Influence of Cu2+ Ions on the Corrosion Resistance of AZ31 Magnesium Alloy with Microarc Oxidation

Review of the Effect of Surface Coating Modification on Magnesium Alloy Biocompatibility

Magnesium alloy, as an absorbable and implantable biomaterial, has been greatly developed in the application field of biomaterials in recent years due to its excellent biocompatibility and biomechanics. However, due to the poor corrosion resistance of magnesium alloy in the physiological environment, the degradation rate will be unbalanced, which seriously affects the clinical use. There are two main ways to improve the corrosion resistance of magnesium alloy: one is by adding alloying elements, the other is by surface modification technology. Compared with adding alloy elements, the surface coating modification has the following advantages: (1) The surface coating modification is carried out without changing the matrix elements of magnesium alloy, avoiding the introduction of other elements; (2) The corrosion resistance of magnesium alloy can be improved by relatively simple physical, chemical, or electrochemical improvement. From the perspective of corrosion resistance and biocompatibility of biomedical magnesium alloy materials, this paper summarizes the application and characteristics of six different surface coating modifications in the biomedical magnesium alloy field, including chemical conversion method, micro-arc oxidation method, sol-gel method, electrophoretic deposition, hydrothermal method, and thermal spraying method. In the last section, it looks forward to the development prospect of surface coating modification and points out that preparing modified coatings on the implant surface combined with various modification post-treatment technologies is the main direction to improve biocompatibility and realize clinical functionalization.

Effect of Cu2+ on Corrosion Behavior of A106B Carbon Steel and 304L Stainless Steels in Seawater

The corrosion behaviors of A106B carbon steel and 304L stainless steel (SS) in seawater with different Cu²⁺ concentrations were studied by the immersion test and the potentiodynamic polarization test. The results showed that with the increasing Cu²⁺ concentration, the mass lot rates of A106B and 304L SS all increased in the immersion test, and compared with A106B, the mass lot rates of 304L SS were all smaller. In the potentiodynamic polarization test, following the concentration of Cu²⁺ increased, the corrosion potential of A106B firstly shifted negatively; then, when Cu²⁺ increased to 100 ppm, the polarization curve moved to the upper right direction; namely, both the corrosion potential and corrosion electrical density increased. The corrosion potential of 304L SS increased with the increasing Cu²⁺, and the passive region was reduced; the pitting sensitivity improved.