In Vitro Study of Laser-Assisted Prefabricated Ceramic Crown Debonding as Compared to Traditional Rotary Instrument Removal

Effect of Er:YAG laser on debonding zirconia and lithium disilicate crowns bonded with 2- and 1-bottle adhesive resin cements

INTRODUCTION

Erbium-doped yttrium-aluminum-garnet (Er:YAG) laser debonding of zirconia and lithium disilicate restorations is increasingly used for a range of clinical applications. Using rotary instruments to remove such restorations for any purpose has proven to be challenging. Erbium laser has been reported to be a conservative method for removing ceramic restorations. There is little data in the literature about the effect of adhesive resin cement type on the debonding time of the ceramic restoration using the Er:YAG laser.

OBJECTIVES

To evaluate and compare the time required for the Er:YAG laser to debond zirconia and lithium disilicate crowns bonded with a 2- and 1-bottle adhesive resin cement systems.

MATERIALS AND METHODS

Forty extracted premolar teeth were prepared and scanned for milled 40 CAD/CAM crowns. Teeth were randomly assigned into groups (n = 10 per group): 3 mol% yttria-partially stabilized zirconia crowns 3Y-PSZ (G1a) bonded with Panavia™ V5 (2-bottle adhesive resin cement), Zirconia 3Y-PSZ crowns (G1b) bonded with RelyX™ Ultimate (1-bottle adhesive resin cement), and for the lithium disilicate crowns bonded with the two types of cements (G2a, G2b). Each specimen was irradiated with an Er:YAG laser at 335 mJ, 15 Hz, 5.0 W, and 50-ms pulse duration (super short pulse mode). The irradiation time required for crowns to be successfully debonded was recorded for each specimen. Data were statistically analyzed using ANOVA and Tukey HSD post-hoc test (p < 0.05), at the 95 percent level of confidence. The intaglio surface of the debonded crown was analyzed using scanning electron microscopy (SEM).

RESULTS

The mean ± standard deviation times needed for crown debonding were 5.75 ± 2.00 min for the G1a group, 4.79 ± 1.20 min for group G1b, 1.69 ± 0.49 min for group G2a, and 1.12 ± 0.17 for group G2b. There was no statistically significant difference in debonding time between the 2- and 1- bottle adhesive resin cement within the groups G1a and b (p = 0.2914), or between groups G2a b (p = 0.7116). A statistically significant difference (p < 0.05) was found between groups G1a and G2a and b and between groups G1b and G2a and b were SEM analysis showed no changes in the microstructure of the ceramic surface after Er:YAG laser irradiation.

CONCLUSION

Zirconia and lithium disilicate restorations can be debonded using Er:YAG lasers in a safe and efficient manner. There is no significant difference in the debonding time between the 2- and 1- bottle adhesive resin cement systems used in this study.

CLINICAL SIGNIFICANCE

Retrieving zirconia and lithium disilicate ceramics can be a challenging process when using diamond rotary instruments. ER:YAG lasers may efficiently debond these ceramics from the tooth structure, independent of the bonding process used for bonding them.

Er:YAG laser debonding of zirconia and lithium disilicate restorations

STATEMENT OF PROBLEM

Yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) restorations of different formulations are being used increasingly in monolithic form for a range of clinical applications. Using rotary instruments to remove such restorations for any purpose is challenging, but they can be removed conservatively with erbium lasers. However, studies on how a laser penetrates different zirconias to break the cement bond between the tooth surface and the zirconia are lacking.

PURPOSE

The purpose of this in vitro study was to evaluate and compare the time required for an erbium-doped yttrium-aluminum-garnet (Er:YAG) laser to remove different types of zirconia and lithium disilicate crowns.

MATERIAL AND METHODS

Forty extracted premolar teeth were prepared, scanned, designed, and milled to fabricate 40 computer-aided design and computer-aided manufacturing (CAD-CAM) crowns, which were assigned to 4 groups (n=10): 3 mol% Y-TZP, 4 mol% Y-TZP, 5 mol% Y-TZP, and lithium disilicate as a control. All crowns were bonded to the teeth with a self-adhesive resin cement (Panavia SA Cement Universal). Each specimen was irradiated with an Er:YAG laser with the following parameters: 300 mJ, 15 Hz, 5.0 W, and a 50-microsecond pulse duration (supershort pulse mode). The irradiation time required for crowns to be retrieved successfully was recorded for each specimen. Data were statistically analyzed using analysis of variance and the Tukey honestly significant difference post hoc test (α=.05). The intaglio surfaces of the restorations were analyzed using scanning electron microscopy (SEM).

RESULTS

The mean ±standard deviation times in minutes needed for crown debonding were 12.46 ±4.17 for the 3 mol% Y-TZP group, 10.30 ±3.33 for the 4 mol% Y-TZP group, 4.03 ±1.62 for the 5 mol% Y-TZP group, and 2.08 ±0.92 for the lithium disilicate group. A statistically significant difference (P<.05) in the debonding time was found for all investigated groups, expect between the 3 mol% and 4 mol% Y-TZP groups and between the 5 mol% Y-TZP and lithium disilicate groups. SEM analysis of the ceramic surfaces showed no visual damage associated with Er:YAG laser irradiation.

CONCLUSIONS

Zirconia crown retrieval time with the Er:YAG laser was influenced by the yttria content of the zirconia, with decreasing retrieval time with increasing yttria content. Er:YAG laser debonding of zirconia crowns is a noninvasive, efficient, and rapid approach to the removal of crowns and could be applied in clinical practice.

Evaluation of the effectiveness and practicality of erbium lasers for ceramic restoration removal: A retrospective clinical analysis

BACKGROUND

The purpose of this study was to assess the effectiveness and practicality of erbium lasers in the removal of ceramic restorations and appliances from natural teeth and dental implant abutments in clinical practice.

METHODS

A retrospective analysis was conducted, involving 29 clinical cases with a total of 52 abutments requiring the removal of various ceramic restorations. The analysis evaluated the clinical procedures performed, including the type and material of the prosthetic, the type of cement used, laser setting parameters, retrieval time, and retrieval success.

RESULTS

Out of the 52 abutments, 50 were successfully retrieved without causing any damage (>95%) using either an Er,Cr:YSGG laser (N = 6) or an Er:YAG laser (N = 46). In one case, a crown was partially sectioned to prevent any negative impact of laser irradiation on the adhesive strength between the post and tooth, and in another case, a fracture occurred during debonding. The restorations consisted of 13 lithium disilicate and 39 zirconia units, including six veneers, 38 single crowns, and three fixed partial dentures (FPDs). The retrieval time varied depending on the restoration type, material thickness, cement type, retention form/fitting of the abutment and restoration, ranging from 2.25 ±0.61 minutes for veneers, 6.89 ±8.07 minutes for crowns, to 25 ±10 minutes per abutment for FPDs. Removal of a zirconia crown required more time, 7.12±8.91 minutes, compared to a lithium disilicate crown, 5.86 ±2.41 minutes. The debonding time was influenced by the laser settings as well as materials and types of prosthesis.

CONCLUSIONS

Erbium lasers present a safe and effective alternative to invasive methods for removing ceramic restorations, without causing harm to the abutment or prosthesis. Laser-assisted debonding allows for recementation of the restorations during the same appointment, making it a conservative and viable option for ceramic crown retrieval in clinical settings.