A Review on Strength and Durability Properties of Wooden Ash Based Concrete

The Influence of Silica Fly Ash and Wood Bottom Ash on Cement Hydration and Durability of Concrete

This research addresses a notable gap in understanding the synergistic effects of high carbon wood bottom ash (BA) and silica fly ash (FA) on cement hydration and concrete durability by using them as a supplementary material to reduce the amount of cement in concrete and CO2 emissions during cement production. This study analyses the synergistic effect of FA and BA on cement hydration through X-ray diffraction (XRD), thermal analysis (TG, DTG), scanning electron microscopy (SEM), density, ultrasonic pulse velocity (UPV), compressive strength, and temperature monitoring tests. In addition, it evaluates concrete properties, including compressive strength, UPV, density, water absorption kinetics, porosity parameters, predicted resistance to freezing and thawing cycles, and results of freeze-thawing resistance. The concrete raw materials were supplemented with varying percentages of BA and FA, replacing both cement and fine aggregate at levels of 0%, 2.5%, 5%, 10% and 15%. The results indicate that a 15% substitution of BA and FA delays cement hydration by approximately 5 h and results in only a 6% reduction in compressive strength, with the hardened cement paste showing a strength similar to a 15% replacement with FA. Concrete mixtures with 2.5% BA and 2.5% FA maintained the same maximum hydration temperature and duration as the reference mix. Furthermore, the combined use of both ashes provided adequate resistance to freeze-thaw cycles, with only a 4.7% reduction in compressive strength after 150 cycles. Other properties, such as density, UPV and water absorption, exhibited minimal changes with partial cement replacement by both ashes. This study highlights the potential benefits of using BA and FA together, offering a sustainable alternative that maintains concrete performance while using waste materials.

New Advances in Cement and Concrete Research

The Special Issue (SI), "New Advances in Cement and Concrete Research", highlights the latest breakthroughs in cement and concrete research [...].

Effect of Walnut-Shell Additive on the Structure and Characteristics of Concrete

The partial replacement of the mineral components of concrete with natural renewable analogues in full possession of the performance characteristics of the final material, allows not only the concrete-production process to be made more environmentally friendly and inexpensive, but also to solve an important task for the agricultural industry, which is that associated with waste disposal. The scientific novelty of the work is in the obtaining of new concrete compositions by the partial replacement of coarse aggregate with a natural analogue in the form of a walnut shell, which has the maximum ratio of the strength of the composite to its density, as well as in identifying new dependencies of strength and density and their ratio on the amount of replacement of mineral coarse-aggregate walnut shell. The main goal of this article was to analyze the effect of composition factors on characteristics of concrete with partial replacement of large aggregates with walnut shells and to search for the optimal compound that would make it possible to obtain concrete with a minimum decrease in strength characteristics with a maximum decrease in concrete density. Cubes and prism laboratory samples were made from concrete of normal density with the replacement of coarse aggregate by 5, 10, 15, 20, 25 and 30%, by volume. The main mechanical properties, such as density, strength (compressive, tensile, tensile strength in bending) of the concrete samples were studied. The investigation used standard methods and scanning electron microscopy. An increase into strength characteristics up to 3.5%, as well as the maximum ratio of strength to density of concrete, was observed at a walnut-shell dosage of 5%. Effective partial replacement of coarse aggregate with walnut shells leads to a reduction in the consumption of crushed stone by up to 10% and a decrease in the mass of concrete by up to 6%.