The purpose of this study was to examine the effect of different cleaning methods and resin cements on the shear bond strength (SBS) of contaminated zirconia. A total of 92 disc-shaped zirconia specimens were contaminated with different procedures. Then, the specimens were grouped according to cleaning methods and resin cements: no cleaning + Variolink Esthetic DC (CN_V ), no cleaning + Panavia V5 (CN_P ), sandblasted + Variolink Esthetic DC (SB_V ), sandblasted + Panavia V5 (SB_P ), Ivoclean + Variolink Esthetic DC (IC_V ), Ivoclean + Panavia V5 (IC_P ), Katana Cleaner + Variolink Esthetic DC (KC_V ), and Katana Cleaner + Panavia V5 (KC_P ). Following an aging protocol in a 37°C for 1 week, SBS analysis was performed with a universal test machine. For the surface topography and elemental analysis, scanning electron microscopy and energy-dispersive X-ray spectroscopy (EDS) were used. Significance was evaluated as p < .05 and p < .01. The highest SBS results were found in the SB_P group, showing a statistically significant difference from all other groups (p < .05). For the same cleaning method, Panavia V5 showed statistically significantly higher SBS values than Variolink Esthetic DC (p < .01), except the CN_P -CN_V (p = .880) and KC_P -KC_V (p = .082) groups. The most detected surface elements by EDS were Zr, O, C, and N, respectively. The contaminated zirconia surfaces must be cleaned for successful adhesion. The use of phosphate-containing adhesives in combination with sandblasting will increase the adhesion strength, and universal cleaning agents can be a good alternative to sandblasting.

Influence of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) incorporated experimental cleaners on the bonding performance of saliva-contaminated zirconia ceramic

OBJECTIVES

To assess the efficacy of experimental cleaners containing 10-methacryloyloxydecyl dihydrogen phosphate (MDP) on the saliva decontamination of ceramic and their influence in restoring zirconia's adherence to resin cement.

MATERIALS AND METHODS

Four hundred sixty alumina-blasted zirconia specimens were categorized into saliva-contaminated and uncontaminated groups which were treated with ceramic primer (P), experimental cleaner 1 (C1), C1 followed by P (C1P), experimental cleaner 2 (C2), and C2 followed by P (C2P). Stainless-steel rods were then attached to the specimens using PanaviaV5 cement (Kuraray Noritake Dental; Tokyo, Japan). Tensile bond strength (TBS) test was performed after 24 h and 5000 thermocycling processes. X-ray photoelectron spectroscopy (XPS) analysis and contact angle measurement of the specimen were performed. The TBS data were analyzed by Weibull analysis and three-way ANOVA. Contact angle data were analyzed by two-way ANOVA (α = 0.05).

RESULTS

C2P groups showed the highest TBS in all conditions among tested groups. Saliva contamination led to a significant reduction of TBS in primer- and cleaner-treated groups, with no significant impact on C2P. Adhesive failure was predominant in contaminated groups except with the C1P and C2P groups. XPS revealed that a nitrogen peak was observed on contaminated groups but not in primed groups. The contact angle was significantly affected by saliva contamination, the cleaners, and/or ceramic primer usage (p < 0.001).

CONCLUSIONS

The MDP cleaner followed by the MDP primer protocol may overcome the effect of saliva contamination and improve the resin-ceramic bond strength.

CLINICAL RELEVANCE

It is recommended to use a combination of MDP-containing cleaner 2 and ceramic primer as a chair-side chemical pretreatment for zirconia substrate with or without saliva contamination.

Durability of resin bonding to zirconia ceramic after contamination and the use of various cleaning methods

OBJECTIVES

The aim of the study was to evaluate the influence of contamination and different cleaning methods on the tensile bond strength with a phosphate monomer containing luting resin to zirconia ceramic.

METHODS

After the contamination with saliva or silicone disclosing agent, 228 polished and airborne-particle abraded zirconia discs were ultrasonically cleaned with 99% isopropanol. In a second step, the specimens were either treated with argon-oxygen plasma, air plasma, enzymatic cleaning agent or did not undergo an additional cleaning process. Uncontaminated zirconia specimens were used as the control group. X-ray photoelectron spectroscopy (XPS) was used for chemical analysis of the bonding surfaces of specimens. Plexiglas tubes filled with composite resin were bonded to zirconia specimens with a phosphate monomer containing luting resin. Tensile bond strength (TBS) was tested after 3 days or 150 days water storage with 37,500 thermal cycles.

RESULTS

XPS revealed a decrease of the carbon/oxygen ratio after plasma treatment and an increase after treatment with an enzymatic cleaning agent in all groups. All contaminated specimens showed high and durable TBS after cleaning with a combination of isopropanol and a non-thermal atmospheric plasma. After the cleaning with enzymatic cleaning agent the TBS was significantly reduced in all groups after 150 days thermal cycling.

SIGNIFICANCE

The combination of isopropanol and plasma cleaning was effective in removing salvia and disclosing agent contamination. Enzymatic clearing agent was not able to remove contamination effectively and had a negative impact on the TBS of non-contaminated specimens.