Effect of Exclusive Primer and Adhesive on Microtensile Bond Strength of Self-Adhesive Resin Cement to Dentin

Degree of conversion of dual-cured composite luting agents: The effect of transition metal-based touch-cure activators

PURPOSE

The aim of the study was (a) to assess the effect of universal adhesives and tooth primers with novel touch-cure activators on the conversion of dual-cured resin composite luting agents (RLAs) polymerized under the self-curing mode, and (b) to investigate the source of the catalytic effect exerted by the activators.

MATERIALS AND METHODS

The materials selected were the adhesive RLAs Panavia V5/Tooth Primer (PV5/TP5), Variolink Esthetic DC/Adhese Universal DC (VLE/ADC), and the self-adhesive RLAs GCem ONE/AE Primer (GCO/AEP), RelyX Universal/Scotchbond Universal Plus (RXU/SUP) and Panavia SA Universal/Clearfil Universal Bond Quick (PSU/CUQ), the later serving as a control with an aryl-sulfinate activator. Coronal dentin specimens were prepared (n = 5/material), treated with the corresponding primers/adhesives (non-irradiated) and covered with a 100 μm-thick RLA layer (SC+A group). Three specimen series were additionally prepared (n = 3 × 5/material): A self-cured without the primers/adhesives (SC group), a dual-cured (20 s irradiation) with the corresponding primers/adhesives (DC+A group) and a dual-cured without primers/adhesives (DC group). All specimens were stored for 15 min (37 °C/dark/60 %RH). After demolding the degree of C = C conversion (DC%, top RLA surfaces) was measured by ATR-FTIR spectroscopy. The primer/adhesive liquids were further analyzed by ICP-MS and the microbrush tips of ADC by SEM-EDS.

RESULTS

The touch-cure activators increased the DC% in all self-cured RLAs but failed to reach the values of the corresponding dual-cured RLAs. The effect of the activators in dual-cured specimens was negligible. The ICP-MS analysis showed the presence of V (AEP, TP5, ADC) and Cu (SUP) transitional metals in the activators, with V been located at the free ends of ADC tip bristles. The V activators demonstrated the highest DC% improvement in self-cured specimens.

CONCLUSION

The new touch-cure activators significantly increased the conversion of the self-cured RLAs. Therefore, this step should be considered as universally applicable and not selective, as currently proposed for the self-adhesive luting agents by the manufacturers.

Promotion of Dentin Biomimetic Mineralization and Bonding Efficacy by Interfacial Control of an Experimental Citric Acid Dental Etching Agent

Resin-bonded restorations are the most important caries treatment method in clinical practice. Thus, improving the durability of dentin bonding remains a pressing issue. As a promising solution, guided tissue remineralization can induce the formation of apatite nanocrystals to repair defects in the dentin bonding interface. In this study, we present an experimental 20 wt % citric acid (CA) dental etching agent that removes the smear layer. After CA-etching, approximately 3.55 wt % residual CA formed a strong bond with collagen fibrils, reducing the interfacial energy between the remineralizing solution and dentin. CA helped achieve almost complete intrafibrillar and extrafibrillar mineralization after 24 h of mineralization. CA also significantly promoted poly(amidoamine)-induced dentin biomimetic mineralization. The elastic modulus and microhardness of remineralized dentin were restored to that of sound dentin. The remineralized interface reduced microleakage and provided a stronger, longer-lasting bond than conventional phosphate acid-etching. The newly developed CA dental etching agents promoted rapid dentin biomimetic mineralization and improved bonding efficacy through interfacial control, representing a new approach with clinical practice implications.

Touch-cure activation by marketed universal resin luting cements of their associated primer to dentin

PURPOSE

The aim of this study was to investigate the dentin shear bond strength (SBS) and bonding interface of three recently developed "universal" resin luting cements based on different modalities.

METHODS

The dentin SBS and interfacial analysis of three recently launched "universal" resin luting cements, namely, G-Cem One, RelyX Universal and Panavia SA cement universal, were studied. All bonding protocols, including the previous use of their dedicated primer or universal adhesive in touch-cure mode or light-cure mode were performed. Variolink Esthetic LC used in conjunction with Scotchbond Universal Plus was used as a control group. For each group (n = 9), 10 specimens were tested for dentin SBS and two were examined by scanning electron microscopy. SBS were analyzed by two-way ANOVA followed by Dunnett's test.

RESULTS

SBS values showed that the three "universal" resin luting cements tested exhibit different adhesive behaviors. G-Cem One with its touch-cure activated primer had a greater SBS to dentin (25.5 MPa) than that of the control group (22.1 MPa).

CONCLUSION

"Universal" resin luting cements have variable efficacy when used in self-curing mode. The touch-curing mode is also of concern but may show high potential for some formulations.

Comparative Assessment of Different Pre-Treatment Bonding Strategies to Improve the Adhesion of Self-Adhesive Composites to Dentin

The aim of this study is to compare the adhesive interface formed in dentin, using self-adhesive composites applied with different bonding strategies, by testing the microtensile bond strength (μTBS) and ultramorphology through the use of light microscopy. Permanent, sound human molars were randomly allocated to six experimental groups. The groups included a negative control group, where only etching was performed via EtchOnly; a positive control group where an adhesive was applied, OptiBondFL (OBFL); and an experimental group where a primer was applied using a co-curing strategy together with a composite (Primer_CoCuring). The samples were sectioned into microspecimens for μTBS (n = 8) and into 1-mm thick slabs for light microscopy using Masson’s trichrome staining protocol (n = 3). The statistical analysis included a two-way ANOVA for μTBS data and Tukey’s HSD was used as a post-hoc test (significance level of 5%; SPSS v. 26.0). The results of the μTBS revealed that the self-adhesive composite (F = 6.0, p < 0.018) and the bonding strategy (F = 444.1, p < 0.001) significantly affected the bond strength to dentin. However, their interactions were not significant (F = 1.2, p = 0.29). Etching dentin with no additional treatment revealed the lowest μTBS (VF_EtchOnly = 2.4 ± 0.8 MPa; CC_EtchOnly = 2.0 ± 0.4 MPa), which was significantly different from using a primer (VF_CoCu = 8.8 ± 0.8 MPa; CC_CoCu = 6.3 ± 1.0 MPa) or using the full adhesive (VF_OptiBondFL = 22.4 ± 0.3 MPa; CC_OptibondFL = 21.2 ± 0.4 MPa). Microscopy images revealed that the experimental Primer_CoCuring was the only group with no collagen fibers exposed to the dentin−composite interface. Overall, the use of a primer, within the limitations of this study, increased the bonding of the self-adhesive composite and provided sufficient infiltration of the collagen based on light-microscopic imaging.