Impact of Fly Ashes from Combustion in Fluidized Bed Boilers and Siliceous Fly Ashes on Durability of Mortars Exposed to Seawater and Carbonation Process

Influence of the Composition and Curing Time on Mechanical Properties of Fluidized Bed Combustion Fly Ash-Based Geopolymer

This paper presents novel research on a fluidized bed combustion (FBC) fly ash-based geopolymer as a contribution to the problem of FBC fly ash disposal, and a proposal for a new geopolymer composition-an environmentally friendly material that is possible to use in construction. Geopolymer samples of various composition (containing FBC fly ash as the main raw material, metakaolin and CRT glass as additional components, and sodium silicate and sodium hydroxide as activators) were subjected to flexural and compressive strength tests. An investigation on the effect of the demolding time was carried out on one selected mixture. The test showed that both the composition and the demolding time have a decisive influence on the basic mechanical properties. A mixture containing FBC fly ash to metakaolin in a mass ratio of 3:1, removed from the mold after 14 days, was found to be the best in terms of the mechanical parameters expected from a material that could be used in construction, e.g., for the production of precast elements. According to the results obtained, FBC fly ash is a promising and environmentally friendly raw material for the production of geopolymer, with good mechanical properties and low density. Moreover, a high compressive strength can be obtained by curing the geopolymer at ambient temperature.

Durability of Cement and Ash Mortars with Fluidized and Siliceous Fly Ashes Exposed to HCl Acid Environment over a Period of 2 Years

The paper presents results of research on the impact of fly ash from fluidized bed combustion (FBC) of lignite, used in quantities of 30 and 45% by mass, and the mixture of FBC and silicious fly ash in amount of 45% by mass, on properties of cement–ash mortars. Mortars were exposed to aggressive environment of 1, 3, and 5% HCl solutions for 2 years. Mortars containing 45% FBC exposed to 1% HCl solution (pH = 2) showed the highest durability from among other mortars. The growth of their strength observed after 90 days of testing in 1% HCl environment, as well as the lowest drop of strength after 730 days of exposure to this environment, resulted from the reduced amount of large pores from 20 to 200 nm in mortars containing fly ash, with simultaneous growth of smaller pores of <20 nm during testing. A beneficial effect has been demonstrated of FBC addition to cement on properties of cement–ash mortars exposed to the aggressive impact of the HCl. Mortars with FBC fly-ash content increased to 45% by mass showed higher strength values, smaller differences in linear and mass changes, and increased durability in an aggressive environment observed during 730 days of testing.