Mechanical Properties of Glass Ionomer Cements after Incorporation of Marine Derived Porous Cuttlefish Bone Hydroxyapatite

Evaluation of the Mechanical Properties of Three Resin-Modified Glass-Ionomer Materials

This study is aimed at evaluating the flexural strength (FS), fracture toughness (FT), and diametral tensile strength (DTS) of three resin-modified glass-ionomer cements (RMGICs): Ketac Nano, Riva Light Cure, and Fuji II LC. One hundred twenty specimens were prepared from the RMGIC materials ( $n=10$ ). The cements were mixed and inserted into different mould sizes according to the test performed: FS: rectangular Teflon mould ( $32\text{mm}\times 3.15\text{mm}\times 2\text{mm}$ ); FT: notchless triangular prism (NTP) Teflon mould ( $6\text{mm}\times 6\text{mm}\times 6\text{mm}\times 12\text{mm}$ ); and DTS: ring road stainless steel mould ( $6\text{mm}\times 3\text{mm}$ ). Specimens were light cured for 20 seconds on each surface and stored in distilled water at ${37}^{°}\text{C}\pm 2^{°}\text{C}$ for seven days prior to tests. To evaluate the influence of storage in the mechanical properties of the RMGIs, specimens tested for DTS were stored in distilled water at ${37}^{°}\text{C}\pm 2^{°}\text{C}$ for 32 days prior to test. Data were analyzed by ANOVA and Tukey’s test ( $\alpha =0.05$ ). Fuji II LC presented significantly higher values for all tests employed when compared to Ketac Nano and Riva LC RMGIs. There was no significant difference on DTS before and after the 32-day storage for each material. Fuji II LC presented superior mechanical properties when compared to Ketac Nano, and Riva LC storage showed no influence on the mechanical properties of the RMGI materials tested.

Effects of Nanohydroxyapatite Incorporation into Glass Ionomer Cement (GIC)

Glass ionomer cement (GIC) or polyalkenoate cement is a water-based cement that is commonly used in clinical dentistry procedures as a restorative material. It exhibits great properties such as fluoride-ion release, good biocompatibility, ease of use and great osteoconductive properties. However, GIC’s low mechanical properties have become a major drawback, limiting the cement’s usage, especially in high stress-bearing areas. Nanohydroxyapatite, which is a biologically active phosphate ceramic, is added as a specific filler into glass ionomer cement to improve its properties. In this review, it is shown that incorporating hydroxyapatite nanoparticles (nHA) into GIC has been proven to exhibit better physical properties, such as increasing the compressive strength and fracture toughness. It has also been shown that the addition of nanohydroxyapatite into GIC reduces cytotoxicity and microleakage, whilst heightening its fluoride ion release and antibacterial properties. This review aims to provide a brief overview of the recent studies elucidating their recommendations which are linked to the benefits of incorporating hydroxyapatite nanoparticles into glass ionomer cement.

Compressive Strength of Conventional Glass Ionomer Cement Modified with TiO2 Nano-Powder and Marine-Derived HAp Micro-Powder

The aim of this research was to investigate the compressive strength (CS), breaking strength (BS), and compressive modulus (CM) of conventional glass ionomer cement (GIC) modified with TiO₂ nano particles, marine-derived hydroxyapatite (md-HAp) microparticles (<45 µm), and a combination of TiO₂ NP and md-HAp particles. The materials used in the study were conventional GIC Fuji IX GP Extra (GC Corporation, Tokyo, Japan), TiO₂ powder P25 (Degussa, Essen, Germany), and HAp synthesized from cuttlefish bone and ground in a mortar to obtain md-HAp powder. md-HAp was characterized using FTIR and SEM analysis. There were four groups of GIC samples: (i) Fuji IX control group, (ii) powder modified with 3 wt% TiO2, (iii) powder modified with 3 wt% HAp, and (iv) powder modified with 1.5 wt% TiO2 + 1.5 wt% HAp. Measurements were performed in a universal testing machine, and CS, BS, and CM were calculated. Statistical analysis was performed using ANOVA and Tukey’s tests. CS, BS, and CM differed significantly between the Fuji IX control group and all experimental groups while differences between the experimental groups were not statistically significant. The addition of TiO₂ NP, md-HAp micro-sized particles, and a combination of TiO₂ and md-HAp reduced the CS, BS, and CM of conventional GICs when mixed at the powder/liquid (p/l) ratio recommended by the manufacturer.