Synthesis of Metal Matrix Composites Based on CrxNiy-TiN for Additive Technology

Effect of Mechanical Activation of Al-Ti-B Powder Mixture on Phase Composition and Structure of Al-TiB2 Composite Materials Obtained by Self-Propagating High-Temperature Synthesis (SHS)

In this study, we successfully obtained Al-TiB₂ composite materials using self-propagating high-temperature synthesis and preliminary mechanical activation of the initial Al-(Ti + 2B) powder mixture with a high aluminum content (70 wt.%). We investigated the possibility of controlling the structure of synthesis products, in particular, the size and shape of ceramic particles. We examined the effects of the mechanical activation of the initial powder mixture on the structure and particle size of titanium diboride in the synthesis products. We proposed a mechanism of structure formation in the synthesis products obtained by SHS using the method of preliminary mechanical activation of the initial mixture. We found that mechanical activation for 60-180 s led to the formation of isolated TiB₂ particles of prolate and irregular shape. The average particle size of TiB₂ in the synthesis products was 0.77 (after 60 s of mechanical activation) and 1.5 µm (after 180 s of mechanical activation), respectively. An increase in the duration of mechanical activation to 900 s led to the formation of an island (skeletal) structure, in which there were interconnected aggregates and isolated particles of titanium diboride. The average size of these particles was 4.3 µm.

Structure and Properties of Metal-Matrix Composites Based on an Inconel 625–TiB2 System Fabricated by Additive Manufacturing

This research work studies the structural phase parameters and physicomechanical properties of metal-matrix composite materials based on a Ni–TiB2 system obtained by additive manufacturing (specifically, direct laser deposition). The properties of the composites obtained were investigated at high temperatures (up to 1000 °C). The feasibility of the fabrication of a composite nanostructure of alloy with advanced physicomechanical properties was shown. The introduction of reinforcing TiB2 particles into an Inconel 625 matrix was confirmed to increase the microhardness and tensile strength of the material obtained. Apparently, the composite structure of the samples facilitates the realisation of several strengthening mechanisms: (1) a grain boundary mechanism that causes strengthening and dislocation movement; (2) a mechanism based on the grain structure breakdown and Hall–Petch relationship realisation.