Waste Glass Powder Reusability in High-Performance Concrete: Leaching Behavior and Ecotoxicity

The Impact of NaOH on the Micro-Mechanical Properties of the Interface Transition Zone in Low-Carbon Concrete

To tackle carbon emissions from cement production and address the decline in concrete's mechanical properties due to the substitution of cement with solid waste (glass powder) and natural mineral admixture (zeolite powder) materials, we employed glass powder and zeolite powder to create composite cementitious materials. These materials underwent alkali activation treatment with a 4% NaOH dosage, replacing 50% of cement to produce low-carbon concrete. Nanoindentation tests and mercury intrusion porosimetry (MIP) were employed to uncover the micro-mechanical properties and influencing mechanisms of alkali-activated low-carbon concrete. The results indicate a notable enhancement in the indentation modulus (19.9%) and hardness (25.9%) of alkali-activated low-carbon concrete compared to non-activated concrete. Simultaneously, the interfacial transition zone thickness decreased by 10 µm. The addition of NaOH led to a reduced volume fraction of pores (diameter >100 nm) and an increased fraction of pores (diameter < 100 nm), thereby reducing porosity by 2.6%, optimizing the pore structure of low-carbon concrete. The indentation modulus, hardness and volume fraction of the hydrated phase derived from Gaussian fitting analysis of the nanoindentation statistics showed that NaOH significantly improved the modulus and hardness of the hydration products of low-carbon concrete. This activation resulted in decreased LDC-S-H gel (low-density hydrated calcium silicate Ca5Si6O16(OH)·4H2O) and pore content, while the HD C-S-H gel (high-density hydrated calcium silicate Ca5Si6O16(OH)·4H2O) and CH (calcium hydroxide crystals Ca(OH)2) content increased by 13.91% and 23.46%, respectively. Consequently, NaOH influenced the micro-mechanical properties of low-carbon concrete by generating more high-density hydration products, reducing pore content, enhancing the pore indentation modulus and hardness, and shortening the interfacial transition zone. This study offers novel insights into reducing carbon emissions and promoting the use of solid waste (glass powder) and natural mineral admixture (zeolite powder) materials in concrete, contributing to the advancement of sustainable construction practices.

Experimental Study on Long-Term Mechanical Properties and Durability of Waste Glass Added to OPC Concrete

This study aims to achieve the sustainable utilization of waste glass resources through an investigation into the influence of three types of admixtures, namely waste glass powder (WGP) (G), waste glass powder-slag (G-S), and waste glass powder-fly ash (G-F), on the mechanical properties and durability performance of waste glass concrete. The experimental results demonstrate that the exclusive use of WGP as an admixture led to the relatively poor early compressive strength of the concrete, which decreased with an increase in dosage. However, at medium to long curing ages, the strength of the waste glass concrete could equal or even surpass that of ordinary concrete. When dual admixtures were employed, the G-S group exhibited higher compressive strength compared to the G-F group. Specifically, within the G-S group, a glass powder dosage of 15% yielded higher compressive strength, and after 180 days, the dual admixture groups exhibited greater strength than ordinary concrete (G0); the compressive strength of the tG1S1 group was 44.57 MPa, and that of the G0 group was 40.07 MPa. The chloride ion diffusion coefficient showed a varying trend with an increase in WGP dosage, initially decreasing and then increasing. The concrete's resistance to erosion was maximized when the glass powder dosage reached 30%. As the WGP dosage increased, the overall frost resistance decreased. For a total dosage of 30%, the optimal glass powder dosage in both G-S and G-F groups was found to be 15%.

Alkali-silica Reaction Elimination Potential of High-Performance Concrete Containing Glass Powder

This study is mainly concerned with the assumption that glass powder can eliminate the potential alkali-silica reaction in high performance concrete. Glass is often land filled, produced as a secondary raw material or as a by-product of production. Chemical analyses were carried out, and the ecotoxicity of the material was investigated, serving as a basis for testing a potential alkali-silica reaction. High performance concrete (HPC) containing different types of waste powder (secondary raw material from production (SGP), jewelry production (SGJ), container waste glass (CWG), and glass from used photovoltaic panels (GPP)) are tested according to the international standard ASTM C1260 and the Czech technical condition TP 137. Newly designed mixtures are innocuous from the ASR point of view in the most cases, except SGP HPC.

Ecotoxicity of Concrete Containing Fine-Recycled Aggregate: Effect on Photosynthetic Pigments, Soil Enzymatic Activity and Carbonation Process

Recycling of materials such as masonry or concrete is one of the suitable ways to reduce amount of disposed construction and demolition waste (CDW). However, the environmental safety of products containing recycled materials must be guaranteed. To verify overall environmental benefits of recycled concrete, this work considers ecotoxicity of recycled concrete, as well as potential environmental impacts of their life cycle. Moreover, impacts related with carbonation of concrete is considered in terms of durability and influence of potential CO2 uptake. Concrete containing fine recycled aggregate from two different sources (masonry and concrete) were examined experimentally at the biochemical level and compared with reference samples. Leaching experiments are performed in order to assess physicochemical properties and aquatic ecotoxicity using water flea, freshwater algae and duckweed. The consequences, such as effects of material on soil enzymatic activity (dehydrogenase activity), photosynthetic pigments (chlorophylls and carotenoids), and the carbonation process, are verified in the laboratory and included in the comparison with the theoretical life cycle assessment. As a conclusion, environmental safety of recycled concrete was verified, and its overall potential environmental impact was lower in comparison with reference concrete.

Influence of Waste Glass Powder Addition on the Microstructure and Mechanical Properties of Autoclaved Building Materials

Lime quartz samples in which ground quartz sand was gradually substituted with waste glass powder (GP) were obtained under hydrothermal conditions to determine the influence of GP addition on the microstructure (observed by SEM), phase composition (analyzed by XRD), and compressive strength of autoclaved building materials. An additional series containing analytical grade NaOH and no GP was formed to evaluate the effect of sodium ions on tobermorite formation and its impact on the mechanical properties of the samples. GP addition hindered the formation of tobermorite during autoclaving. Instead, a higher amount of an amorphous and semi-crystalline C-S-H phase formed, leading to the densification of the composite matrix. Nevertheless, tobermorite-like structures were found during both XRD and SEM analyses, proving that the presence of small amounts of Al³⁺ ions allowed, to an extent, for the stabilization of the phase despite the high sodium content. The compressive strength values indicate that the presence of alkali in the system and the resulting formation of additional portions of C-S-H have a beneficial influence on the mechanical properties of autoclaved composites. However, the effect fades with increasing glass powder content which, together with a slight expansion of the samples, suggests that at high sand substitution levels, an alkali-silica reaction takes place.