Orientation-Independent Yield Stress and Activation Volume of Dislocation Nucleation in LiTaO3 Single Crystal by Nanoindentation

The Strain Rate Sensitivity and Creep Behavior for the Tripler Plane of Potassium Dihydrogen Phosphate Crystal by Nanoindentation

As an excellent multifunctional single crystal, potassium dihydrogen phosphate (KDP) is a well-known, difficult-to-process material for its soft-brittle and deliquescent nature. The surface mechanical properties are critical to the machining process; however, the characteristics of deformation behavior for KDP crystals have not been well studied. In this work, the strain rate effect on hardness was investigated on the mechanically polished tripler plane of a KDP crystal relying on nanoindentation technology. By increasing the strain rate from 0.001 to 0.1 s⁻¹, hardness increased from 1.67 to 2.07 GPa. Hence, the strain rate sensitivity was determined as 0.053, and the activation volume of dislocation nucleation was 169 ų. Based on the constant load-holding method, creep deformation was studied at various holding depths at room temperature. Under the spherical tip, creep deformation could be greatly enhanced with increasing holding depth, which was mainly due to the enlarged holding strain. Under the self-similar Berkovich indenter, creep strain could be reduced at a deeper location. Such an indentation size effect on creep deformation was firstly reported for KDP crystals. The strain rate sensitivity of the steady-state creep flow was estimated, and the creep mechanism was qualitatively discussed.

Revealing the Plastic Mode of Time-Dependent Deformation of a LiTaO3 Single Crystal by Nanoindentation

Recently, instrumental nanoindentation has been widely applied to detect time-dependent plastic deformation or creep behavior in numerous materials, particularly thin films and heterogeneous materials. However, deformation mechanism at nanoindentation holding stage has not been well revealed hitherto. In the current work, nanoindentation holding tests with high loads were performed on a brittle LiTaO₃ single crystal. The surface morphologies of residual impressions with various holding times were investigated. It was indicated that generation of secondary cracks and propagation of both main and secondary cracks were the dominating mechanism for time-dependent plastic deformation at the initial holding stage, and the density and length of cracks were invariable at the steady-state holding stage, which suggested a nonlocalized plastic deformation beneath the indenter. It could be concluded that time-dependent plastic deformation of brittle ceramic under nanoindentation is composed of instant cracking as the continuation of loading sequence and homogeneous creep flow by high shear-compression stress at room temperature.

On the Room-Temperature Creep Behavior and Its Correlation with Length Scale of a Litao3 Single Crystal by Spherical Nanoindentation

Relying on nanoindentation technology, the room-temperature creep behavior of a LiTaO₃ single crystal in the typical orientation (01 1 ¯ 2), i.e., Y-42° plane was investigated. Three kinds of spherical tips with the radii of 0.76, 2.95 and 9.8 μm were respectively applied to detect nanoindentation length scale effect on creep deformation at both elastic and plastic regions. Superficially, both creep displacement and rate were nearly linearly increased with increasing holding depth and independent of tip size, which could be ascribed to the simultaneously enlarged holding strain and deformation volume beneath the indenter. At a similar holding strain, creep deformation, i.e., creep strain and strain rate were more pronounced under smaller spherical tips. Strain rate sensitivities of creep flows under different spherical tips and holding strains were also estimated. The potential room-temperature creep mechanism of LiTaO₃ under high shear compression stress was discussed.