Sintered Glass-Ceramics, Self-Glazed Materials and Foams from Metallurgical Waste Slag

Modeling of Non-Ferrous Metallurgy Waste Disposal with the Production of Iron Silicides and Zinc Distillation

This paper presents studies on the possibility of utilization of technogenic waste from the metallurgical industry by the method of complex processing in order to reduce the anthropogenic load on the environment of the region with the example of the zinc silicate-magnetite-carbon system. The selected sample of clinker dump from welting was subjected to chemical and scanning electron microscopic analyses and thermodynamic modeling. Thermodynamic studies were carried out in the temperature range 1600–2200 K and pressure p = 0.1 MPa, modeling the process of electric melting of clinker from welting in an arc furnace using the software application Astra 4 developed at the Bauman Moscow State Technical University (Moscow, Russian Federation). As a result of the thermodynamic modeling, the optimal temperature range was established, which was 1800–1900 K. Thermodynamic studies established that it is possible to drive away zinc from the system under study by 99–100% in the entire temperature range under study. The maximum degree of silicon extraction (α_Si) in the alloy is up to 69.44% at T = 1900 K, and the degree of iron extraction (α_Fe) in the alloy is up to 99.996%. In particular, it was determined and proved that clinker waste from welting can act as a secondary technogenic raw material when it is processed as a mono mixture to produce iron silicides with a silicon content of 18 to 28%.

Recent Developments in Steelmaking Industry and Potential Alkali Activated Based Steel Waste: A Comprehensive Review

The steel industry is responsible for one-third of all global industrial CO₂ emissions, putting pressure on the industry to shift forward towards more environmentally friendly production methods. The metallurgical industry is under enormous pressure to reduce CO₂ emissions as a result of growing environmental concerns about global warming. The reduction in CO₂ emissions is normally fulfilled by recycling steel waste into alkali-activated cement. Numerous types of steel waste have been produced via three main production routes, including blast furnace, electric arc furnace, and basic oxygen furnace. To date, all of the steel waste has been incorporated into alkali activation system to enhance the properties. This review focuses on the current developments over the last ten years in the steelmaking industry. This work also summarizes the utilization of steel waste for improving cement properties through an alkali activation system. Finally, this work presents some future research opportunities with regard to the potential of steel waste to be utilized as an alkali-activated material.