A Silver Yarn-Incorporated Song Brocade Fabric with Enhanced Electromagnetic Shielding

Shielding Performance of Electromagnetic Shielding Fabric Implanted with "Split-Ring Resonator"

The electromagnetic shielding (EMS) fabric is an important electromagnetic protection product, which is widely applied in various fields. The improvement of its shielding effectiveness (SE) has always been the focus of research. This article proposes to implant a metamaterial structure of a "split-ring resonator (SRR)" in the EMS fabrics, so that the fabric not only maintains the porous and lightweight characteristics, but also obtains the SE improvement. With the help of the invisible embroidery technology, stainless-steel filaments were used to implant hexagonal SRRs inside the fabric. The effectiveness and influencing factors of the SRR implantation were described by testing the SE of the fabric and analyzing the experimental results. It was concluded that the SRR implantation inside the fabric can effectively improve the SE of the fabric. For the stainless-steel EMS fabric, the increase amplitude of the SE reached between 6 dB and 15 dB in most frequency bands. The overall SE of the fabric showed a decrease trend with the reduction of the outer diameter of the SRR. The decrease trend was sometimes fast and sometimes slow. The decreasing amplitudes were different in various frequency ranges. The number of embroidery threads had a certain effect on the SE of the fabric. When other parameters remained unchanged, the increase of the diameter of the embroidery thread resulted in the increase of the SE of the fabric. However, the overall improvement was not significant. Finally, this article also points out that other influencing factors of the SRR need to be explored, and the failure phenomenon may occur under certain situations. The proposed method has the advantages of the simple process, convenient design, no pore formation, SE improvement retaining the original porous characteristics of the fabric. This paper provides a new idea for the design, production, and development of new EMS fabrics.

A Rapid Thermal Absorption Rate and High Latent Heat Enthalpy Phase Change Fiber Derived from Bio-Based Low Melting Point Copolyesters

A series of poly(butylene adipate-co-hexamethylene adipate) (PBHA) copolymers with different content of 1,4-cyclohexanedimethanol (CHDM) was synthesized via one-step melt polymerization. The PBHA copolymer with 5 mol% CHDM (PBHA-C5) exhibited a low melting point (T_m) and high enthalpy of fusion (∆H_m) of 35.7 °C and 43.9 J g⁻¹, respectively, making it a potential candidate for an ambient temperature adjustment textile phase change material (PCM). Polybutylene terephthalate (PBT) was selected as the matrix and blended at different weight ratios of PBHA-C5, and the blended samples showed comparable T_m and ∆H_m after three cycles of cooling and reheating, indicating good maintenance of their phase changing ability. Samples were then processed via melt spinning with a take-up speed of 200 m min⁻¹ at draw ratios (DR) of 1.0 to 3.0 at 50 °C. The fiber’s mechanical strength could be enhanced to 2.35 g den⁻¹ by increasing the DR and lowering the PBHA-C5 content. Infrared thermography showed that a significant difference of more than 5 °C between PBT and other samples was achieved within 1 min of heating, indicating the ability of PBHA-C5 to adjust the temperature. After heating for 30 min, the temperatures of neat PBT, blended samples with 27, 30, and 33 wt% PBHA-C5, and neat PBHA-C5 were 53.8, 50.2, 48.3, 47.2, and 46.5 °C, respectively, and reached an equilibrium state, confirming the temperature adjustment ability of PBHA-C5 and suggesting that it can be utilized in thermoregulating applications.