Optimisation of Shrinkage and Strength on Thick Plate Part Using Recycled LDPE Materials

Study of Injection Molding Process to Improve Geometrical Quality of Thick-Walled Polycarbonate Optical Lenses by Reducing Sink Marks

This study investigates the challenges and potential of conventional injection molding for producing thick-walled optical components. The research primarily focuses on optimizing process parameters and mold design to enhance product quality. The methods include software simulations and experimental validation using polycarbonate test samples (optical lenses). Significant parameters such as melt temperature, mold temperature, injection pressure, and packing pressure were varied to assess their impact on geometric accuracy and visual properties. The results show that lower melt temperatures and higher mold temperatures significantly reduce the occurrence of dimensional defects. Additionally, the design of the gate system was found to be crucial in minimizing defects and ensuring uniform material flow. Effective packing pressure was essential in reducing volumetric shrinkage and sink marks. Furthermore, we monitored the deviation between the predicted and actual defects relative to the thickness of the sample wall. After optimization, the occurrence of obvious defects was eliminated across all sample thicknesses (lenses), and the impact of the critical defect, the sink mark on the planar side of the lens, was minimized. These findings demonstrate the substantial potential of conventional injection molding to produce high-quality thick-walled parts when these parameters are precisely controlled. This study provides valuable insights for the efficient design and manufacturing of optical components, addressing the growing demand for high-performance thick-walled plastic products.

Computer-Aided Reengineering towards Plastic Part Failure Minimization

The work reported here intends to identify and mitigate the causes for failure in a plastic faucet holder, a part of an integral float faucet with a well-documented history of fracture occurrence. A methodology for the identification of hidden internal defects in plastic parts and the elaboration of the required corrective actions towards quality improvement is, therefore, presented. Firstly, part defects were identified via injection moulding process numerical simulation. The latter has enabled the prediction of an excessive volumetric shrinkage at the core of the faucet holder, highlighting the presence of internal voids and, hence, the possible deterioration of the load-bearing capacity. The supposition was later confirmed by X-ray topography scans. Part reengineering, consisting of localized thickness reduction, was the option chosen for decreasing the high shrinkage at the core. For validation purposes, structural analyses were carried out, with and without accounting for the injection moulding processing history. The results obtained during part structural analysis have enabled us to conclude that, when taking into account the residual stresses generated during injection moulding, the analysis more closely reflects the experimental data and allows us to implicitly envisage the propensity to fracture. Moreover, the part modifications, undertaken during the faucet holder reengineering, led to the reduction of the cumulative (processing and imposed by load) stresses by 50%, when compared to the original design analysed.