Surface Characteristics of High Translucent Multilayered Dental Zirconia Related to Aging

Effect of toothbrushing on surface roughness, gloss, and topography of polished and glazed ultra-translucent zirconia

PURPOSE

This study evaluated the effect of toothbrushing cycles on surface roughness (Ra), gloss (GU), and morphology of two zirconia finishing and polishing protocols.

MATERIALS AND METHODS

An ultra-translucent zirconia disc was sectioned into rectangular plates (12 mm × 7 mm × 3 mm) and divided into two groups according to the polishing and finishing system used (diamond rubber abrasive/DRA or glazing/GLA). Bovine enamel (BEN) plates with the same dimensions were used as a Control. Specimens of zirconia and enamel were analyzed for Ra and GU (n = 11) and surface morphology by scanning electron microscopy (n = 3) before toothbrushing (baseline) and after 15,000 and 30,000 toothbrushing cycles. Ra and GU data were analyzed by ANOVA two-way and post-hoc Tukey's test (α = 0.05), while the surface morphology was analyzed qualitatively.

RESULTS

The Ra decreased significantly after 30,000 toothbrushing cycles for DRA and GLA zirconia ceramics. DRA showed a higher GU at the baseline, after 15,000 and 30,000 toothbrushing cycles than GLA and BEN. Toothbrushing polished the zirconia, creating a smooth surface, while no changes were observed for BEN.

CONCLUSIONS

The increase in toothbrushing cycles (30,000) changed the surface roughness of DRA and GLA zirconia ceramics. DRA zirconia presented the highest GU, which did not change with toothbrushing.

The Effect of Polishing, Glazing, and Aging on Optical Characteristics of Multi-Layered Dental Zirconia with Different Degrees of Translucency

(1) Background: Considering that the appearance of a dental material is an important factor that contributes to the success of prosthetic restorations. The purpose of this study is to investigate the optical properties and color changes among the layers of three commercial zirconias, to compare the aspect of the polished and glazed surfaces before and after aging and to evaluate the effects of hydrothermal degradation on their aesthetics. (2) Methods: Forty-eight plate-shaped samples were sectioned from presintered blocks of each multilayer translucent zirconia with different Yttrium content: Ceramill Zolid fx ML (5 mol%) = CeZ, STML (4 mol%) = STM, IPS e.maxZirCAD CEREC/in Lab MT Multi (4 mol% + 5 mol%) = IPZ. The samples were sintered according to the recommendation of each manufacturer, and half (24) of them were polished and the other half (24) glazed on one of the surfaces. Each type was equally divided into one control and one aging group, and, for each material, this resulted in four groups (n = 12): polished-control, polished-autoclaved glazed-control, and glazed-autoclaved. The artificial aging was carried out with an autoclave and distilled water at 134 °C, 0.2 MPa for 1 h, and for optical parameters (TP, CR, OP) and color change (ΔE*) measurements on a black and white background in a CIE L*a*b* color system, a spectrophotometer was used. The specimens were evaluated in incisal, cervical, and medium areas on polished and glazed samples before and after the aging stage. Statistical analysis was achieved with a two-way ANOVA test, the unpaired t-test, and the paired t-test. (3) Results: Before and after aging, the mean TP values for polished samples were higher than the glazed ones. After aging, the mean TP values increased for all groups (except polished CeZ), and significant differences were reported for polished STM, IPZ. After LTD, the opalescence registered an increase for almost all groups (except polished CeZ, polished and glazed IPZ-medium area), and significant differences were reported for almost all groups (except STM-incisal, IPZ-cervical, medium areas). The levels of color change were between extremely slight to perceivable. (4) Conclusions: Optical properties of the selected multilayer zirconia were influenced by polishing and glazing as surface treatment and affected by artificial aging (CeZ the least); perceivable color changes for polished STM, IPZ were detected.