The Effects of Staining and Cleaning on the Color and Light Transmittance Changes of a Copolyester Retainer Material with Different Surface Textures

Comparison of light transmittance and color changes between polyurethane and copolyester retainer materials after staining and destaining

BACKGROUND

Retainers are the only effective approach to prevent orthodontic relapse. The aim of this study was to compare the changes in color and light-transmittance of rough and smooth thermoformed polyurethane and copolymer retainer samples after staining in different solutions and destaining with different approaches.

METHODS

Four hundred copolyester (Essix® ACE) and 400 polyurethane (Zendura®) samples with different surface textures, smooth and rough, were stained in 4 different solutions (n = 100 per solution) over 28 days. Each of the four groups of 100 stained samples of each material was subdivided into 5 groups of 20 samples and subjected to different destaining solutions. Light transmittance and color changes were evaluated using a spectrometer and a spectrophotometer. Mean differences were compared using a two-way analysis of variance (ANOVA) and posthoc multiple comparison tests at P = 0.05.

RESULTS

No significant differences in light transmittance were found between both untreated materials. Both materials were stained in a similar fashion and showed no significant differences between two materials after staining. Coffee and tea stained both materials more significantly than wine, but there was a significant difference of changes of color and light transmittance between rough and smooth surfaces during the destaining in coffee- and tea-stained samples of copolyester material. All destaining solutions were effective at removing all stains on the samples. The surface roughness of the material plays a significant role in the ability of the materials to be destained, demonstrating a more significant greater effect on cleaning rough samples for improvements in light-transmittance and greater changes in color.

CONCLUSIONS

This study concluded that the surface of materials plays a significant role in the material destaining and staining. In addition, the different polymers used for retainer fabrication exhibited different responses during the destaining process depending on types of stains.

Coffee Staining and Simulated Brushing Induced Color Changes and Surface Roughness of 3D-Printed Orthodontic Retainer Material

This in vitro study evaluated the influence of combined coffee staining and simulated brushing-induced color changes and surface roughness on 3D-printed orthodontic retainers. Specimens measuring 10 × 10 × 0.75 mm³ were obtained either by conventional vacuum forming or 3D printing at four print angulations (0°, 15°, 30°, and 45°) (n = 10). The prepared specimens were immersed in a coffee beverage and then mechanically brushed using a simulating device. The specimen's color difference (ΔE) and surface roughness (Ra) were quantified using a spectrophotometer and a non-contact profilometer, respectively. The highest and lowest mean ΔE values were recorded for the 3D-printed-45° (4.68 ± 2.07) and conventional (2.18 ± 0.87) groups, respectively. The overall mean comparison of ΔE between the conventional and 3D-printed groups was statistically significant (p < 0.01). After simulated brushing, all groups showed a statistically significant increase in the Ra values (p < 0.01). The highest Ra was in the 3D-printed-45° (1.009 ± 0.13 µm) and conventional (0.743 ± 0.12 µm) groups, respectively. The overall ΔE of 3D-printed orthodontic retainers was not comparable to conventional VFRs. Among the different angulations used to print the retainers, 15° angulations were the most efficient in terms of color changes and surface roughness and were comparable to conventional VFRs.