse
Affiliation(s)
| | - Seçkin Aksu
- Department of Pediatric Dentistry, Faculty of Dentistry, Mersin University, Çiftlikköy Campus, Yenişehir, Mersin, Turkey.
| | - Seçil Çalışkan
- Department of Pediatric Dentistry, Faculty of Dentistry, Eskişehir Osmangazi University, Eskişehir, Turkey
| | | |
Collapse
|
4
|
Kunert M, Piwonski I, Hardan L, Bourgi R, Sauro S, Inchingolo F, Lukomska-Szymanska M. Dentine Remineralisation Induced by "Bioactive" Materials through Mineral Deposition: An In Vitro Study. NANOMATERIALS (BASEL, SWITZERLAND) 2024; 14:274. [PMID: 38334546 PMCID: PMC10857417 DOI: 10.3390/nano14030274] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 12/18/2023] [Revised: 01/24/2024] [Accepted: 01/25/2024] [Indexed: 02/10/2024]
Abstract
This study aimed to assess the ability of modern resin-based "bioactive" materials (RBMs) to induce dentine remineralisation via mineral deposition and compare the results to those obtained with calcium silicate cements (CSMs). The following materials were employed for restoration of dentine cavities: CSMs: ProRoot MTA (Dentsply Sirona), MTA Angelus (Angelus), Biodentine (Septodont), and TheraCal LC (Bisco); RBMs: ACTIVA BioACTIVE Base/Liner (Pulpdent), ACTIVA Presto (Pulpdent), and Predicta Bioactive Bulk (Parkell). The evaluation of the mineral deposition was performed through scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX) on the material and dentine surfaces, as well as at the dentine-material interface after immersion in simulated body fluid. Additionally, the Ca/P ratios were also calculated in all the tested groups. The specimens were analysed after setting (baseline) and at 24 h, 7, 14, and 28 days. ProRoot MTA, MTA Angelus, Biodentine, and TheraCal LC showed significant surface precipitation, which filled the gap between the material and the dentine. Conversely, the three RBMs showed only a slight ability to induce mineral precipitation, although none of them was able to remineralise the dentine-material interface. In conclusion, in terms of mineral precipitation, modern "bioactive" RBMs are not as effective as CSMs in inducing dentine remineralisation; these latter represent the only option to induce a possible reparative process at the dentin-material interface.
Collapse
Affiliation(s)
- Marta Kunert
- Department of General Dentistry, Medical University of Lodz, 251 Pomorska St., 92-213 Lodz, Poland;
| | - Ireneusz Piwonski
- Department of Materials Technology and Chemistry, Faculty of Chemistry, University of Lodz, 163 Pomorska St., 90-236 Lodz, Poland;
| | - Louis Hardan
- Department of Restorative Dentistry, School of Dentistry, Saint-Joseph University, Beirut 1107 2180, Lebanon; (L.H.); (R.B.)
| | - Rim Bourgi
- Department of Restorative Dentistry, School of Dentistry, Saint-Joseph University, Beirut 1107 2180, Lebanon; (L.H.); (R.B.)
- Department of Biomaterials and Bioengineering, INSERM UMR_S 1121, University of Strasbourg, 67000 Strasbourg, France
| | - Salvatore Sauro
- Dental Biomaterials and Minimally Invasive Dentistry, Departamento de Odontología, Facultad de Ciencias de la Salud, Universidad CEU-Cardenal Herrera C/Del Pozo ss/n, Alfara del Patriarca, 46115 Valencia, Spain
- Department of Interdisciplinary Medicine, University of Bari “Aldo Moro”, 70124 Bari, Italy;
| | - Francesco Inchingolo
- Department of Interdisciplinary Medicine, University of Bari “Aldo Moro”, 70124 Bari, Italy;
| | | |
Collapse
|
5
|
Celiksoz O, Irmak O. Delayed vs. immediate placement of restorative materials over Biodentine and RetroMTA: a micro-shear bond strength study. BMC Oral Health 2024; 24:130. [PMID: 38273289 PMCID: PMC10811922 DOI: 10.1186/s12903-024-03917-3] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/19/2023] [Accepted: 01/19/2024] [Indexed: 01/27/2024] Open
Abstract
BACKGROUND The aim of the present study was to investigate the micro-shear bond strength (µSBS) of various restorative materials applied on two different fast-setting calcium silicate-based materials and to evaluate the effect of restoration time on µSBS. METHODS A total of 180 acrylic blocks with a cavity in the center were randomly divided into 2 main groups according to the capping material to be used (Biodentine or RetroMTA). The specimens were also randomly divided into 3 groups according to the restoration time (3 min, 12 min, 24 h). After the specified waiting periods, glass hybrid material (EQUIA Forte HT), resin composite (Filtek Z550) and light-cured calcium silicate material (Theracal LC) were placed on the specimens with tygon tubes. The specimens were kept for 24 h and then subjected to µSBS test. Statistical analysis was performed by 3-way ANOVA followed by Tukey test for pairwise comparisons (α = 0.05). RESULTS There is a statistically significant difference (p < 0.05) between the µSBS values obtained by applying resin composite on RetroMTA after different setting times (24 h > 12 min > 3 min). The µSBS obtained for the Biodentine-resin composite at the end of the 3 min setting time is significantly lower (p < 0.05) than the µSBS values at 12 min and 24 h. For both calcium silicate cements, at the end of all time periods, the µSBS obtained when resin composite was applied at the end was higher than the other materials (p < 0.05). CONCLUSIONS For Biodentine-resin composite bonding, the manufacturer's recommendation of 12 min can be considered an appropriate time, whereas for RetroMTA-resin composite bonding, the µSBS increased as the waiting time increased. Regardless of the waiting time, it is recommended to prefer direct composite resin restoration over Biodentine and RetroMTA.
Collapse
Affiliation(s)
- Ozge Celiksoz
- Department of Restorative Dentistry, Faculty of Dentistry, Eskisehir Osmangazi University, Eskisehir, Turkey.
| | - Ozgur Irmak
- Department of Restorative Dentistry, Faculty of Dentistry, Cyprus Health and Social Sciences University, Guzelyurt, Cyprus
| |
Collapse
|
6
|
Sedek EM, Abdelkader S, Fahmy AE, Kamoun EA, Nouh SR, Khalil NM. Histological evaluation of the regenerative potential of a novel photocrosslinkable gelatin-treated dentin matrix hydrogel in direct pulp capping: an animal study. BMC Oral Health 2024; 24:114. [PMID: 38243218 PMCID: PMC10799547 DOI: 10.1186/s12903-024-03868-9] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/01/2023] [Accepted: 01/05/2024] [Indexed: 01/21/2024] Open
Abstract
BACKGROUND To assess histologically the success of the pulp capping approach performed in traumatically exposed dogs' teeth using a novel injectable gelatin-treated dentin matrix light cured hydrogel (LCG-TDM) compared with LCG, MTA and TheraCal LC. METHODS Sixty-four dogs' teeth were divided into two groups (each including 32 teeth) based on the post-treatment evaluation period: group I: 2 weeks and group II: 8 weeks. Each group was further subdivided according to the pulp capping material into four subgroups (n = 8), with subgroup A (light-cured gelatin hydrogel) as the control subgroup, subgroup B (LCG-TDM), subgroup C (TheraCal LC), and subgroup D (MTA). Pulps were mechanically exposed in the middle of the cavity floor and capped with different materials. An assessment of periapical response was performed preoperatively and at 8 weeks. After 2 and 8-week intervals, the dogs were sacrificed, and the teeth were stained with hematoxylin-eosin and graded by using a histologic scoring system. Statistical analysis was performed using the chi-square and Kruskal-Wallis tests (p = 0.05). RESULTS All subgroups showed mild inflammation with normal pulp tissue at 2 weeks with no significant differences between subgroups (p ≤ 0.05), except for the TheraCal LC subgroup, which exhibited moderate inflammation (62.5%). Absence of a complete calcified bridge was reported in all subgroups at 2 weeks, while at 8 weeks, the majority of samples in the LCG-TDM and MTA-Angelus subgroups showed complete dentin bridge formation and absence of inflammatory pulp response with no significant differences between them (p ≤ 0.05). However, the formed dentin in the LCG-TDM group was significantly thicker, with layers of ordered odontoblasts identified to create a homogeneous tubular structure and numerous dentinal tubule lines suggesting a favourable trend towards dentin regeneration. TheraCal LC samples revealed a reasonably thick dentin bridge with moderate inflammation (50%) and LCG showed heavily fibrous tissue infiltrates with areas of degenerated pulp with no signs of hard tissue formation. CONCLUSIONS LCG-TDM, as an extracellular matrix-based material, has the potential to regenerate dentin and preserve pulp vitality, making it a viable natural alternative to silicate-based cements for healing in vivo dentin defects in direct pulp-capping procedures.
Collapse
Affiliation(s)
- Eman M Sedek
- Dental Biomaterials Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt.
| | - Sally Abdelkader
- Dental Biomaterials Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - Amal E Fahmy
- Dental Biomaterials Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - Elbadawy A Kamoun
- Polymeric Materials Research Department, Advanced Technology and New Materials Research Institute, City of Scientific Research and Technological Applications (SRTA-City), New Borg Al-Arab City 21934, Alexandria, Egypt
- Nanotechnology Research Center (NTRC), The British University in Egypt, El-Shreouk City, Cairo, Egypt
| | - Samir R Nouh
- Surgery Department, Faculty of Veterinary Medicine, Alexandria University, Alexandria, Egypt
| | - Nesma Mohamed Khalil
- Oral Biology Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| |
Collapse
|
7
|
Chen CL, Chi CW, Lee CY, Tsai YL, Kasimayan U, K P O M, Lin HP, Chiang YC. Effects of surface treatments of bioactive tricalcium silicate-based restorative material on the bond strength to resin composite. Dent Mater 2024; 40:102-110. [PMID: 37919112 DOI: 10.1016/j.dental.2023.10.027] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/09/2023] [Revised: 10/19/2023] [Accepted: 10/25/2023] [Indexed: 11/04/2023]
Abstract
OBJECTIVES This study aimed to enhance the bond strength between Biodentine™ (BD), a bioactive tricalcium silicate (C3S) based material, and resin composite through various surface treatments. METHODOLOGY BD samples were immersed in either double distilled water or Hank's Balanced Salt Solution and analyzed using X-ray Diffraction (XRD). Shear bond strength (SBS) evaluations of BD were performed using Prime & Bond™ NT (PNT), Single Bond Universal (SBU), Xeno V (Xeno), and glass ionomer cement (GIC) following various etching durations (0 s/ 15 s/ 30 s/ 60 s with 37.5% phosphoric acid). Two primers, RelyX™ Ceramic Primer (RCP) and Monobond ™ Plus (MBP), were chosen to prime BD for SBS enhancement. Fractography and bonding interfaces were examined with energy dispersive X-ray spectroscopy (EDS)/ scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FTIR). RESULTS XRD confirmed BD's main compositions as C3S, Ca(OH)2, CaCO3 and ZrO2 after 14 days crystal maturation. Etched BD did not improve SBS. GIC exhibited the lowest SBS (p < 0.05) among all adhesives, regardless of the etching mode (all < 1 MPa). The highest SBS (17.5 ± 3.6 MPa, p < 0.05) was achieved when BD primed with MBP followed by SBU application. FTIR and EDS showed γ-MPTS and10-MDP within the MBP primer interacted with C3S and ZrO2 of BD, achieving enhanced SBS. Most specimens exhibited mixed or cohesive failure modes. Significance BD's subpar mechanical properties and texture may contribute to its poor adhesion to resin composite. Pretreating BD with MBP primer, followed by SBU adhesive is recommended for improving bond strength.
Collapse
Affiliation(s)
- Che-Lun Chen
- School of Dentistry and Graduate Institute of Clinical Dentistry, National Taiwan University and National Taiwan University Hospital, Taipei, Taiwan; Division of Restorative and Aesthetic Dentistry, Dental Department, National Taiwan University Hospital, No. 1, Chang-Te Street, Taipei 10016, Taiwan
| | - Chih-Wen Chi
- Department of Dentistry, National Taiwan University Hospital, Hsin-Chu Branch, No. 25, Ln. 442, Section 1, Jingguo Rd., North Dist., Hsinchu City 300195, Taiwan
| | - Chen-Yi Lee
- Division of Restorative and Aesthetic Dentistry, Dental Department, National Taiwan University Hospital, No. 1, Chang-Te Street, Taipei 10016, Taiwan
| | - Yi-Ling Tsai
- School of Dentistry and Graduate Institute of Clinical Dentistry, National Taiwan University and National Taiwan University Hospital, Taipei, Taiwan
| | - Uma Kasimayan
- School of Dentistry and Graduate Institute of Clinical Dentistry, National Taiwan University and National Taiwan University Hospital, Taipei, Taiwan
| | - Mahesh K P O
- School of Dentistry and Graduate Institute of Clinical Dentistry, National Taiwan University and National Taiwan University Hospital, Taipei, Taiwan
| | - Hong-Ping Lin
- Department of Chemistry, National Cheng Kung University. No.1, Daxue Rd., Tainan City 701, Taiwan
| | - Yu-Chih Chiang
- School of Dentistry and Graduate Institute of Clinical Dentistry, National Taiwan University and National Taiwan University Hospital, Taipei, Taiwan; Division of Restorative and Aesthetic Dentistry, Dental Department, National Taiwan University Hospital, No. 1, Chang-Te Street, Taipei 10016, Taiwan; Molecular Imaging Center, National Taiwan University, Taipei 10617, Taiwan; School of Dentistry, Kaohsiung Medical University, Kaohsiung 80708, Taiwan.
| |
Collapse
|
8
|
BinSaleh S, Sulimany AM, Aldowsari MK, Al-Homaidhi M, Alkuait N, Almashham L, Alghamdi N. Evaluation of the shear bond strength of a tricalcium silicate-based material to four self-adhering glass ionomer materials: an in vitro study. Front Pediatr 2023; 11:1303005. [PMID: 38111624 PMCID: PMC10726004 DOI: 10.3389/fped.2023.1303005] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 09/27/2023] [Accepted: 11/23/2023] [Indexed: 12/20/2023] Open
Abstract
Background This study aimed to evaluate and compare the shear bond strength (SBS) of EQUIA Forte HT with that of other restorative materials, including EQUIA Forte, glass ionomer cement (GIC), and resin-modified glass ionomer cement (RMGIC) when bonded to NeoMTA 2. Materials and methods A total of 120 holes were created in Teflon molds and filled with NeoMTA 2. The restorative materials were immediately applied using customized silicone molds. The samples were randomly divided into two main groups: one to measure the immediate SBS and the other to measure the delayed SBS. These two main groups were further divided into four subgroups based on the restorative material used: EQUIA Forte HT, EQUIA Forte, GIC, and RMGIC. Results The study groups showed statistically significant differences in the mean SBS (p < 0.0001). The immediate SBS of the RMGIC group (mean ± SD: 5.43 ± 1.22) was significantly higher than those of the GIC and EQUIA Forte groups, with no significant difference found compared to the SBS of EQUIA Forte HT. In the delayed SBS, both the RMGIC and EQUIA Forte HT groups (4.98 ± 0.67 and 4.93 ± 0.60, respectively) demonstrated significantly higher bond strengths than the GIC and EQUIA Forte groups (3.81 ± 0.57 and 4.2 ± 0.63, respectively). However, there were no statistically significant differences between the RMGIC and EQUIA Forte HT groups or between the GIC and EQUIA Forte groups. Conclusion Based on our findings, EQUIA Forte HT has shown promising outcomes when used as a restorative material following pulpotomies, with results comparable to those of RMGIC.
Collapse
Affiliation(s)
- Saad BinSaleh
- Department of Pediatric Dentistry and Orthodontics, College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Ayman M. Sulimany
- Department of Pediatric Dentistry and Orthodontics, College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Mannaa K. Aldowsari
- Department of Pediatric Dentistry and Orthodontics, College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Majedah Al-Homaidhi
- Department of Pediatric Dentistry and Orthodontics, College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Nour Alkuait
- College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Lama Almashham
- College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Nada Alghamdi
- College of Dentistry, King Saud University, Riyadh, Saudi Arabia
| |
Collapse
|
9
|
Candan M, Altinay Karaca FK, Öznurhan F. Evaluation of the Shear Bond Strength of Immediate and Delayed Restorations of Various Calcium Silicate-Based Materials with Fiber-Reinforced Composite Resin Materials. Polymers (Basel) 2023; 15:3971. [PMID: 37836020 PMCID: PMC10575331 DOI: 10.3390/polym15193971] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/24/2023] [Revised: 09/17/2023] [Accepted: 09/20/2023] [Indexed: 10/15/2023] Open
Abstract
Due to significant tissue loss in teeth requiring pulp treatments, hermetic restoration of the remaining dental tissues is one of the most crucial factors in determining the treatment's success. The adhesion of composite resins to calcium silicate cements (CSCs) is considered challenging. Consequently, it is crucial to identify the optimal method for obtaining optimal adhesion. The aim of the present study is to evaluate the shear bond strength (SBS) values of immediate and delayed restorations with fiber-reinforced composites on powder-liquid, premixed, and resin-containing flowable CSCs. In the present study, the SBS values obtained after immediate (14 min) and delayed (7 days) restorations of three different CSCs (NeoMTA2, NeoPutty, and TheraCal PT) with three different resin composite materials (EverX FlowTM, EverX PosteriorTM, and Filtek Z550) were compared. The fracture types were evaluated using a stereomicroscope and SEM. TheraCal PT had the highest SBS values for both immediate and delayed restorations, and the comparison with other materials showed a statistically significant difference (p = 0.001). In contrast, there was no statistically significant difference between the SBS values of NeoMTA and NeoPutty (p > 0.05). In both immediate and delayed restorations, there was no statistically significant difference between nanohybrid and fiber-reinforced composites (p > 0.05). The simple use and strong bonding ability of TheraCal PT with composite resins may provide support for the idea that it is suitable for pulpal interventions. Nevertheless, due to the in vitro nature of this study, additional in vitro and clinical studies are required to investigate the material's physical, mechanical, and biological properties for use in clinical applications.
Collapse
Affiliation(s)
- Merve Candan
- Department of Pedodontics, Faculty of Dentistry, Eskişehir Osmangazi University, Eskişehir 26040, Turkey
| | | | - Fatih Öznurhan
- Department of Pedodontics, Faculty of Dentistry, Sivas Cumhuriyet University, Sivas 58140, Turkey
| |
Collapse
|
10
|
Mohamed DAA, Abdelwahab SA, Mahmoud RH, Taha RM. Radiographic and immuno-histochemical evaluation of root perforation repair using MTA with or without platelet-rich fibrin or concentrated growth factors as an internal matrix in dog's teeth: in vivo animal study. Clin Oral Investig 2023; 27:5103-5119. [PMID: 37500933 PMCID: PMC10492699 DOI: 10.1007/s00784-023-05131-x] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/22/2023] [Accepted: 06/20/2023] [Indexed: 07/29/2023]
Abstract
OBJECTIVES To comparatively evaluate the in vivo outcome of MTA repair for contaminated and non-contaminated furcation perforations (FP) with or without PRF and CGF as a matrix in dogs' teeth. METHODS Ninety dog teeth were divided into five groups based on the iatrogenic FP repair approach after doing root canal treatment: negative control (without FP), positive control (FP without repair), MTA, MTA + PRF and MTA + CGF groups, where FP were repaired promptly in subdivision 1 (n = 10; non-contaminated) and after 4 weeks of oral contamination in subdivision 2 (n = 10;contaminated). After 3 months, the perforation site was assessed radiographically (vertical bone density), histologically (inflammatory cell count, epithelial proliferation, cementum and bone deposition) and immunohistochemically (OPN and TRAP antibodies localisation). Data collected were statistically analysed using SPSS software at a 0.05 significance level. RESULTS The MTA + PRF and MTA + CGF groups demonstrated significantly more bone formation, OPN immunolocalisation and fewer inflammatory cell counts than MTA group. MTA, MTA + PRF and MTA + CGF groups showed significantly favourable radiographic, histological and immunohistochemical healing features than the positive control, especially in non-contaminated subdivisions, that significantly showed better features than the contaminated subdivisions (P < 0.001). CONCLUSION The use CGF and PRF as a matrix beneath MTA in FP repair in dog's teeth is promising as it could increase hard and soft tissue regeneration in non-contaminated and contaminated perforations. CLINICAL RELEVANCE The repair of FP is challenging especially when associated with contaminated inter-radicular bone loss. Radiographic, histological and immunohistochemical comprehensive evaluation of the root and surrounding attachment apparatus response to different perforation repair protocols could give a predictable clinical outcome.
Collapse
Affiliation(s)
- Dalia Abd-Allah Mohamed
- Endodontic Department, Faculty of Dentistry, Suez Canal University, 4.5 Ring Road, Ismailia, 41522 Egypt
| | - Safinaz AbdelFatah Abdelwahab
- Dental Material Department, Faculty of Dentistry, Suez Canal University, 4.5 Ring Road, Ismailia, 41522 Egypt
- Restorative Department, Faculty of Dentistry, Umm Al-Qura University, Mecca, Saudi Arabia
| | - Rania Hanafi Mahmoud
- Oral Pathology Department, Faculty of Dentistry, Suez Canal University, 4.5 Ring Road, Ismailia, 41522 Egypt
- Oral Pathology Department, Faculty of Dentistry, Umm Al-Qura University, Mecca, Saudi Arabia
| | - Rasha Mohamed Taha
- Oral Biology Department, Faculty of Dentistry, Suez Canal University, 4.5 Ring Road, Ismailia, 41522 Egypt
| |
Collapse
|
11
|
Durmazpinar PM, Recen D, Çeliksöz Ö, Yazkan B. Micro shear bond strength of mineral trioxide aggregate to different innovative dental restorative materials. Proc Inst Mech Eng H 2023; 237:762-769. [PMID: 37171056 DOI: 10.1177/09544119231173506] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 05/13/2023]
Abstract
The objective of this in vitro study was to investigate the micro shear bond strength (µSBS) of mineral trioxide aggregate to four different restorative materials. Sixty mineral trioxide aggregate (MTA) samples were randomly assigned into four experimental groups based on the restorative materials used: nanohybrid resin composite as a control, giomer, alkasite and ormocer. µSBS samples were prepared for each group (n = 15). These samples were then submitted to a µSBS test (crosshead speed, 0.5 mm/min). The resulting data were statistically analyzed by one-way analysis of variance (ANOVA), Levene, and Bonferroni tests (α = 0.05). The bond strength of the alkasite group was statistically significantly higher than all the tested groups (p<0.05), while there were no significant differences between the nanohybrid resin composite, giomer, or ormocer groups (p > 0.05). Within the limitations of this study, alkasite restorative material could be a promising material when placed over MTA.
Collapse
Affiliation(s)
| | - Duygu Recen
- Department of Restorative Dentistry, Faculty of Dentistry, Izmir Democracy University, Istanbul, Turkey
| | - Özge Çeliksöz
- Department of Restorative Dentistry, Faculty of Dentistry, Eskisehir Osmangazi University, Eskisehir, Turkey
| | - Başak Yazkan
- Department of Restorative Dentistry, Faculty of Dentistry, Pamukkale University, Denizli, Turkey
| |
Collapse
|
12
|
Al-Ali M, Camilleri J. The scientific management of deep carious lesions in vital teeth using contemporary materials—A narrative review. FRONTIERS IN DENTAL MEDICINE 2022. [DOI: 10.3389/fdmed.2022.1048137] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/25/2022] Open
Abstract
AimThe aim of this article is to review the scientific evidence for deep caries removal in permanent vital teeth and the choice of dentine replacement material and restoration of the teeth to maintain long term tooth vitality and function.MethodThe two position statements namely the European Society of Endodontology and the American Association of Endodontists position statements on vital pulp therapy will be scrutinized and compared with regards to the deep caries removal strategy and assessed for evidence of best practice. The properties of materials used to manage vital pulps and the best way to restore the teeth will be reviewed and guidance on the full management of vital teeth will be suggested.ConclusionsPromoting new treatment modalities for reversible and irreversible pulpitis allowing for pulp preservation should be considered. Although debatable, cases with deep caries should be managed by complete non-selective caries removal which will allow for pulpal management if needed and a more predictable outcome can be expected when using the new materials and treatment modalities of vital pulp therapy.
Collapse
|
13
|
The Cytotoxicity and Genotoxicity of Bioactive Dental Materials. Cells 2022; 11:cells11203238. [PMID: 36291107 PMCID: PMC9600439 DOI: 10.3390/cells11203238] [Citation(s) in RCA: 7] [Impact Index Per Article: 3.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/13/2022] [Revised: 10/01/2022] [Accepted: 10/12/2022] [Indexed: 12/31/2022] Open
Abstract
The promotion of biologically based treatment strategies in restorative dentistry is of paramount importance, as invasive treatments should be avoided to maintain the tooth's vitality. This study aimed to assess the biocompatibility of commercially available bioactive materials that can be used for dental pulp capping. The study was performed with a monocyte/macrophage peripheral blood SC cell line (ATCC CRL-9855) on the following six specific bioactive materials: ProRoot MTA (Dentsply Sirona), MTA Angelus (Angelus), Biodentine (Septodont), TheraCal LC (Bisco), ACTIVA BioACTIVE (Pulpdent) and Predicta Bioactive Bulk (Parkell). The cytotoxicity of the investigated agents was measured using a resazurin-based cell viability assay, while the genotoxicity was evaluated using an alkaline comet assay. Additionally, flow cytometry (FC) apoptosis detection was conducted with a FITC (fluorescein isothiocyanate) Annexin V Apoptosis Detection Kit I. FC cell-cycle arrest assessment was carried out with propidium iodide staining. The results of this study showed no significant cytotoxicity and genotoxicity (p > 0.05) in ProRoot MTA, MTA Angelus, Biodentine, ACTIVA BioACTIVE and Predicta Bioactive. Conversely, TheraCal LC presented a significant decrease (p < 0.001). In conclusion, due to excellent biocompatibility and low cytotoxicity, MTA, Biodentine, ACTIVA BioACTIVE and Predicta Bioactive may be suitable for pulp capping treatments. On the other hand, due to the high cytotoxicity of TheraCal LC, its use should be avoided in vital pulp therapies.
Collapse
|
14
|
Influence of Acidic Environmental Conditions on Push-Out Bonding Strength of Four Calcium Silicate-Based Materials to Root Dentin. Int J Dent 2022; 2022:9169221. [PMID: 36249725 PMCID: PMC9553478 DOI: 10.1155/2022/9169221] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/09/2022] [Revised: 08/27/2022] [Accepted: 09/08/2022] [Indexed: 11/17/2022] Open
Abstract
Introduction. Calcium silicate-based cements (CSCs) are frequently used in various endodontic procedures such as perforation repair, vital pulp therapy, regenerative treatments, or apexification. One of their areas of use, treatment of perforations, can be challenging in clinical practice. Selection of stable, durable, and compatible material with structural and biological alterations is a must in such situations. Aim. This study aimed to compare the dislocation resistance of various calcium-silicate-containing materials used in endodontic treatment exposed to various environmental conditions in a push-out study model. Methods. Selected ninety-six human mandibular premolars with single root canals were cut from the middle portion to obtain dentin slices of 2 mm thickness (n = 192). Then, the canal lumen was enlarged by using #4Gates-Glidden drills. Specimens for each repair material (MTA, Angelus, Endosequence RRM (ERRM), Biodentine, BioMTA) were placed in shaped lumens, wrapped in pieces of gauze, and randomly divided into four groups (n = 48) according to the storage time and media: group A: 4 days in phosphate-buffered saline (PBS), group B: 4 days in acetic acid (pH = 4.4), group C: 34 days in PBS, and group D: 4 days in acetic acid (pH = 4.4) followed by exposure to PBS for 30 days. A universal testing machine measured the dislodgement resistance followed by scanning electron microscopy imaging to evaluate the material-dentin interface. Results. ERRM showed the highest dislocation resistance in all test groups (
). The greatest bonding strength was observed (13,54 ± 5,56 MPa) after exposure to 34 days in PBS (pH = 7.2). The values for ERRM decreased in contact with acetic acid (pH = 4.4) and increased when placed in PBS (
). Conclusion. All repair materials showed a higher dislocation resistance when stored in PBS regardless of storage time. However, the improved pH of the surrounding media was not successful in reversing the deteriorating effect caused by lower pH in relation to dislocation resistance in all tested materials except for ERRM.
Collapse
|
15
|
MUTLUAY AT. Does adding accelerators to Mineral Trioxide Aggregate affect the shear bond strength? SELCUK DENTAL JOURNAL 2022; 9:501-508. [DOI: 10.15311/selcukdentj.973299] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 09/01/2023]
Abstract
Amaç: Bu çalışmada, farklı hızlandırıcı ilave edilen Mineral Trioksit Agregat’ın (MTA) kompozite farklı sertleşme sürelerinde makaslama bağlanma dayanımının (MBD) değerlendirilmesi amaçlanmıştır.
Gereç ve Yöntemler: Merkezi boşluklara sahip 120 adet akrilik blok 4 ana gruba ayrıldı. 1. grup (kontrol); sadece MTA, 2, 3 ve 4. grup ise sırasıyla %10 kalsiyum klorür (CaCl2), %23,1 kalsiyum laktat glokonat (CLG) ve %15 disodyum hidrojen fosfat (Na2HPO4) ile karıştırılmış MTA içermektedir. Her grup 2 saat 45 dakika , 24 saat ve 96 saat sertleşme süresine göre 3 alt gruba ayrıldı. Bekleme süreleri tamamlandıktan sonra adeziv sistem (Clearfil SE Bond, Kuraray) ve kompozit rezin (Clearfil Majesty, Kuraray) işlemleri tamamlanan örneklere evrensel test cihazında MBD testi uygulandı. Elde edilen verilerinin karşılaştırmasında, tek yönlü varyans analizi (ANOVA) ve Tukey HSD testleri kullanıldı.
Bulgular: Hızlandırıcısız MTA en yüksek ortalama MBD değeri sergiledi. Hızlandırıcısız MTA, hızlandırıcı olarak CLG ve Na2HPO4 eklenen MTA ile kıyaslandığında aralarındaki fark anlamlı bulundu (p<0.0001). Başlangıç sertleşme süresinde alt gruplar arasında istatistiksel olarak anlamlı farklılık gözlenmedi (p>0,05), diğer sertleşme sürelerinde fark anlamlı bulundu (p<0,05). MTA’ya hızlandırıcı olarak CLG ve Na2HPO4 ilavesinin tüm sürelerde MBD değerlerini azalttığı, CaCl2 ilavesinin ise 96 saatin ardından MBD değerini anlamlı olarak yükselttiği gözlendi.
Sonuç: MTA içerisine hızlandırıcı eklemek MBD değerini düşürmektedir. Ancak MTA’ya hızlandırıcı olarak %10 CaCl2 eklemek 96 saatin ardından yapılacak restoratif işlemlerde pozitif bağlantı sonuçları ortaya çıkarabilir.
Collapse
|
16
|
Evaluation of the Shear Bond Strength of Four Bioceramic Materials with Different Restorative Materials and Timings. MATERIALS 2022; 15:ma15134668. [PMID: 35806792 PMCID: PMC9267194 DOI: 10.3390/ma15134668] [Citation(s) in RCA: 7] [Impact Index Per Article: 3.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 05/04/2022] [Revised: 06/29/2022] [Accepted: 06/30/2022] [Indexed: 02/05/2023]
Abstract
The objectives of this study were to evaluate the shear bond strength (SBS) of a resin composite (RC) and a resin-modified glass ionomer (RMGI) to four different bioceramic materials and to compare the effects of the immediate vs. delayed placement of restoration on the SBS. A total of 160 Teflon blocks and 40 blocks/material, were randomly filled with one of the bioceramic materials (NeoPUTTY®, NeoMTA2®, TotalFill® BC RRM™ Fast Set Putty, and ProRoot® MTA). The restoration was performed immediately or in a delayed time frame (after 7 days) using a Filtek™ Z350 XT Flowable composite (bonded to the bioceramic materials using Single bond universal 3M) or GC Fuji II LC® RMGI. The SBS test was performed at a crosshead speed of 1 mm/min, and the failure mode was evaluated under a digital microscope by one blinded examiner. One-way analysis of variance (ANOVA) with the Games–Howell post hoc test was used to compare the mean SBS between the groups. The mean SBS of the bioceramic materials to RC was significantly higher than to RMGI except for ProRoot MTA (p-value 0.65). The SBS values to RC were as follows: ProRoot MTA (7.64 MPa); NeoMTA2 (8.57 MPa) which was significantly higher than both NeoPUTTY (4.04 MPa) and TotalFill® BC RRM™ Fast Set Putty (4.38 MPa). For RMGI groups, ProRoot MTA showed the highest SBS (7.18 MPa), followed by NeoMTA2 (4.15 MPa), NeoPUTTY (1.62 MPa), and TotalFill® BC RRM™ Fast Set Putty (1.54 MPa). The delayed timing restoration showed a significantly higher SBS than the immediate, except for the immediate RMGI restoration with MTA. To conclude, the SBS of RC to the bioceramic materials was significantly higher than RMGI, except for ProRoot MTA. Both restorative materials had a significantly higher SBS to the MTA groups in comparison to premixed bioceramics. Delayed RC restoration had a higher SBS than immediate restoration. Similarly, delayed RMGI restoration had a higher SBS than immediate restoration with premixed bioceramic but not with MTA.
Collapse
|
17
|
Long-term outcome of nonvital immature permanent teeth treated with apexification and corono-radicular adhesive restoration - a case series. J Endod 2022; 48:1191-1199. [PMID: 35750220 DOI: 10.1016/j.joen.2022.06.007] [Citation(s) in RCA: 13] [Impact Index Per Article: 6.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/07/2022] [Revised: 06/03/2022] [Accepted: 06/14/2022] [Indexed: 12/26/2022]
Abstract
INTRODUCTION This study aims to evaluate the long-term outcome of sixteen permanent maxillary central incisors with nonvital pulps and open apices treated with apexification and corono-radicular adhesive restorations, within a follow-up span of 5 to 22 years. METHODS Fourteen patients providing a total of sixteen teeth treated with MTA (n = 12), Biodentine (n = 3) or β-tricalcium phosphate (n = 1) apical barrier and corono-radicular restoration, with or without fiberglass post, were included. Clinical and radiographic criteria were defined for assessment at recall. Restoration and periapical tissues' status evaluation were performed according to FDI World Dental Federation's esthetic, functional and biological criteria and Ørstavik Periapical Index (PAI). Outcome was dichotomized in "healed" (PAI ≤ 2, asymptomatic with absence of signs of infection) or "not healed" (PAI ≥ 3, presence of clinical signs and/or symptoms). RESULTS Fourteen out of twenty-four patients were available for the present study (recall rate = 58%). Within a follow-up of 5 to 22 years, ten (62.5%) teeth were considered "healed", fulfilling both strict clinical and radiographic success criteria. Only one tooth was missing due to root resorption and one patient was presenting with clinical signs and symptoms at recall, resulting in a survival rate of 93.8%. CONCLUSIONS Adhesive corono-radicular restoration in nonvital permanent immature teeth treated with apexification allows for favorable long-term outcomes, by ensuring structural reinforcement and coronal microleakage prevention. Teeth sustaining a substantial loss of coronal structure may require post/core placement. In the case of failure, this endodontic-restorative combination assured teeth survival until growth phase conclusion, thus allowing for proper prosthetic rehabilitation approaches.
Collapse
|
18
|
Bond Strength of Adhesive Systems to Calcium Silicate-Based Materials: A Systematic Review and Meta-Analysis of In Vitro Studies. Gels 2022; 8:gels8050311. [PMID: 35621609 PMCID: PMC9141246 DOI: 10.3390/gels8050311] [Citation(s) in RCA: 8] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/20/2022] [Revised: 05/08/2022] [Accepted: 05/16/2022] [Indexed: 12/16/2022] Open
Abstract
Since the adhesion of resin composites to calcium silicate-based cement is considered challenging. Therefore, the best adhesion strategy should be indicated. This review aimed to assess the effect of different adhesive systems on the bond strength of resin composite to calcium silicate-based cement through a systematic review and meta-analysis. The subsequent PICOS framework used was: population, calcium silicate-based cement; intervention, use of self-etch adhesive systems; control, use of total-etch adhesive systems; outcome, bond strength; study design, in vitro studies. The literature search was conducted independently by two reviewers up to 18 February 2021. Electronic databases (PubMed, ISI Web of Science, SciELO, Scopus, and Embase) were searched for applicable articles. In vitro manuscripts studying the effect of adhesive systems on the bond strength of calcium silicate-based cement were considered. The meta-analyses were performed using Review Manager Software version 5.3.5 (The Nordic Cochrane Centre, The Cochrane Collaboration, Copenhagen, Denmark). Bond strength comparisons were made considering the type of calcium silicate-based cement (Mineral Trioxide Aggregate (MTA), Biodentine™, or TheraCal LC®). A p-value < 0.05 was considered statistically significant. A total of 7321 studies were retrieved in databases searched. After full-text evaluation, 37 eligible papers were assessed for qualitative analysis, leaving a total of 22 papers for the quantitative analysis. According to the meta-analysis, the bond strength values of resin composite materials to MTA and TheraCal LC® cement were favored when a total-etch adhesive system was used (p ≤ 0.02). On the other hand, the meta-analysis of the bond strength of resin-based materials to Biodentine™ calcium silicate-based cement was similar between both approaches (p = 0.12). The in vitro evidence suggests that the bond strength of resin-based materials to both MTA and TheraCal LC® cement was preferred by using the total-etch adhesive strategy. However, when bonding to Biodentine™, the use of self-etch or total-etch strategies displayed promising results. Given the lack of evidence related to the chemical interaction of self-etch adhesive materials with the bioceramics, if self-etch adhesives are used for bonding resin-based restorations to calcium silicate-based cement, a pretreatment with phosphoric acid could be recommended.
Collapse
|
19
|
Trivedi S, Hiremath H, Solanki A, Verma D. Evaluation of shear bond strength of e-mineral trioxide aggregate and biodentine with glass ionomer cement: An in vitro study. ENDODONTOLOGY 2022. [DOI: 10.4103/endo.endo_17_22] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/04/2022] Open
|
20
|
Dumrongvute K, Adel S, Wada T, Kawashima N, Piyachon C, Watanabe H, Kurabayashi T, Okiji T, Uo M. Distrontium Cerate as a Radiopaque Component of Hydraulic Endodontic Cement. MATERIALS (BASEL, SWITZERLAND) 2021; 15:284. [PMID: 35009428 PMCID: PMC8746137 DOI: 10.3390/ma15010284] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 11/26/2021] [Revised: 12/24/2021] [Accepted: 12/28/2021] [Indexed: 11/17/2022]
Abstract
This study aimed to synthesize distrontium cerate (2SrO·CeO2: S2Ce) and evaluate its properties as an alternative component of the endodontic cement. S2Ce cement was prepared through calcination of strontium hydroxide and cerium carbonate. Subsequently, the crystal phase was confirmed using X-ray diffraction. S2Ce cement exhibited a rapid setting time (121 min) and achieved a high compressive strength (72.1 MPa) at 1 d after mixing, comparable to the compressive strength of a commercial mineral trioxide aggregate (MTA) cement (ProRoot MTA) after 28 d post mixing. However, the compressive strength decreased after 28 d of storage when the W/P ratio was 0.30-0.40 (p < 0.05). Ion dissolution test of the S2Ce cement showed that strontium ions were released after immersion in water (5.27 mg/mL after 1 d), whereas cerium dissolution was not detected. S2Ce exhibited approximately three times higher radiopacity (9.0 mm aluminum thickness equivalent) compared to the commercial MTA (p < 0.05). These findings suggest that S2Ce is a possible component for hydraulic endodontic cement that demonstrates a rapid setting and high radiopacity.
Collapse
Affiliation(s)
- Kunlanun Dumrongvute
- Department of Pulp Biology and Endodontics, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan; (K.D.); (S.A.); (N.K.); (T.O.)
- Department of Conservative Dentistry and Prosthetics, Faculty of Dentistry, Srinakharinwirot University, 114 Sukhumvit 23, Wattana, Bangkok 10110, Thailand;
| | - Sherif Adel
- Department of Pulp Biology and Endodontics, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan; (K.D.); (S.A.); (N.K.); (T.O.)
- National Research Centre of Egypt, Department of Restorative Dentistry and Dental Materials, Oral and Dental Research Division, El Buhouth Street, Dokki, Cairo 12622, Egypt
| | - Takahiro Wada
- Department of Advanced Biomaterials, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan;
| | - Nobuyuki Kawashima
- Department of Pulp Biology and Endodontics, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan; (K.D.); (S.A.); (N.K.); (T.O.)
| | - Chinalai Piyachon
- Department of Conservative Dentistry and Prosthetics, Faculty of Dentistry, Srinakharinwirot University, 114 Sukhumvit 23, Wattana, Bangkok 10110, Thailand;
| | - Hiroshi Watanabe
- Department of Oral and Maxillofacial Radiology, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan; (H.W.); (T.K.)
| | - Tohru Kurabayashi
- Department of Oral and Maxillofacial Radiology, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan; (H.W.); (T.K.)
| | - Takashi Okiji
- Department of Pulp Biology and Endodontics, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan; (K.D.); (S.A.); (N.K.); (T.O.)
| | - Motohiro Uo
- Department of Advanced Biomaterials, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University, 1-5-45 Yushima, Bunkyo-ku, Tokyo 113-8549, Japan;
| |
Collapse
|
21
|
Unpredictable Outcomes of a Regenerative Endodontic Treatment. Case Rep Dent 2021; 2021:2478310. [PMID: 34659840 PMCID: PMC8514905 DOI: 10.1155/2021/2478310] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/17/2021] [Revised: 09/20/2021] [Accepted: 09/24/2021] [Indexed: 11/18/2022] Open
Abstract
Regenerative endodontic treatment (RET) is a valuable treatment for necrotic immature teeth with many advantages such as increasing root length and thickness of root wall. The success of RETs is based on healthy stem cells, suitable scaffolds, and growth factors and takes place when bacterial contamination is well controlled. The aim of this article is to address controversy in a case with multiple success criteria. This paper reports a 9-year-old boy with a complicated crown fracture of the maxillary left central incisor about three years prior to referral with a diagnosis of intrusive luxation with spontaneous reeruption. The tooth had an underdeveloped root and a well-defined periapical radiolucent lesion around the root apex. RET was considered according to the stage of root development. Upon the three-week recall session, the clinical examination indicated that the patient was asymptomatic in the affected site. However, the patient returned two weeks later with a sinus tract pertaining to the apex of tooth #9. Therefore, debridement of the root canal space was repeated and the RET redone. On the second trial, the patient was symptom-free, but no more evidence of root maturation was observed on 18-month follow-up. The tooth was asymptomatic (without swelling, drainage, and pain) during this time, and esthetics was provided for the patient.
Collapse
|
22
|
Evaluation of the Interfaces between Restorative and Regenerative Biomaterials Used in Vital Pulp Therapy. MATERIALS 2021; 14:ma14175055. [PMID: 34501145 PMCID: PMC8434275 DOI: 10.3390/ma14175055] [Citation(s) in RCA: 6] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 07/13/2021] [Revised: 08/21/2021] [Accepted: 08/27/2021] [Indexed: 12/15/2022]
Abstract
BACKGROUND Calcium-silicate-based cements (CSC) have gained an increasing scientific and clinical relevance, enabling more conservative approaches, namely pulp preservation and regeneration therapies. This research aims to study the influence of four clinical variables on the interfaces between CSC and composite adhesive restoration, concerning shear bond strength (SBS) and ultra-morphological patterns. METHODS SBS tests were performed in 320 specimens divided in 16 groups (n = 20) according to: two CSC (NuSmile® NeoMTA, BiodentineTM); two adhesive systems (ClearfilTM SE Bond 2 (CSEB2), ClearfilTM Universal Bond Quick (CUBQ)); optional application of an additional hydrophobic bonding layer (HBL); two restoration times (immediate, seven days). Scanning electron microscopy (SEM) was performed to conduct the ultra-morphology interface analysis in 32 deciduous molars prepared and randomly allocated into the 16 groups. RESULTS Globally, SBS tests showed higher bond strength of CUBQ compared to CSEB2 (p < 0.001), as with an additional HBL application (p = 0.014) and delayed restoration (p < 0.001). SEM showed the interpenetration between adhesive systems and CSC forming a hybrid layer, whose depth and thickness depended on the restoration time and adhesive strategy. CONCLUSIONS The independent clinical variables adhesive system, application of an additional HBL and restoration time affected the bond performance and ultra-morphological interface between composite adhesive restoration and CSC.
Collapse
|
23
|
Guagnano R, Romano F, Defabianis P. Evaluation of Biodentine in Pulpotomies of Primary Teeth with Different Stages of Root Resorption Using a Novel Composite Outcome Score. MATERIALS 2021; 14:ma14092179. [PMID: 33923152 PMCID: PMC8123062 DOI: 10.3390/ma14092179] [Citation(s) in RCA: 4] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 03/23/2021] [Revised: 04/16/2021] [Accepted: 04/22/2021] [Indexed: 12/20/2022]
Abstract
This study aimed to assess the success of pulpotomy in primary molars using Biodentine, new-developed tri-calcium, di-calcium-based silicate cement, at 6 and 12 months. The hypothesis was that stages of root resorption could influence the treatment success. A novel composite score was used based on five clinical and radiographic outcomes: soft-tissue pathology, pain to percussion, pathologic mobility, radiolucency and pathologic root resorption. Patients’ compliance and intraoperative pain experience were recorded using the Frankl scale and the Wong–Baker scale. A total of 22 primary molars, 9 in stage S (stability) and 13 in stage R (resorption) were submitted to pulpotomy using Biodentine and restored with composite resin. The success rate was 92.3% in the R group compared to 100% in the S group at both 6 and 12 months (p = 0.850). There was no statistically significant effect of type of molar, tooth position and type of carious lesions on the composite outcome (all p > 0.05). Overall, 73% of the children experienced no or mild/moderate pain and 77% had a cooperative attitude. Children younger than 7 years old experienced more pain (p = 0.04). Biodentine is a promising biomaterial for pulpotomy of primary teeth regardless of the stage of root resorption.
Collapse
Affiliation(s)
- Rosa Guagnano
- Department of Surgical Sciences, C.I.R. Dental School, Section of Pediatric Dentistry, University of Turin, 10126 Turin, Italy;
| | - Federica Romano
- Department of Surgical Sciences, C.I.R. Dental School, Section of Periodontology, University of Turin, 10126 Turin, Italy;
| | - Patrizia Defabianis
- Department of Surgical Sciences, C.I.R. Dental School, Section of Pediatric Dentistry, University of Turin, 10126 Turin, Italy;
- Correspondence:
| |
Collapse
|
24
|
Arandi NZ, Thabet M. Minimal Intervention in Dentistry: A Literature Review on Biodentine as a Bioactive Pulp Capping Material. BIOMED RESEARCH INTERNATIONAL 2021; 2021:5569313. [PMID: 33884264 PMCID: PMC8041541 DOI: 10.1155/2021/5569313] [Citation(s) in RCA: 12] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 01/09/2021] [Revised: 03/03/2021] [Accepted: 03/27/2021] [Indexed: 11/18/2022]
Abstract
Root canal treatment has been the treatment of choice for carious pulp exposures. In the perspective of minimally invasive dentistry and preventive endodontics, a direct pulp capping procedure with a reliable bioactive material may be considered an alternative approach provided that the pulp status is favorable. However, the treatment of pulp exposure by pulp capping is still a controversial issue with no clear literature available on this topic, leaving the concerned practitioner more confused than satisfied. Biodentine is a relatively new bioactive material explored for vital pulp therapy procedures. This article discusses its role in direct pulp capping procedures. A thorough literature search of the database was done using PubMed, Google Scholar, and Scopus using the keywords preventive endodontics, calcium silicate cement, direct pulp capping, Biodentine, and vital pulp therapy. Reference mining of the articles that were identified was used to locate other papers and enrich the findings. No limits were imposed on the year of publication, but only articles in English were considered. This paper is aimed at reviewing the current literature on Biodentine as a direct pulp capping material. The review will provide a better understanding of Biodentine's properties and can aid in the decision-making process for maintaining the vitality of exposed dental pulp with minimal intervention.
Collapse
Affiliation(s)
- Naji Ziad Arandi
- Department of Conservative Dentistry and Prosthodontics, Arab American University, Jenin, State of Palestine
| | - Mohammad Thabet
- Department of Orthodontics and Pediatric Dentistry, Arab American University, Jenin, State of Palestine
| |
Collapse
|
25
|
Detection of Inflammatory and Homeostasis Biomarkers after Selective Removal of Carious Dentin-An In Vivo Feasibility Study. J Clin Med 2021; 10:jcm10051003. [PMID: 33801317 PMCID: PMC7958315 DOI: 10.3390/jcm10051003] [Citation(s) in RCA: 3] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/02/2021] [Revised: 02/20/2021] [Accepted: 02/23/2021] [Indexed: 11/20/2022] Open
Abstract
Deep carious dentin lesions induce an immune reaction within the pulp-dentin complex, leading to the release of cytokines, which might be suitable biomarkers in pulp diagnostics. This in vivo feasibility study determines the concentration of different cytokines after selective removal of carious infected dentin (SCR). In our methodology, paired samples are obtained from 21 patients—each of them with two deep carious lesions at posterior teeth without clinical symptoms. After SCR, lesions are randomly assigned to treatment strategy: Group 1 (11 patients): Carious dentin is covered either with BiodentineTM (n = 11) or gutta-percha (n = 11) before using the adhesive OptibondTM FL. Group 2 (10 patients): The adhesives ClearfilTM SE Protect Bond (n = 10) or ClearfilTM SE Bond 2 (n = 10) are directly applied. Prepared cavities are rinsed with phosphate buffered saline containing 0.05% Tween 20 (10X) for five minutes immediately after SCR (visit 1) and eight weeks later (visit 2). Rinsing liquid is regained. Concentrations of IL-1β, IL-6, IL-10, C-reactive protein (CRP), TNF-α, IFN-γ, TIMP-1, -2, and MMP-7, -8, -9 are assessed by customized multiplex assays, evaluated with fluorescence analyzer. Non-parametric statistical analysis (Wilcoxon, Mann–Whitney U Test, p < 0.05) is performed (SPSS 25). Our results show that concentrations of CRP, IL-1β, IL-6, TIMP-1, -2, and MMPs were detectable. Median concentrations of CRP, IL-1β und IL-6 were significantly higher in visit 1 (304.9, 107.4, 3.8 pg/mL), compared to visit 2 (67.8, 2.3, 0.0 pg/mL; pi < 0.001). The study revealed that the non-invasive determination of cytokines from prepared dental cavities is possible.
Collapse
|
26
|
Different Approaches to the Regeneration of Dental Tissues in Regenerative Endodontics. APPLIED SCIENCES-BASEL 2021. [DOI: 10.3390/app11041699] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 12/17/2022]
Abstract
(1) Background: The regenerative procedure has established a new approach to root canal therapy, to preserve the vital pulp of the tooth. This present review aimed to describe and sum up the different approaches to regenerative endodontic treatment conducted in the last 10 years; (2) Methods: A literature search was performed in the PubMed and Cochrane Library electronic databases, supplemented by a manual search. The search strategy included the following terms: “regenerative endodontic protocol”, “regenerative endodontic treatment”, and “regenerative endodontics” combined with “pulp revascularization”. Only studies on humans, published in the last 10 years and written in English were included; (3) Results: Three hundred and eighty-six potentially significant articles were identified. After exclusion of duplicates, and meticulous analysis, 36 case reports were selected; (4) Conclusions: The pulp revascularization procedure may bring a favorable outcome, however, the prognosis of regenerative endodontics (RET) is unpredictable. Permanent immature teeth showed greater potential for positive outcomes after the regenerative procedure. Further controlled clinical studies are required to fully understand the process of the dentin–pulp complex regeneration, and the predictability of the procedure.
Collapse
|
27
|
Pradelle-Plasse N, Mocquot C, Semennikova K, Colon P, Grosgogeat B. Interface between calcium silicate cement and adhesive systems according to adhesive families and cement maturation. Restor Dent Endod 2020; 46:e3. [PMID: 33680892 PMCID: PMC7906853 DOI: 10.5395/rde.2021.46.e3] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/23/2020] [Revised: 06/25/2020] [Accepted: 06/29/2020] [Indexed: 12/03/2022] Open
Abstract
Objectives This study aimed to evaluate the interface between a calcium silicate cement (CSC), Biodentine and dental adhesives in terms of sealing ability. Materials and Methods Microleakage test: 160 standardized class II cavities were prepared on 80 extracted human molars. The cavities were filled with Biodentine and then divided into 2 experimental groups according to the time of restoration: composite resin obturation 15 minutes after Biodentine handling (D0); restoration after 7 days (D7). Each group was then divided into 8 subgroups (n = 5) according to the adhesive system used: etch-and-rinse adhesive (Prime & Bond); self-etch adhesive 2 steps (Optibond XTR and Clearfil SE Bond); self-etch adhesive 1 step (Xeno III, G-aenial Bond, and Clearfil Tri-S Bond); and universal used as etch-and-rinse or self-etch (ScotchBond Universal ER or SE). After thermocycling, the teeth were immersed in a silver nitrate solution, stained, longitudinally sectioned, and the Biodentine/adhesive percolation was quantified. Scanning electron microscopic observations: Biodentine/adhesive interfaces were observed. Results A tendency towards less microleakage was observed when Biodentine was etched (2.47%) and when restorations were done without delay (D0: 4.31%, D7: 6.78%), but this was not significant. The adhesives containing 10-methacryloyloxydecyl dihydrogen phosphate monomer showed the most stable results at both times studied. All Biodentine/adhesive interfaces were homogeneous and regular. Conclusions The good sealing of the CSC/adhesive interface is not a function of the system adhesive family used or the cement maturation before restoration. Biodentine can be used as a dentine substitute.
Collapse
Affiliation(s)
- Nelly Pradelle-Plasse
- Department of Conservative Dentistry - Endodontics, Faculty of Dental Surgery, University of Paris, Paris, France.,Rothschild Hospital, Assistance Publique Hôpitaux de Paris, Paris, France.,Multimaterials and Interfaces Laboratory (UMR 5615), Biomaterials Team, Villeurbanne, France
| | - Caroline Mocquot
- Department of Conservative Dentistry - Endodontics, Faculty of Dental Surgery, University of Paris, Paris, France.,Rothschild Hospital, Assistance Publique Hôpitaux de Paris, Paris, France.,Multimaterials and Interfaces Laboratory (UMR 5615), Biomaterials Team, Villeurbanne, France
| | - Katherine Semennikova
- Department of Conservative Dentistry - Endodontics, Faculty of Dental Surgery, University of Paris, Paris, France.,Rothschild Hospital, Assistance Publique Hôpitaux de Paris, Paris, France.,Multimaterials and Interfaces Laboratory (UMR 5615), Biomaterials Team, Villeurbanne, France
| | - Pierre Colon
- Department of Conservative Dentistry - Endodontics, Faculty of Dental Surgery, University of Paris, Paris, France.,Rothschild Hospital, Assistance Publique Hôpitaux de Paris, Paris, France.,Multimaterials and Interfaces Laboratory (UMR 5615), Biomaterials Team, Villeurbanne, France
| | - Brigitte Grosgogeat
- Multimaterials and Interfaces Laboratory (UMR 5615), Biomaterials Team, Villeurbanne, France.,Department of Biomaterials, Faculty of Dental Surgery, University of Lyon 1, Lyon, France.,Hospices Civils de Lyon, Lyon, France
| |
Collapse
|
28
|
Salerno M, Vizza F, Amaroli A, Signore A, Itri A. 3D optical profilometer analysis of the marginal gap of Class II restorations made with different materials for vital pulp therapy procedures. Dent Mater J 2020; 40:407-415. [PMID: 33208576 DOI: 10.4012/dmj.2020-066] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/23/2022]
Abstract
We considered Class II dental cavities in critical tooth areas concerned with vital pulp therapy, and evaluated the marginal gap after treatment with Biodentine and Geristore, and one composite after either etching and adhesive (V2) and after use of a self-etching system (iBond Universal). We measured the surface morphology at the marginal gap by optical profilometry, and carried out analysis of the 3D data according to a new effective definition of marginal gap. The defined quantity was assessed for statistical significance of the apparent differences. The largest gaps appeared for Geristore (first) and Biodentine (not significantly lower), whereas the gaps of the composite controls were both lower, the lowest being the two-step self-etched system with respect to the three-steps etched and adhesive system, yet without statistical significance. Obviously, there is still room for improvement of the vital pulp therapy restorative materials, as compared to the use of standard composite systems.
Collapse
Affiliation(s)
- Marco Salerno
- Istituto Italiano di Tecnologia, Materials Characterization Facility.,Ronin Institute
| | - Francesca Vizza
- Department of Therapeutic Dentistry, I. M. Sechenov First Moscow State Medical University
| | - Andrea Amaroli
- Department of Orthopaedic Dentistry, I. M. Sechenov First Moscow State Medical University.,Department of Surgical Sciences and Integrated Diagnostic, University of Genoa
| | - Antonio Signore
- Department of Therapeutic Dentistry, I. M. Sechenov First Moscow State Medical University
| | - Angelo Itri
- Department of Therapeutic Dentistry, I. M. Sechenov First Moscow State Medical University
| |
Collapse
|
29
|
The Effect of Biodentine Maturation Time on Resin Bond Strength When Aged in Artificial Saliva. Int J Dent 2020; 2020:8831813. [PMID: 33144858 PMCID: PMC7599420 DOI: 10.1155/2020/8831813] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/22/2020] [Revised: 09/25/2020] [Accepted: 10/06/2020] [Indexed: 12/16/2022] Open
Abstract
Biodentine is a calcium silicate cement (CSC) that has been broadly applied in vital pulp therapy. The quality of the Biodentine-composite bond has a significant effect on the longevity of the definitive restoration. The aim of this study is to investigate the shear bond strength (SBS) between Biodentine and composite restoration at different maturation times of Biodentine aged in artificial saliva. Fifteen Biodentine discs were allocated into three groups (n = 5) based on the timeframe of performance of composite restoration: immediate (after 12 min), after 14 days, and after 28 days of Biodentine maturation. Total etch and rinse adhesive system and bulk-fill regular resin composite were used. The shear bond strength and the failure pattern were assessed. One-way ANOVA with the Bonferroni post hoc test was applied for statistical analysis at p < 0.05. The highest (32.47 ± 8.18 MPa) and the lowest (4.08 ± 0.81 MPa) SBS values were recorded for 14 days and 12 min groups, respectively. Significant statistical differences were reported among the groups, and a high statistically significant difference was found between the immediate group and the other groups. Adhesive failure patterns were evident in all groups. More clinically acceptable bond strength between the Biodentine and overlaid composite restoration is at 14 days after Biodentine maturation. Delaying the coverage of Biodentine later than 14 days may significantly reduce the SBS. Using the artificial saliva as an aging medium may affect the SBS between Biodentine and composite material.
Collapse
|
30
|
Palma PJ, Marques JA, Antunes M, Falacho RI, Sequeira D, Roseiro L, Santos JM, Ramos JC. Effect of restorative timing on shear bond strength of composite resin/calcium silicate-based cements adhesive interfaces. Clin Oral Investig 2020; 25:3131-3139. [PMID: 33047203 DOI: 10.1007/s00784-020-03640-7] [Citation(s) in RCA: 28] [Impact Index Per Article: 7.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/27/2020] [Accepted: 10/07/2020] [Indexed: 12/21/2022]
Abstract
OBJECTIVES The aim of this study was to evaluate the shear bond strength inherent to immediate and delayed definitive composite resin restorations, over three different biomaterials. METHODS Fifty-four aluminum blocks were randomly assigned to six experimental groups (n = 9) according to the biomaterial (Biodentine, TotalFill BC Putty, or PCM) and restoration timing (immediate or 7 days delayed). Regarding the restorative procedures, a two-step self-etch bonding system (Clearfil SE Bond) was applied and subsequently restored using a flowable composite resin (SDR). After shear bond strength testing, fracture pattern analysis was performed. The significance level was set at α = 0.05. RESULTS Within the immediate groups, Biodentine showed the highest mean shear bond strength value, with no statistically significant differences (P > 0.05) being detected when compared with both TotalFill (P = 0.072) and PCM (P = 0.232) groups. Regarding the delayed restoration groups, Biodentine and TotalFill presented the highest mean shear bond strength value, with statistical differences when compared with PCM (P = 0.002 and P = 0.043, respectively). No statistically significant differences (P > 0.05) were verified between both immediate and delayed groups for each tested biomaterial. Also, a statistically significant association was found between the fracture type and the biomaterial (P < 0.001). CONCLUSIONS AND CLINICAL RELEVANCE Our findings suggest that all tested biomaterials present suitable alternatives which allow to perform restorative procedures immediately after pulp capping biomaterial placement (3 or 12 min, depending on the bioactive cement), therefore requiring one single appointment to complete the procedure. Biodentine and TotalFill BC Putty have shown superior shear bond strength results when compared with PCM, within a delayed timeframe (7 days).
Collapse
Affiliation(s)
- Paulo J Palma
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal. .,Center for Innovation and Research in Oral Sciences (CIROS), Faculty of Medicine, University of Coimbra, Coimbra, Portugal.
| | - Joana A Marques
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal
| | - Márcia Antunes
- Dentistry Department, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal
| | - Rui I Falacho
- Institute of Oral Implantology and Prosthodontics, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal
| | - Diana Sequeira
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal
| | - Luís Roseiro
- Department of Mechanical Engineering, Institute of Engineering of Coimbra, Polytechnic - ISEC, 3000, Coimbra, Portugal
| | - João Miguel Santos
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal.,Center for Innovation and Research in Oral Sciences (CIROS), Faculty of Medicine, University of Coimbra, Coimbra, Portugal
| | - João C Ramos
- Center for Innovation and Research in Oral Sciences (CIROS), Faculty of Medicine, University of Coimbra, Coimbra, Portugal.,Institute of Operative Dentistry, Faculty of Medicine, University of Coimbra, 3000-075, Coimbra, Portugal
| |
Collapse
|
31
|
Munoz-Sanchez ML, Linas N, Decerle N, Nicolas E, Hennequin M, Cousson PY. A Combination of Full Pulpotomy and Chairside CAD/CAM Endocrown to Treat Teeth with Deep Carious Lesions and Pulpitis in a Single Session: A Preliminary Study. INTERNATIONAL JOURNAL OF ENVIRONMENTAL RESEARCH AND PUBLIC HEALTH 2020; 17:ijerph17176340. [PMID: 32878168 PMCID: PMC7503687 DOI: 10.3390/ijerph17176340] [Citation(s) in RCA: 9] [Impact Index Per Article: 2.3] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 07/29/2020] [Revised: 08/26/2020] [Accepted: 08/27/2020] [Indexed: 12/17/2022]
Abstract
A higher chance of carrying out a successful full pulpotomy may depend on whether the coronal restoration can be completed within a single appointment. The development of chairside CAD/CAM (Computer Aided Design and Manufacturing) technology has made it possible to carry out indirect restoration of endodontically treated teeth in a single session. This study aimed to evaluate the long-term outcome of a full pulpotomy with Biodentine™ immediately covered with a chairside CAD/CAM endocrown on teeth affected by pulpitis and deep carious lesions. The investigation involved a cohort of 30 molars that were treated by pulpotomy and CAD/CAM endocrown. Clinical and radiological examinations were scheduled at 1, 6, and 12 months postoperatively. Overall, all treatments were effective at any time during the follow-up. The results of this study need to be confirmed with a longer-term follow-up to allow for comparison with the literature. This original combination of endodontic and restorative treatments provides an Endo-prosthetic continuum in a single session, with the objective of long-term success in terms of tooth health.
Collapse
Affiliation(s)
- Marie-Laure Munoz-Sanchez
- Centre de Recherche en Odontologie Clinique (CROC), Université Clermont Auvergne, F-63000 Clermont-Ferrand, France; (M.-L.M.-S.); (N.L.); (N.D.); (E.N.); (P.-Y.C.)
- CHU Clermont-Ferrand, Service d’Odontologie, F-63003 Clermont-Ferrand, France
| | - Natacha Linas
- Centre de Recherche en Odontologie Clinique (CROC), Université Clermont Auvergne, F-63000 Clermont-Ferrand, France; (M.-L.M.-S.); (N.L.); (N.D.); (E.N.); (P.-Y.C.)
- CHU Clermont-Ferrand, Service d’Odontologie, F-63003 Clermont-Ferrand, France
| | - Nicolas Decerle
- Centre de Recherche en Odontologie Clinique (CROC), Université Clermont Auvergne, F-63000 Clermont-Ferrand, France; (M.-L.M.-S.); (N.L.); (N.D.); (E.N.); (P.-Y.C.)
- CHU Clermont-Ferrand, Service d’Odontologie, F-63003 Clermont-Ferrand, France
| | - Emmanuel Nicolas
- Centre de Recherche en Odontologie Clinique (CROC), Université Clermont Auvergne, F-63000 Clermont-Ferrand, France; (M.-L.M.-S.); (N.L.); (N.D.); (E.N.); (P.-Y.C.)
- CHU Clermont-Ferrand, Service d’Odontologie, F-63003 Clermont-Ferrand, France
| | - Martine Hennequin
- Centre de Recherche en Odontologie Clinique (CROC), Université Clermont Auvergne, F-63000 Clermont-Ferrand, France; (M.-L.M.-S.); (N.L.); (N.D.); (E.N.); (P.-Y.C.)
- CHU Clermont-Ferrand, Service d’Odontologie, F-63003 Clermont-Ferrand, France
- Correspondence:
| | - Pierre-Yves Cousson
- Centre de Recherche en Odontologie Clinique (CROC), Université Clermont Auvergne, F-63000 Clermont-Ferrand, France; (M.-L.M.-S.); (N.L.); (N.D.); (E.N.); (P.-Y.C.)
- CHU Clermont-Ferrand, Service d’Odontologie, F-63003 Clermont-Ferrand, France
| |
Collapse
|
32
|
Tooth Discoloration after Regenerative Endodontic Procedures with Calcium Silicate-Based Cements—An Ex Vivo Study. APPLIED SCIENCES-BASEL 2020. [DOI: 10.3390/app10175793] [Citation(s) in RCA: 27] [Impact Index Per Article: 6.8] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 01/04/2023]
Abstract
The aim of the present ex vivo study was to assess and compare coronal discoloration induced by four endodontic biomaterials used in regenerative endodontic procedures (REPs). Root resection was executed horizontally, 2 mm apical to the cementoenamel junction, in all fifty-four teeth. After accessing the pulp chamber, specimens were randomly divided in groups and filled with either saline solution or blood, followed by calcium silicate-based cements (CSCs) placement: ProRoot mineral trioxide aggregate (MTA) (Dentsply Sirona), Biodentine (Septodont), TotalFill BC (FKG), or pulp capping material (PCM) (Coltène). Color change (ΔE) was assessed using the L* a* b* system at five different timepoints (before and immediately after biomaterial application, 72 h, 7 days, and 6 months). The significance level for statistical analysis was set at p < 0.05. There are statistically significant differences regarding ΔE over time (p < 0.001). Statistical differences are found considering material (p < 0.001), treatment (p = 0.007), or both (p = 0.002). If solely the material or treatment is considered, regardless of time, statistically significant differences are detected (p < 0.001). After a six-month period of evaluation, blood exposure might be a critical factor in biomaterials’ color variation. Biodentine presents the lowest discoloration potential, followed by TotalFill and PCM, albeit without statistically significant differences. MTA exhibited the greatest color variation. The selection of biomaterial should consider the material’s discoloration potential.
Collapse
|
33
|
Al-Sherbiny IM, Farid MH, Abu-Seida AM, Motawea IT, Bastawy HA. Chemico-physical and mechanical evaluation of three calcium silicate-based pulp capping materials. Saudi Dent J 2020; 33:207-214. [PMID: 34025083 PMCID: PMC8119770 DOI: 10.1016/j.sdentj.2020.02.001] [Citation(s) in RCA: 12] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/02/2019] [Revised: 02/04/2020] [Accepted: 02/10/2020] [Indexed: 02/05/2023] Open
Abstract
Aim This study compared biointeractivity (pH of soaking water and calcium ions), porosity, water sorption, solubility, compressive strength, lap shear strength, as well as the apatite forming ability of three calcium silicate-based capping materials: Mineral trioxide aggregate (MTA), Biodentine (BD) and Tech Biosealer capping (BS). Methods One hundred and five discs of the tested materials were prepared in compliance with the manufacturer's instructions. The materials' pastes were placed in Teflon molds and allowed to set before testing. The pH and Ca+2 ions were measured by a potentiometric method. Porosity, water sorption, and solubility were calculated through the measurement of initial mass, mass, saturated mass and dry mass. Apatite forming ability was measured by an Environmental Scanning Electron Microscope that was connected to a secondary electron detector for energy dispersive X-ray analysis. Meanwhile compressive strength was measured by a computer controlled universal testing machine. Lap shear strength was measured by computer software on the testing machine. All data were statistically analyzed. Results The tested materials showed Ca ions release and alkalization, which decreased with soaking time. The BD exhibited a very high Ca release at both short (3 h) and long times (28 days). Significant high values of open and apparent porosities, water sorption, and solubility were measured for BS, which was followed by the MTA then BD (P < .05). The BD had significant higher compressive and lap shear bond strength than the MTA and BS (P < .05). Conclusion MTA, BD and BS are biointeractive bioactive materials that possess the ability to release ions and form calcium phosphate deposits. Unlike BD, BS is incapable of alternating MTA in pulp capping due to its high porosities, water sorption and solubility, as well as poor compressive and lap shear bond strength.
Collapse
Affiliation(s)
- Inas M Al-Sherbiny
- Dental Biomaterials Department, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo, Egypt
| | - Mona H Farid
- Oral Biology Department, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo, Egypt
| | - Ashraf M Abu-Seida
- Department of Surgery, Anesthesiology & Radiology, Faculty of Veterinary Medicine, Cairo University, Giza, Egypt
| | - Inas T Motawea
- Dental Biomaterials Department, Faculty of Dental Medicine for Girls, Al-Azhar University, Cairo, Egypt
| | - Hagar A Bastawy
- Department of Endodontics, Faculty of Dentistry, King Abdulaziz University (KAU), Jeddah, Saudi Arabia
| |
Collapse
|
34
|
Regenerative Endodontic Management of an Immature Molar Using Calcium Hydroxide and Triple Antibiotic Paste: a Two-Year Follow-Up. Case Rep Dent 2020; 2020:9025847. [PMID: 32095292 PMCID: PMC7035542 DOI: 10.1155/2020/9025847] [Citation(s) in RCA: 5] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/12/2019] [Accepted: 01/22/2020] [Indexed: 01/01/2023] Open
Abstract
The regenerative endodontic procedure (REP) is considered a viable treatment option for immature teeth with necrotic pulp and periapical radiolucency which can facilitate continued root formation. In this report, an immature necrotic mandibular molar received REP in three appointments wherein chemomechanical debridement was performed with a sequential application of nonsetting calcium hydroxide (in the whole canal) and triple antibiotics paste (in the root's middle third) dressings in the first and second appointments, respectively. In the third appointment, blood clots were created in the root canals. MTA was placed over the blood clots and the tooth was restored with a composite filling and stainless-steel crown. Recall appointments were performed for two years where the tooth was deemed asymptomatic clinically and a complete root formation with significant periapical healing was evident radiographically. More cases are required to warrant the feasibility of this disinfection protocol.
Collapse
|
35
|
Does Apical Papilla Survive and Develop in Apical Periodontitis Presence after Regenerative Endodontic Procedures? APPLIED SCIENCES-BASEL 2019. [DOI: 10.3390/app9193942] [Citation(s) in RCA: 40] [Impact Index Per Article: 8.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 12/16/2022]
Abstract
Regenerative endodontic procedures (REPs) have emerged as a treatment option for immature necrotic teeth to allow the reestablishment of a newly formed vital tissue and enable continued root development. The apical papilla stem cells (SCAPs) play an important role in physiologic root development and may also contribute to further root development during REPs. The goal of these case reports is to show evidence of the apical papilla survival and development, in human teeth with apical periodontitis, after REPs, with 5-year clinical and radiographic follow-up. In the first case, an 11-year-old girl with acute apical abscess of tooth 15 was referred for a REP. Treatment was performed with an intracanal medication followed by induction of a blood clot and a Mineral Trioxide Aggregate (MTA) cervical barrier. The 5-year follow-up showed an appreciable increase in root length as well as root canal thickness. In case 2, a 16-year-old girl was referred for endodontic treatment of tooth 21. The parents of the patient recalled a previous dental trauma (no specified on the patient records) on tooth 21 at age 7. The dental history reports a previous endodontic treatment failure and presence of a long-standing sinus tract. A mineralized tissue beyond the root apical portion could be seen at the preoperative X-ray. Nonsurgical root canal retreatment with an apical barrier was suggested as the treatment plan and accepted by the patient. After 2 weeks, the patient was recalled for a follow-up appointment presenting spontaneous pain, swelling, and sinus tract. Apical surgery was performed. Histopathological assessment of the apical root fragment collected showed the presence of dentin, cementum and pulp tissue, including odontoblasts. The 5-year follow-up depicted complete apical healing. The present case reports support survival and continued potential differentiation of the apical papilla after endodontic infection.
Collapse
|
36
|
Voicu G, Didilescu AC, Stoian AB, Dumitriu C, Greabu M, Andrei M. Mineralogical and Microstructural Characteristics of Two Dental Pulp Capping Materials. MATERIALS 2019; 12:ma12111772. [PMID: 31159182 PMCID: PMC6600720 DOI: 10.3390/ma12111772] [Citation(s) in RCA: 11] [Impact Index Per Article: 2.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 05/13/2019] [Revised: 05/26/2019] [Accepted: 05/28/2019] [Indexed: 02/07/2023]
Abstract
This paper aims to investigate the composition, surface, and microstructural characteristics, and bioactivity of two commercially available pulp capping materials known as TheraCal LC and BIO MTA+. The materials were prepared as cylindrical samples and assessed by X-ray diffraction (XRD) and complex thermal analysis for mineralogical characterization, and by scanning electron microscopy (SEM) coupled with energy dispersive of X-ray (EDX), Fourier-Transformed Infrared Spectroscopy (FT-IR), and atomic force microscopy (AFM) for microstructural and surface characteristics. The in vitro bioactivity was highlighted by surface mineralization throughout SEM coupled with EDX and FT-IR analysis. XRD analysis performed on both materials showed calcium silicate phases and different radiopacifying compounds. AFM measurements indicated a smoother and more homogenous surface with a lower average roughness for TheraCal LC due to the resin matrix from its composition. FT-IR analysis displayed bands for several compounds in both materials. Both materials exhibited bioactive properties showing surface mineralization after being immersed in solution similar to the human physiological environment. However, the MTA cement showed a better mineralization due to the anhydrous and hydrated phases.
Collapse
Affiliation(s)
- Georgeta Voicu
- Department of Biomaterials and Medical Devices, Faculty of Medical Engineering, University Politehnica of Bucharest, 1-7 Polizu, 011061 Bucharest, Romania.
| | - Andreea C Didilescu
- Division of Embryology, Faculty of Dental Medicine, Carol Davila University of Medicine and Pharmacy, 8 Eroii Sanitari Boulevard, 050474 Bucharest, Romania.
| | - Andrei B Stoian
- Department of General Chemistry, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, University Politehnica of Bucharest, 1-7 Polizu, 011061 Bucharest, Romania.
| | - Cristina Dumitriu
- Department of General Chemistry, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, University Politehnica of Bucharest, 1-7 Polizu, 011061 Bucharest, Romania.
| | - Maria Greabu
- Division of Biochemistry, Carol Davila University of Medicine and Pharmacy, 8 Eroii Sanitari Boulevard, 050474 Bucharest, Romania.
| | - Mihai Andrei
- Division of Embryology, Faculty of Dental Medicine, Carol Davila University of Medicine and Pharmacy, 8 Eroii Sanitari Boulevard, 050474 Bucharest, Romania.
| |
Collapse
|
37
|
Regenerative Endodontic Procedures Using Contemporary Endodontic Materials. MATERIALS 2019; 12:ma12060908. [PMID: 30893790 PMCID: PMC6471897 DOI: 10.3390/ma12060908] [Citation(s) in RCA: 36] [Impact Index Per Article: 7.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 02/04/2019] [Revised: 02/28/2019] [Accepted: 03/13/2019] [Indexed: 12/12/2022]
Abstract
Calcium hydroxide apexification and Mineral Trioxide Aggregate (MTA) apexification are classical treatments for necrotic immature permanent teeth. The first tend to fail for lack of compliance given the high number of sessions needed; the second has technical difficulties such as material manipulation and overfilling. With both techniques, the root development is interrupted leaving the tooth with a fragile root structure, a poor crown-to-root ratio, periodontal breakdown, and high risk of fracture, compromising long-term prognosis of the tooth. New scientific literature has described a procedure that allows complete root development of these specific teeth. This regenerative endodontic procedure (REP) proposes the use of a combination of antimicrobials and irrigants, no canal walls instrumentation, induced apical bleeding to form a blood clot and a tight seal into the root canal to promote healing. MTA is the most used material to perform this seal, but updated guidelines advise the use of other bioactive endodontic cements that incorporate calcium and silicate in their compositions. They share most of their characteristics with MTA but claim to have fewer drawbacks with regards to manipulation and aesthetics. The purpose of the present article is to review pertinent literature and to describe the clinical procedures protocol with its variations, and their clinical application.
Collapse
|
38
|
Six-Month Color Stability Assessment of Two Calcium Silicate-Based Cements Used in Regenerative Endodontic Procedures. J Funct Biomater 2019; 10:jfb10010014. [PMID: 30823393 PMCID: PMC6462979 DOI: 10.3390/jfb10010014] [Citation(s) in RCA: 23] [Impact Index Per Article: 4.6] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/13/2019] [Revised: 02/18/2019] [Accepted: 02/18/2019] [Indexed: 02/07/2023] Open
Abstract
AIM The purpose of the present study is to assess the color stability of two calcium silicate-based cements (CSCs) used in regenerative endodontic procedures (REPs). METHODS A total of 40 acrylic single-rooted transparent teeth, with immature apex, were used. Root canals were filled up to 3 mm below the level of the cementoenamel junction, with either saline solution (Mineral Trioxide Aggregate (MTA)/saline and Biodentine/saline) or blood (MTA/blood and Biodentine/blood). Subsequently, ProRoot MTA® or BiodentineTM was placed in the root canal to create a cervical barrier. Color measurement was carried out at four different evaluation periods (3 h, 72 h, 7 days, and 6 months). Shade analysis within the L* a* b* color space was performed and color variation (∆E) calculated. The significance level for statistical analysis was set at p < 0.05. RESULTS The four groups showed a significant decrease in L* values over time. The ΔE value increased over time for all groups but was not statistically significant for the Biodentine/blood group. Two-way ANOVA showed no interaction between the CSC and treatment (contact with saline solution or blood). CSC used was the factor responsible for ΔE over time, inducing statistically significant color variations from T3H to T7D (p = 0.04) and T3H to T6M (p < 0.01). After 6 months, MTA/saline had 5.08 (p = 0.001) higher ΔE than Biodentine/Saline and the MTA/blood had 3.65 (p = 0.009) higher than Biodentine/blood. CONCLUSIONS After 6 months, regardless of blood exposure, Biodentine exhibits superior color stability compared to MTA. Biodentine might be a suitable alternative to MTA as a cervical barrier material in REPs.
Collapse
|
39
|
Sequeira DB, Seabra CM, Palma PJ, Cardoso AL, Peça J, Santos JM. Effects of a New Bioceramic Material on Human Apical Papilla Cells. J Funct Biomater 2018; 9:E74. [PMID: 30558359 PMCID: PMC6306901 DOI: 10.3390/jfb9040074] [Citation(s) in RCA: 40] [Impact Index Per Article: 6.7] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/22/2018] [Revised: 12/12/2018] [Accepted: 12/13/2018] [Indexed: 12/18/2022] Open
Abstract
BACKGROUND The development of materials with bioregenerative properties is critically important for vital pulp therapies and regenerative endodontic procedures. The aim of this study was to evaluate the cytocompatibility and cytotoxicity of a new endodontic biomaterial, PulpGuard, in comparison with two other biomaterials widely used in endodontic procedures, ProRoot Mineral Trioxide Aggregate (MTA) and Biodentine. METHODS Apical papilla cells (APCs) were isolated from third molars with incomplete rhizogenesis from patients with orthodontic indication for dental extraction. Cultured APCs were incubated for 24, 48, or 72 h with different dilutions of eluates prepared from the three materials. Cellular viability, mobility, and proliferation were assessed in vitro using the Alamar Blue assay and a wound-healing test. The cells were also cultured in direct contact with the surface of each material. These were then analyzed via Scanning Electron Microscopy (SEM), and the surface chemical composition was determined by Energy-Dispersive Spectroscopy (EDS). RESULTS Cells incubated in the presence of eluates extracted from ProRoot MTA and PulpGuard presented rates of viability comparable to those of control cells; in contrast, undiluted Biodentine eluates induced a significant reduction of cellular viability. The wound-healing assay revealed that eluates from ProRoot MTA and PulpGuard allowed for unhindered cellular migration and proliferation. Cellular adhesion was observed on the surface of all materials tested. Consistent with their disclosed composition, EDS analysis found high relative abundance of calcium in Biodentine and ProRoot MTA and high abundance of silicon in PulpGuard. Significant amounts of zinc and calcium were also present in PulpGuard discs. Concerning solubility, Biodentine and ProRoot MTA presented mild weight loss after eluate extraction, while PulpGuard discs showed significant water uptake. CONCLUSIONS PulpGuard displayed a good in vitro cytocompatibility profile and did not significantly affect the proliferation and migration rates of APCs. Cells cultured in the presence of PulpGuard eluates displayed a similar profile to those cultured with eluates from the widely used endodontic cement ProRoot MTA.
Collapse
Affiliation(s)
- Diana B Sequeira
- CNC-Center for Neuroscience and Cell Biology, University of Coimbra, Coimbra 3004-504, Portugal.
- Institute for Interdisciplinary Research (IIIUC), University of Coimbra, Coimbra 3030-789, Portugal.
- PhD Program in Experimental Biology and Biomedicine (PDBEB), University of Coimbra, Coimbra 3004-504, Portugal.
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, Coimbra 3000-075 Portugal.
| | - Catarina M Seabra
- CNC-Center for Neuroscience and Cell Biology, University of Coimbra, Coimbra 3004-504, Portugal.
- Institute for Interdisciplinary Research (IIIUC), University of Coimbra, Coimbra 3030-789, Portugal.
| | - Paulo J Palma
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, Coimbra 3000-075 Portugal.
| | - Ana Luísa Cardoso
- CNC-Center for Neuroscience and Cell Biology, University of Coimbra, Coimbra 3004-504, Portugal.
- Institute for Interdisciplinary Research (IIIUC), University of Coimbra, Coimbra 3030-789, Portugal.
| | - João Peça
- CNC-Center for Neuroscience and Cell Biology, University of Coimbra, Coimbra 3004-504, Portugal.
- Institute for Interdisciplinary Research (IIIUC), University of Coimbra, Coimbra 3030-789, Portugal.
| | - João Miguel Santos
- Institute of Endodontics, Faculty of Medicine, University of Coimbra, Coimbra 3000-075 Portugal.
| |
Collapse
|