Investigation of Welds and Heat Affected Zones in Weld Surfacing Steel Plates Taking into Account the Bead Sequence

Optimization of Bead Morphology for GMAW-Based Wire-Arc Additive Manufacturing of 2.25 Cr-1.0 Mo Steel Using Metal-Cored Wires

The fabrication of components involves the deposition of multiple beads in multiple layers for wire-arc additive manufacturing (WAAM). WAAM performed using gas metal arc welding (GMAW) allows for the manufacturing of parts through multiple-bead multi-layer deposition, which depends on the process variables. Thus, the selection of process parameters along with their required levels is mandatory to deposit multiple layers for WAAM. To obtain the desired levels of parameters, bead-on-plate trials were taken on the base plate of low alloy steel by following an experimental matrix produced through the Box–Behnken design (BBD) on GMAW-based WAAM. Wire feed speed, travel speed, and voltage were chosen as the input parameters and bead width and bead height were chosen as the output parameters. Furthermore, the robustness and adequacy of the obtained regression equations were analyzed by using analysis of variance (ANOVA). For both responses of BW and BH, values of R2 and adj. R2 were found to be near unity, which has shown the fitness of the model. Teaching–learning-based optimization (TLBO) technique was then employed for optimization. Within the selected range of process variables, the single-objective optimization result showed a maximum bead height (BH) of 7.81 mm, and a minimum bead width (BW) of 4.73 mm. To tackle the contradicting nature of responses, Pareto fronts were also generated, which provides a unique non-dominated solution. Validation trials were also conducted to reveal the ability and suitability of the TLBO algorithm. The discrepancy between the anticipated and measured values was observed to be negligible, with a deviation of less than 5% for all the validation trials. This demonstrates the success of the established model and TLBO algorithm. The optimum feasible settings for multi-layer metal deposition were determined after further tuning. A multi-layer structure free from any disbonding was successfully manufactured at the optimized variables. The authors suggest that the optimum parametric settings would be beneficial for the deposition of layer-by-layer weld beads for additive manufacturing of components.

Effective Jet-Grouting Application for Improving the State of Deformation of Landmarks

The problem of improving the state of deformation of landmarks is an important aspect when performing civil services, because they have a historical interest and bring symbolisms which relate to an event of particular interest for the community. The engineering–geological surveys, technical evaluation and operational suitability of landmarks of national significance are performed to improve the state of deformation. The conducted analytical assessment of landslide hazard slope stability in the RocScience Slide computational complex shows that in the presence of landslide prevention works, and the stability coefficient is increased by a factor of 1.21–1.37. The regularities of deformation and strength parameters of the soil–cement obtained during the jet-grouting application indicated an increase in strength gain of amplifier elements by an average of 1.6–4.0 times. This proves the effectiveness of the jet-grouting application for improving the state of deformation of landmarks of national significance.

Development of Laser Welding and Surface Treatment of Metals

This Special Issue on Development of Laser Welding and Surface Treatment of Metals contains as many as twenty-two research articles mainly related to the application of lasers, but also on other welding processes that may be competitive to laser technologies under specific conditions. Despite the introduction of lasers for material processing in the 1960s, the continuous development of laser devices also leads to the development and expansion of laser technology applications. This Special Issue is a compendium of knowledge in the field of fusion welding, the manufacturing of surface layers and coatings with increased wear resistance and tribological characteristics, as well as corrosion resistance and the characterization of coatings and surface layers. The topics of the presented research articles include aspects related to laser welding (eight articles), especially technological conditions, the properties of different types of joints, and analytical and numerical aspects of modelling the laser heat sources. The second dominant issue concerns laser cladding and laser surface treatment of different ferrous and nonferrous metallic and composite materials (six articles). In addition, there are interesting results of the study of fusion welding under forced cooling of the deposit or underwater conditions (four articles), results on the characterization of wear resistance coating produced by different technologies that can be competitive for laser cladding (three articles), and an original study on local strengthening of the thin-walled structure by laser treatment (one article). This Special Issue provides very wide and valuable knowledge based on theoretical and empirical study in the field of laser and fusion welding, laser and related coating technologies, characterization of coatings, and wear phenomena.

Elucidating the Effect of Step Cooling Heat Treatment on the Properties of 2.25 Cr-1.0 Mo Steel Welded with a Combination of GMAW Techniques Incorporating Metal-Cored Wires

The prospect of using metal-cored wires instead of solid wires during gas metal arc welding (GMAW) of 2.25 Cr–1.0 Mo steels embraces several challenges. The in-service requirements for the equipment made up of these steels are stringent. The major challenge faced by the manufacturers is temper embrittlement. In the current study, the temper embrittlement susceptibility of the welded joint was ascertained by subjecting it to step cooling heat treatment. A 25 mm thick 2.25 Cr–1.0 Mo weld joint was prepared using a combination of the regulated metal deposition (RMD) and GMAW processes incorporating metal-cored wires. After welding the plates were exposed to post-weld heat treatment followed by a rigorous step cooling heat treatment prescribed by API standards. The temper embrittlement susceptibility of the weld joint was ascertained by Bruscato X-factor as well as by formulating ductile-to-brittle transition temperature (DBTT) curves by carrying out the impact toughness testing at various temperatures. Detailed microscopy and hardness studies were also carried out. It was established from the study that the X-factor value for the welded joint was 15.4. The DBTT for the weld joint was found to occur at −37 °C which was well below 10 °C. Optical microscopy and scanning electron microscopy indicated the presence of carbides and the energy dispersive X-ray spectrometry studies indicated the presence of chromium and manganese-rich carbides along with the presence of sulfur near the grain boundaries. This study establishes a base for the usage of metal-cored wires particularly in high temperature and pressure application of Cr–Mo steels.

Effect of Welding Sequence and the Transverse Geometry of the Weld Overlay on the Distribution of Residual Stress in the Weld Overlay Repair of T23 Tubes

Water-wall tubes are important components in power plants and are used to absorb the heat from the boilers, and they often fail prematurely due to corrosion, erosion, and fatigue during service. To repair the defects, weld overlay repair is often adopted by forming a compressive stress area around the susceptible area to prevent the cracks from propagating. In order to obtain reasonable process parameters of weld overlay repair, a study combining experiments and numerical simulations was performed to investigate the welding residual stress distribution on the repaired area with different welding repair methods. The results reveal that a compressive stress area is generated on the repaired area after the repair, and a center-to-outside welding sequence is better than either a right-to-left welding sequence or an outside-to-center welding sequence when overlaying a one-layer weld; with an increase in the number of weld layers, the compressive stress area of the repaired area is expanded, and the stress level is increased, which results from the upward movement of the compressive stress area of the subsequent-overlaying layer and the superposition of the compression areas of the subsequent-overlaying layer and previous-overlaying layer, respectively. In addition, the number of the weld passes of each layer should be not less than four with the center-to-outside welding sequence.

Weldability of Underwater Wet-Welded HSLA Steel: Effects of Electrode Hydrophobic Coatings

The paper presents the effects of waterproof coatings use to cover electrodes on the weldability of high-strength, low-alloy (HSLA) steel in water. With the aim of improving the weldability of S460N HSLA steel in water, modifications of welding filler material were chosen. The surfaces of electrodes were covered by different hydrophobic substances. The aim of the controlled thermal severity (CTS) test was to check the influence of these substances on the HSLA steel weldability in the wet welding conditions. The visual test, metallographic tests, and hardness Vickers HV10 measurements were performed during investigations. The results proved that hydrophobic coatings can reduce the hardness of welded joints in the heat-affected zone by 40–50 HV10. Additionally, the number of cold cracks can be significantly reduced by application of waterproof coatings on the filler material. The obtained results showed that electrode hydrophobic coatings can be used to improve the weldability of HSLA steel in underwater conditions.